Colorful rubber composition for tire sidewall and preparation method of colorful rubber composition

A rubber composition and color technology, applied in the fields of rubber tires and chemical manufacturing, can solve the problems of low sidewall flex resistance, easy fading of sidewalls, and low aging resistance, so as to improve compatibility and shorten mixing time, performance-enhancing effects

Inactive Publication Date: 2017-01-25
山东新大陆橡胶科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the shortcomings of the prior art, to seek a color rubber composition for tire sidewalls and its preparation method, to solve the problem of low flex resistance and low aging resistance of colored rubber sidewalls in the prior art And the problem of easy fading of the sidewall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful rubber composition for tire sidewall and preparation method of colorful rubber composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The colored rubber composition used in the sidewall of the tire involved in this embodiment, its raw material components and parts by weight of each component are: 35 parts of SVR-3L type rubber, 15 parts of KEP-350 type rubber, and 15 parts of CIIR-1066 type rubber 50 parts, tackifying resin 1.5 parts, stearic acid 2 parts, dispersant 1.5 parts, non-polluting anti-aging agent 0.5 parts, kaolin 28 parts, titanium dioxide 35 parts, benzidine yellow 20 parts, rubber scarlet 2 parts, promote 0.8 parts of agent DM, 0.5 parts of accelerator RPS-710, 0.5 parts of sulfur, 0.1 parts of anti-scorch agent;

[0021] The preparation method of the colored rubber composition that this embodiment relates to is used for tire sidewall, and its specific preparation process comprises the following steps:

[0022] (1) Batching and compounding: carry out compounding and compounding according to the raw material components and parts by weight of the colored rubber compositions used for tire ...

Embodiment 2

[0029] The colored rubber composition used in the tire sidewall involved in this embodiment, its raw material components and parts by weight of each component are: 30 parts of SVR-3L type rubber, 20 parts of KEP-350 type rubber, 20 parts of CIIR-1066 type rubber 50 parts, 2 parts of tackifying resin, 1.5 parts of stearic acid, 1 part of dispersant, 0.7 parts of non-polluting anti-aging agent, 25 parts of kaolin, 35 parts of titanium dioxide, 20 parts of benzidine yellow, 2 parts of rubber red, promote 0.8 parts of agent DM, 0.6 parts of accelerator RPS-710, 0.8 parts of sulfur, 0.1 parts of anti-scorch agent;

[0030] The preparation method of the colored rubber composition that this embodiment relates to is used for tire sidewall, and its specific preparation process comprises the following steps:

[0031] (1) Batching and compounding: carry out compounding and compounding according to the raw material components and parts by weight of the colored rubber compositions used for...

Embodiment 3

[0038] The colored rubber composition used in the sidewall of the tire involved in this embodiment, its raw material components and parts by weight of each component are: 40 parts of SVR-3L type rubber, 15 parts of KEP-350 type rubber, and 15 parts of CIIR-1066 type rubber 45 parts, tackifying resin 1.5 parts, stearic acid 2 parts, dispersant 2 parts, non-polluting anti-aging agent 1 part, kaolin 30 parts, titanium dioxide 35 parts, benzidine yellow 20 parts, rubber scarlet 2 parts, promote 0.9 parts of agent DM, 0.5 parts of accelerator RPS-710, 0.6 parts of sulfur, 0.1 parts of anti-scorch agent;

[0039] The preparation method of the colored rubber composition that this embodiment relates to is used for tire sidewall, and its specific preparation process comprises the following steps:

[0040] (1) Batching and compounding: carry out compounding and compounding according to the raw material components and parts by weight of the colored rubber compositions used for tire sidew...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical fields of rubber tires and chemical manufacturing, and relates to a colorful rubber composition for a tire sidewall and a preparation method of the colorful rubber composition. The colorful rubber composition for the tire sidewall is prepared from the following raw material ingredients in parts by weight: 30-40 parts of natural rubber, 10-20 parts of ethylene propylene terpolymer, 45-55 parts of chlorinated butyl rubber, 1-2 parts of tackifying resin, 1.5-2.5 parts of an activating agent without carbon black, 1-2 parts of a dispersant, 0.5-1 part of a no-pollution anti-aging agent, 25-30 parts of kaolin, 30-40 parts of titanium pigment, 19-24 parts of a coloring agent, 1-1.5 parts of an accelerant, 0.4-1 part of sulphur and 0.1 part of an anti-scorching agent. In combination with a three-phase mixing process in the preparation process, the problems of low flexing resistance, low aging resistance and high color fading possibility of a colorful rubber tire sidewall in the prior art are solved. The rubber composition not only meets the requirements of tire sidewall rubber for high flexing resistance and high aging resistance, but also meets the aesthetic vision for a user to modify tire appearance.

Description

technical field [0001] The invention belongs to the technical field of rubber tires and chemical manufacturing, and relates to a colored rubber composition for tire sidewalls and a preparation method thereof, which meet the requirements of tire sidewall rubbers with high flex resistance and high aging resistance, and satisfy users' requirements for tire appearance Aesthetic vision for grooming. Background technique [0002] The sidewall is an important part of the structural integrity of the tire. It protects the carcass from lateral physical and chemical damage, and is also the most eye-catching part of the tire. The development of tires in color has gone through the process of maintaining the original white color of the rubber at first, and adding various color additives to the colorful tires, because of their poor strength and tear resistance, poor aging resistance, high cost, After a long time of use, the rubber compound will gradually turn yellow and brown and other re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L7/00C08L23/16C08L91/06C08K13/02C08K5/09C08K3/34C08K3/22C08K3/06C08K5/47C08K5/3437C08K5/18B29B7/10B29B7/28
CPCC08L23/283B29B7/10B29B7/28C08L2201/08C08L2205/02C08L2205/035C08L7/00C08L23/16C08L91/06C08K13/02C08K5/09C08K3/346C08K2003/2241C08K3/06C08K5/47C08K5/3437
Inventor 陆中勇刘奇王成杰
Owner 山东新大陆橡胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com