Compound dressing with high liquid absorption performance and preparation method of compound dressing

A high-performance, high-absorbing technology, applied in absorbent pads, pharmaceutical formulations, pharmaceutical sciences, etc., can solve problems such as poor biocompatibility, poor mechanical properties, adverse environmental effects, etc., achieve high porosity, good controllability, Significant social benefits

Inactive Publication Date: 2017-01-25
QINGDAO CHENLAND MARINE BIOTECH CO LTD
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chitosan often faces several difficulties in the preparation of dressings, such as solubility, liquid absorption, bacteriostasis, comfort, etc. Although some patents have shown some research results, it is obvious that it needs to be studied as a large-scale production process, such as In Chinese patent CN 101816802 A, a chitosan-based medical dressing is prepared, but because the film formed by them is brittle and has poor mechanical properties, it is often necessary to improve its mechanical properties by blending with other materials; invention patent CN1431021A Disclosed is a chitosan-collagen sponge used for gynecological diseases. In the preparation process, acidic solutions such as hydrochloric acid or acetic acid are used to dissolve chitosan, and the acidic solution is used, which is likely to cause adverse effects on the environment and requires secondary vacuum freezing Drying increases cost; invention patent CN105477679 A discloses a preparation method of chitosan rapid hemostatic cotton based on polysaccharide crosslinking. Polysaccharide is poor, so it can only be used as a hemostatic material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound dressing with high liquid absorption performance and preparation method of compound dressing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh 1.0 g of sodium alginate and dissolve it in 140 mL of water, add 10 mL of sodium periodate solution (40 mg / mL) dropwise, and react with electromagnetic stirring at room temperature for 4 hours. Add 0.200 mL of ethylene glycol dropwise therein, stir and react for 1 hour, then use a dialysis bag with a molecular weight cut-off of 3500 to soak in deionized water for dialysis for 24 hours, during which the water is changed every 4 hours, and the vacuum equipment is freeze-dried for 48 hours to obtain Hydroformylated sodium alginate solid.

[0030] Then weigh 1.0 g of carboxymethyl chitosan and dissolve it in 30 mL of water. During the process, ultrasound or stirring is required to dissolve for about 30 minutes. At the same time, the following solution is prepared: 50 mg of the above-mentioned alginate sodium alginate is dissolved in 10 mL of water; 1.50 G glycerol was dissolved in 1 mL water, 0.30 g poloxamer 407 was dissolved in 9 mL water and 10 mL PBS. Next, add t...

Embodiment 2

[0033] Weigh 1.5 g of starch and dissolve it in 150 mL of water, add 10 mL of sodium periodate solution (80 mg / mL) dropwise, and react with electromagnetic stirring at room temperature for 2 hours. Add 0.40 mL of ethylene glycol dropwise therein, and react for 1 hour, then use a dialysis bag with a molecular weight cut-off of 3500 to soak in deionized water for dialysis for 24 hours, during which the water is changed every 4 hours, and the vacuum equipment is freeze-dried for 48 hours to obtain Aldehydated starch.

[0034]Then weigh 2.0 g of carboxymethyl chitosan and dissolve it in 60 mL of water. During the process, ultrasound or stirring is required to dissolve for about 30 minutes. At the same time, the following solution is prepared: 100 mg of the above-mentioned formaldehyde starch is dissolved in 20 mL of water; 1.5 g of glycerol Dissolved in 2 mL of water, 0.60 g of poloxamer 407 was dissolved in 20 mL of water. Next, add the prepared glycerin into the carboxymethyl c...

Embodiment 3

[0038] The preparation of the macromolecular cross-linked substance is the same as in Example 1.

[0039] Weigh 2.40 g of carboxymethyl chitosan and dissolve in 110 mL of water, 120 mg of alginate sodium alginate in 20 mL of water, 3.0 g of glycerol in 2 mL of water, and 0.60 g of poloxamer 407 in 38 mL of water , 12 mg of quaternized PEI was dissolved in 10 mL of water. Add glycerin to the above chitosan solution and stir for 5 min. Add the PEI solution to the chitosan solution and stir for 15 minutes. Then the sodium alginate solution was added dropwise into the chitosan solution and stirred for 25 min. Add the poloxamer solution into the chitosan solution, and stir at high speed for 60 minutes.

[0040] Fix the cotton polysaccharide woven fabric at the bottom of the coating machine, pour the liquid obtained by the above-mentioned high-speed stirring on the upper end of the non-woven fabric, set the coating height to 5mm, and perform composite coating, and freeze-dry the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to compound dressing with high liquid absorption performance and a preparation method of the compound dressing. The compound dressing is prepared from chitosan serving as a raw material and consists of a supporting layer and a functional layer, wherein the supporting layer is functional nonwoven cloth; the functional layer is prepared by performing water dissolving, macromolecular crosslinking, foaming, freeze drying and the like on carboxymethyl chitosan. The compound dressing is high in mechanical property and pore-forming property; furthermore, by the compound design of a dual-layer structure, the liquid absorption performance is higher than that of common dressing, and the compound dressing is suitable for perpendicular absorption application. Chitosan is a natural macromolecular polymer and belongs to aminopolysaccharide, so that the dressing is high in mechanical property, high in seepage absorption, and also high in biological compatibility, degradability and nontoxicity, can induce tissue regeneration and remodeling, can effectively promote healing of a wound, and is a more ideal healing promotion material.

Description

technical field [0001] The invention belongs to the field of medical devices, and relates to a composite dressing and a production process thereof, in particular to a non-woven dressing made of chitosan and cotton polysaccharide as raw materials, which is suitable for tissue repair with high mechanical strength and high liquid absorption. A biomedical material, the dressing is suitable for covering and treating burn wounds, trauma wounds, chronic ulcer wounds, decubitus wounds, infected wounds, and surgical wounds. Background technique [0002] Medical dressings are a class of clinical medical materials that temporarily cover burns, ulcers, wounds and other wounds. Its main function is to control the exudate of the wound and protect the wound from external sources such as bacteria and dust particles. With the accelerated pace of modern life and the increasing demand for medical care, the demand for medical dressings is also increasing year by year. From a global perspective,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/42
CPCA61L15/28A61L15/42A61L15/425A61L2400/04C08L5/04C08L5/08C08L3/02C08L5/00
Inventor 杨毅林莎莎李乘风
Owner QINGDAO CHENLAND MARINE BIOTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products