Heat treatment method of aluminum alloy

A heat treatment method and aluminum alloy technology, applied in the field of aluminum alloy material manufacturing, can solve the problems of sensitivity to intergranular corrosion, low strength of 6000 series aluminum alloys, affecting the life and safety of aircraft, etc., and achieve high resistance to intergranular corrosion, high the effect of strength

Inactive Publication Date: 2017-01-11
张家港市丰乐汽车设备有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, the proportion of 6000-series aluminum alloys used in aircraft manufacturing is significantly lower than that of 7000-series and 2000-series aluminum alloys
The primary reason for this phenomenon is the relatively low strength of 6000 series aluminum alloys.
Although artificially aged to the peak state (T6), the strength of 6000-series aluminum alloys is still much lower than that of 7000-series and 2000-series aluminum alloys, which cannot reflect the advantages of weight reduction; at the same time, 6000-series aluminum alloys still have serious Inter-corrosion sensitivity, which seriously affects the life and safety of aircraft

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention is further illustrated by the following examples: According to the following examples, the present invention can be better understood. However, those skilled in the art can easily understand that the specific material ratios, process conditions and results described in the examples are only used to illustrate the present invention, and should not and will not limit the present invention described in the claims.

[0016] In this embodiment, the aluminum alloy heat treatment method includes steps:

[0017] (1) Solid solution and quenching are carried out with the aluminum alloy plate as the raw material, the solution treatment temperature is 560°C, and the solution holding time is 40 minutes;

[0018] The material of the aluminum alloy sheet includes: 1% Cu; 0.8% Si; 0.5% Fe; 1.1% Mg; 0.6% Mn; 0.1% Cr; 0.2% Zn; 0.1% Ti, The balance is Al.

[0019] (2) After solution quenching, perform primary aging at 135°C / 6h, secondary aging at 170°C / 8h, and tert...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat treatment method of an aluminum alloy. The heat treatment method comprises the steps that (1) an aluminum alloy plate is used as a raw material to be subjected to solid solution and quenching, the solid solution treatment temperature is 560 DEG C, and the solid solution holding time is 40 min; and (2) after solid solution and quenching, primary aging under the conditions of 135 DEG C and 6 h, secondary aging under the conditions of 170 DEG C and 8 h and tertiary aging under the conditions of 150 DEG C and 8 h are sequentially carried out, and aging is carried out in an air circulation furnace. The aluminum alloy plate is subjected to three levels of aging heat treatment, and the aluminum alloy with high intergranular corrosion resisting performance and strength can be obtained.

Description

technical field [0001] The application belongs to the technical field of aluminum alloy material manufacturing, and in particular relates to a heat treatment method for aluminum alloy. Background technique [0002] Age-hardening aluminum alloy has low density, high specific strength, good corrosion resistance and plastic formability, and is an important lightweight structural material widely used in aircraft manufacturing, mainly including ultra-high strength 7000 series Al-Zn-Mg-Cu alloy (500-700MPa), high-strength 2000 series Al-Cu-Mg alloy (400-500MPa) and medium-strength 6000 series Al-Mg-Si-Cu alloy (300-400MPa), the representative alloy grades are 7075, 2024 and 6056. Compared with the 7000 series and 2000 series aluminum alloys, although the 6000 series aluminum alloys have the advantages of low material density and cost, ingot formability, plastic processing performance, excellent surface treatment performance and low tendency to stress corrosion cracking. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/047C22F1/04
Inventor 赵英
Owner 张家港市丰乐汽车设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com