Jewelry white surface treatment plating solution, preparation method and electroplating method thereof

A technology for surface treatment and jewelry, applied in the field of jewelry treatment, can solve the problems of poor corrosion resistance and affect the use effect, and achieve the effects of good corrosion resistance, low preparation cost and simple preparation method

Inactive Publication Date: 2017-01-04
江捷新 +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Treating the surface of jewelry to white is very popular with consumers, so people usually treat the surface of jewelry to white, but the existing treatment methods have poor corrosion resistance, and the white brightness of jewelry after wearing for a period of time It is not so high, so it is easy to affect its use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jewelry white surface treatment plating solution, preparation method and electroplating method thereof
  • Jewelry white surface treatment plating solution, preparation method and electroplating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to express the present invention more clearly, the present invention will be further described below in conjunction with the accompanying drawings.

[0035] Plating solution for jewelry white surface treatment of the present invention comprises the following components according to quality: ammonium sulfamate 70-100g, nickel sulfamate 10-25 g, palladium content 4.5-25 g in dinitrosodiammine palladium 7 g.

[0036] see figure 1 , the present invention also provides a kind of preparation method of jewelry white surface treatment plating solution, it is characterized in that, comprises the following steps:

[0037] Step Sa1, weighing about 90g of ammonium sulfamate and about 20g of nickel sulfamate into a 1L beaker;

[0038] Step Sa2, add 700ml of water to dilute and dissolve;

[0039] Step Sa3, add a stirrer, put the beaker into a heat-collecting constant temperature heating magnetic stirrer and heat and stir for 40 minutes; the temperature of this step is bet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a jewelry white surface treatment plating solution, a preparation method and an electroplating method thereof. The preparation method comprises the steps that about 90 g of ammonium sulfamate and about 20 g of nickel aminosulfonate are weighed and poured into a 1 L beaker; 700 ml of water is added for dilution and dissolution; a stirrer is added, the beaker is added into a thermal-collection type constant temperature heating magnetic stirrer for performing heating and stirring for 40 min; the mixture is taken out, and then dinitroso-diamine palladium is added, wherein the content is palladium is about 6 g; water is added to reach about 950 ml and the mixture is added into the thermal-collection type constant temperature heating magnetic stirrer for performing heating and stirring for 15 min; the beaker is taken out, a solution is filtered, the filtered solution is subjected to testing of PH value through PH paper of the specification of 6-9, if the PH value is 8-9, the plating solution is obtained; if the PH value is not 8-9, a dropper is used for taking ammonium hydroxide, a half amount of the ammonium hydroxide in the dropper is added, a glass rod is used for performing stirring for 203 min, then, the PH value is tested, and the steps are repeatedly executed till the PH value is 8-9; finally, pure water is added to supplement the solution to reach 1 L so that the plating solution can be formed.

Description

technical field [0001] The invention relates to the technical field of jewelry treatment, in particular to a white surface treatment plating solution for jewelry, a preparation method and an electroplating method thereof. Background technique [0002] Treating the surface of jewelry to white is very popular with consumers, so people usually treat the surface of jewelry to white, but the existing treatment methods have poor corrosion resistance, and the white brightness of jewelry after wearing for a period of time It is not so high, so it is easy to affect its use effect. Contents of the invention [0003] Aiming at the deficiencies in the above technologies, the present invention provides a white surface treatment plating solution for jewelry, a preparation method and an electroplating method thereof. The white surface electroplating effect is good, the electroplating brightness is high, and the color will not fade after long-term use. The phenomenon. [0004] In order ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D3/56C25D5/34
CPCC25D3/562C25D5/34
Inventor 江捷新曹霖
Owner 江捷新
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap