A kind of nickel base superalloy and preparation method thereof

A technology for high-temperature alloys and metal products, which is applied in the field of high-temperature alloys and can solve problems such as fatigue strength, yield strength and ultimate tensile strength mechanical properties decline

Active Publication Date: 2018-05-08
CENT SOUTH UNIV +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical properties of nickel-based superalloys such as fatigue strength, yield strength and ultimate tensile strength will decrease significantly during high-temperature long-term service.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nickel base superalloy and preparation method thereof
  • A kind of nickel base superalloy and preparation method thereof
  • A kind of nickel base superalloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0205] The present invention has no special limitation on the sources of the raw materials used in the examples, they can be purchased from the market or prepared according to the preparation methods well known to those skilled in the art.

[0206] The present invention has no special restrictions on the preparation method of the high-stable powder metallurgy high-temperature nickel alloy described in the examples and the source of other raw materials, which can be prepared according to the preparation method known to those skilled in the art or purchased on the market.

[0207] The present invention prepares the powder metallurgy high-temperature nickel alloy CSU-A3 according to a certain alloy composition ratio, and compares the composition with the existing typical second-generation and third-generation powder metallurgy superalloys. The comparison results are shown in Table 1. 1 is the composition comparison between the superalloy obtained in Example 1 of the present invent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides nickel-base superalloy and a preparation method thereof, and in particular relates to powder metallurgy nickel alloy with high stability, and articles made from the powder metallurgy nickel alloy. The nickel-base superalloy is prepared from the following components by mass percent: 18.5-19.5% of Co, 12.75-13.25% of Cr, 2.8-3.2% of Al, 3.5-3.9% of Ti, 3.75-4.25% of W, 3.75-4.25% of Mo, 0.9-1.1% of Ta, 1.1-1.3% of Nb, 0.17-0.23% of Hf, 0.04-0.06% of C, 0.003-0.015% of B, 0.03-0.07% of Zr and the balance of Ni. The superalloy designed by the invention has better structure stability and high-temperature strength, and the temperature tolerance of the alloy is further improved.

Description

technical field [0001] The invention relates to the technical field of superalloys, in particular to a nickel-based superalloy and a preparation method thereof. Background technique [0002] Generally speaking, superalloys refer to high-temperature metal materials that can work for a long time above 600 °C and under certain stress conditions. performance. With the rapid development of industry, superalloys have shown good application prospects in various fields, and are mainly used to manufacture high-temperature components such as turbine blades, guide vanes, turbine disks, high-pressure compressor disks, and combustion chambers of gas turbine engines. [0003] According to the preparation process, superalloy materials can be divided into deformed superalloys, cast superalloys and powder metallurgy superalloys. Superalloy materials can be divided into iron-based superalloys, nickel-based superalloys and cobalt-based superalloys according to matrix elements. Due to the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/03
Inventor 不公告发明人
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products