High tensile strength rubber composition and preparation method thereof

A technology of high tensile strength and rubber composition, applied in the field of rubber, can solve the problems of difficult synthesis, limited application and high cost, and achieve the effects of improving oil resistance and solvent resistance, small volume resistivity and low hardness

Inactive Publication Date: 2016-12-14
ANHUI WEIWEI RUBBER PARTS GRP
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Fluorosilicone rubber is a new type of special rubber, which combines the advantages of fluororubber and silicone rubber. Compared with fluororubber or silicone rubber, fluorosilicone rubber is more difficult to synthesize, so the cost is higher, which limits its electrical conductivity. Application in rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High tensile strength rubber composition and preparation method thereof
  • High tensile strength rubber composition and preparation method thereof
  • High tensile strength rubber composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The present invention proposes a kind of high tensile strength rubber composition, and its raw material comprises by weight:

[0028]

[0029]

[0030] The reinforcing agent is carbon black, the anti-aging agent is N-phenyl-α-aniline, the vulcanizing agent is dicumyl peroxide, the silicone rubber is methyl silicone rubber, the fluororubber is polyolefin fluororubber, and the conductive filler is graphite .

[0031] The invention also discloses a preparation method of a high tensile strength rubber composition, comprising the following steps:

[0032] Step 1: Carry out low-temperature mastication of silicone rubber and fluororubber respectively through an open mill;

[0033] Step 2: plasticize the silicone rubber, fluororubber, conductive filler, nano-zinc oxide, rosin, sulfur, anti-aging agent, reinforcing agent, calcium carbonate, zinc diethyldithiocarbamate, vulcanizing agent, The silane coupling agent is mixed, and the resulting mixture is mixed twice;

[00...

Embodiment 2

[0037] The present invention proposes a kind of high tensile strength rubber composition, and its raw material comprises by weight:

[0038]

[0039]

[0040] The reinforcing agent is carbon black, the anti-aging agent is N-phenyl-α-aniline, the vulcanizing agent is dicumyl peroxide, the silicone rubber is methyl silicone rubber, the fluororubber is polyolefin fluororubber, and the conductive filler is graphite .

[0041] The invention also discloses a preparation method of a high tensile strength rubber composition, comprising the following steps:

[0042] Step 1: Carry out low-temperature mastication of silicone rubber and fluororubber respectively through an open mill;

[0043] Step 2: plasticize the silicone rubber, fluororubber, conductive filler, nano-zinc oxide, rosin, sulfur, anti-aging agent, reinforcing agent, calcium carbonate, zinc diethyldithiocarbamate, vulcanizing agent, The silane coupling agent is mixed, and the resulting mixture is mixed twice;

[00...

Embodiment 3

[0047] The present invention proposes a kind of high tensile strength rubber composition, and its raw material comprises by weight:

[0048]

[0049]

[0050] The reinforcing agent is carbon black, the anti-aging agent is N-phenyl-α-aniline, the vulcanizing agent is dicumyl peroxide, the silicone rubber is methyl silicone rubber, the fluororubber is polyolefin fluororubber, and the conductive filler is silver Aluminum clad.

[0051] The invention also discloses a preparation method of a high tensile strength rubber composition, comprising the following steps:

[0052] Step 1: Carry out low-temperature mastication of silicone rubber and fluororubber respectively through an open mill;

[0053] Step 2: plasticize the silicone rubber, fluororubber, conductive filler, nano-zinc oxide, rosin, sulfur, anti-aging agent, reinforcing agent, calcium carbonate, zinc diethyldithiocarbamate, vulcanizing agent, The silane coupling agent is mixed, and the resulting mixture is mixed tw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high tensile strength rubber composition. The high tensile strength rubber composition is prepared from, by weight, 50-100 parts of silicon rubber, 20-60 parts of fluororubber, 5-10 parts of nanometer zinc oxide, 30-60 parts of conductive filler, 1-5 parts of a sulfurizing agent, 1-5 parts of rosin, 5-10 parts of sulphur, 10-20 parts of calcium carbonate, 1-5 parts of diethyldithiocarbamate zinc thiocarbamate, 3-15 parts of a silane coupling agent, 10-20 parts of an anti-aging agent and 10-20 parts of a reinforcing agent. The silicon rubber, the fluororubber, the conductive filler, the anti-aging agent, the reinforcing agent, the sulfurizing agent and the silane coupling agent are made into the conductive rubber composition with the good characteristics of the silicon rubber and the fluororubber, and the high tensile strength rubber composition has the advantages that the silicon rubber is small in volume resistivity, small in hardness, resistant to high and low temperature and aging, good in processing and manufacturing technological performance and capable of achieving the oil resistance and solvent resistance of the fluororubber, the volume change rate is only 1.2%, the volume change rate of traditional silicon rubber through the same test is 25%, and the volume change rate of the fluororubber is 3%, and the sample obtained through the technical scheme remarkably improves oil resistance and solvent resistance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a rubber composition with high tensile strength and a preparation method thereof. Background technique [0002] Rubber material is a polymer material that can quickly recover from deformation under large deformation. It is one of the important basic industries of the national economy. Conductive rubber is based on rubber, filled with mixed conductive fillers and cross-linking agents. It has good conductivity and filling performance, and is widely used in the fields of electronics, telecommunications, electric power, military industry, aviation, aerospace and ships, etc., and is mostly used for sealing and sealing of electronic and microwave waveguide systems such as chassis, cabinets, and shelters. Electromagnetic shielding occasions. Most of the existing conductive rubbers are based on silicone rubber. Compared with general conductive rubber, conductive silicone rubber has the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L83/07C08L27/12C08K13/06C08K9/10C08K13/02C08K3/04C08K5/18C08K5/14C08K3/26C08K3/22C08K3/08
CPCC08L83/04C08K2201/011C08K2201/014C08L2201/08C08L2205/03C08L27/12C08K13/06C08K9/10C08K3/04C08K5/18C08K5/14C08K2003/265C08K2003/2296C08K2003/0812C08K13/02
Inventor 李俊梁天也李斌商李徐兵
Owner ANHUI WEIWEI RUBBER PARTS GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap