Ceramic dispersing agent and preparation method thereof
A technology of ceramic dispersant and initiator, which is applied in the field of ceramic dispersant and its preparation, can solve the problems of side effects, easy solidification, and narrow debonding range, and achieve the reduction of the use of reinforcing agents, good fluidity and viscosity, and production The effect of simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0026] A kind of preparation method of ceramic dispersant, realizes by following steps:
[0027] (1) After adding allyl thiourea, sodium cardanol sulfonate, acid regulator and water into the reactor, start stirring, and start heating;
[0028] (2) When the temperature rises to 100-120°C, start to add glyoxal dropwise for 1-5 hours;
[0029] (3) Add cardanol epoxy propylene ether and isopentenol polyoxyethylene ether in the reaction kettle again, start to drip the initiator solution that mass percent concentration is 1~10% after waiting to stir, this initiator solution It is prepared from the initiator and part of the water; the dropping time is controlled at 0.5-3 hours, and the temperature is controlled at 95-120°C during the dropping;
[0030] (4) After the dropwise addition, keep the temperature and continue to react for 1 to 4 hours, add an alkaline regulator for neutralization, add the remaining water after the neutralization is completed, cool down and discharge the mat...
Embodiment 1
[0033] A kind of ceramic dispersant of the present invention is made of the raw material components of following proportioning by weight:
[0034]
[0035] Its preparation method is realized through the following steps:
[0036] (1) Add 2 parts of allylthiourea, 6 parts of sodium cardanol sulfonate, 3 parts of hydroxyethylidene diphosphonic acid and 10 parts of water into the reactor, start stirring, and start heating;
[0037] (2) When the temperature rises to 110°C, start to add 9 parts of glyoxal dropwise for 1.5 hours;
[0038] (3) add 2 parts of cardanol epoxy propylene ethers, 1 part of isopentenol polyoxyethylene ethers in reactor again, start to drip the sodium persulfate solution that mass percent concentration is 5% after waiting to stir evenly, this The sodium persulfate solution is prepared from 1 part of sodium persulfate and 19 parts of water; the dropping time is controlled at 1.5 hours, and the temperature is controlled at 110°C during the dropping;
[003...
Embodiment 2
[0041] A ceramic dispersant, made of the following raw material components in parts by weight:
[0042]
[0043] Its preparation method is realized through the following steps:
[0044] (1) Add 3 parts of allyl thiourea, 7 parts of sodium cardanol sulfonate, 3 parts of 2-phosphonic acid butane-1,2,4-tricarboxylic acid and 10 parts of water into the reaction kettle and start stirring, and start to heat up;
[0045] (2) When the temperature rises to 112°C, start to drop 10 parts of glyoxal for 2 hours;
[0046] (3) add 2 parts of cardanol epoxy propylene ethers, 1 part of isopentenol polyoxyethylene ethers in reactor again, start to drip the sodium persulfate solution that mass percent concentration is 2% after waiting to stir evenly, this The sodium persulfate solution is prepared from 1 part of sodium persulfate and 49 parts of water; the dropping time is controlled at 2 hours, and the temperature is controlled at 115°C during the dropping;
[0047] (4) After the dropwis...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction