A kind of grease composition and preparation method thereof

A technology of grease composition and crosslinking method, which is applied in lubricating compositions, additives, petroleum industry, etc., can solve problems such as poor viscosity-temperature performance, achieve excellent viscosity-temperature performance, not easy to change color, and reduce interfacial friction Effect

Active Publication Date: 2019-08-20
CHINA PETROLEUM & CHEM CORP +1
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a kind of grease composition with excellent viscosity-temperature performance, a kind of preparation method of grease composition and by this method in order to overcome the relatively poor defect of viscosity-temperature performance of existing grease composition. Prepared grease composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of grease composition and preparation method thereof
  • A kind of grease composition and preparation method thereof
  • A kind of grease composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method of the lubricating grease composition provided by the present invention comprises mixing and dispersing base oil and styrene-butadiene rubber particles to be dispersed with a crosslinked structure prepared by a radiation crosslinking method, and relative to 100 parts by weight of the base oil, the amount of the styrene-butadiene rubber particles to be dispersed is 10-180 parts by weight.

[0030] According to the preparation method of the lubricating grease composition provided by the present invention, as mentioned above, relative to 100 parts by weight of the base oil, the amount of the styrene-butadiene rubber particles to be dispersed is 10-180 parts by weight, but in order to make the base oil Play a better synergistic effect with the styrene-butadiene rubber particles to be dispersed, and then make the resulting grease composition have better viscosity-temperature properties, preferably, relative to 100 parts by weight of the base oil, the to...

Embodiment approach

[0040] The present invention is not particularly limited to the manner of mixing and redispersing, as long as the styrene-butadiene rubber particles to be dispersed can be effectively dispersed in the base oil, thereby obtaining a mixture with the base oil as the continuous phase and the styrene-butadiene rubber particles as the dispersed phase. phase grease composition. According to a preferred embodiment of the present invention, the mixing and dispersing mode includes:

[0041] (1) adding the styrene-butadiene rubber particles to be dispersed in the base oil and mixing by mechanical stirring, so that the styrene-butadiene rubber particles to be dispersed are dispersed or suspended in the base oil to obtain a preliminary dispersed composition;

[0042](2) redispersing the initially dispersed composition until the average particle diameter of the dispersed styrene-butadiene rubber particles reaches in the range of 20-2000nm, preferably in the range of 50-1000nm, more preferab...

Embodiment 1

[0060] This example is used to illustrate the grease composition provided by the present invention and its preparation method.

[0061] 100 parts by weight of mineral base oil Ib150 and 10 parts by weight of styrene-butadiene rubber particles VP101 to be dispersed are mixed and mechanically stirred evenly, and then homogenized and circulated five times in a three-roller mill. When the gap between the rolls is as small as 10μm, a mixed material is obtained. The above mixed material was kept in a high-temperature oven at 150°C for 4 hours, and then passed through a three-roll mill for homogenization and circulation five times. The roll speed during homogenization was 280 rpm, and the gap between the rolls was as small as 5 μm during dispersion to obtain a grease combination. See Table 1 and Table 2 for their dynamic viscosity, oil separation and lubricating properties. In addition, the microscopic morphology of the grease composition is as follows figure 2 shown. from figu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of lubricating grease, and particularly provides a lubricating grease composition and a preparation method thereof. The lubricating grease composition contains base oil and butadiene styrene rubber particles, the butadiene styrene rubber particles are dispersed in the base oil and prepared through an irradiation crosslinking method and have a cross-linked structure, the base oil serves as a continuous phase, the butadiene styrene rubber particles serve as a dispersion phase, and relative to 100 parts by weight of base oil, the content of the butadiene styrene rubber particles ranges from 10 parts by weight to 180 parts by weight. The viscosity of the lubricating grease composition can be effectively adjusted along with temperature changes, the temperature application range is wide, and compared with a lubricating grease composition containing butadiene styrene rubbers obtained through peroxide crosslinking, the kinematic viscosity of the lubricating grease composition is low at the temperature of 40 DEG C, and the kinematic viscosity of the lubricating grease composition is high at the temperature of 100 DEG C. In addition, the lubricating grease composition has excellent antiwear and antifriction performance.

Description

technical field [0001] The invention relates to a lubricating grease composition, a preparation method of the lubricating grease composition and a lubricating grease composition prepared by the method. Background technique [0002] Grease is generally a semi-solid and solid lubricant obtained by dispersing a thickener in one or several lubricating base oils and undergoing a saponification reaction. Common grease thickeners are divided into soap-based, non-soap-based and hydrocarbon-based types. Soap-based thickeners are mostly fatty acid salts, such as calcium stearate and 12-hydroxystearic acid calcium salt. Thickeners include organic polyurea, inorganic compounds, etc., and hydrocarbon-based thickeners are generally paraffins. Grease prepared with the above thickeners can generally meet the needs of ordinary use, but with the rapid development of modern industry, the emerging high-end mechanical equipment has higher and higher requirements for grease performance, and need...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M159/12C10M169/04C10N30/04C10N30/06C10N30/08
Inventor 张晓红蔡传伦赖金梅乔金樑宋志海戚桂村李秉海王湘高建明张红彬蒋海斌何谷茹越
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com