Two-component transparent fireproof coating material preparation method

A fire-resistant coating, a two-component technology, applied in the direction of fire-resistant coatings, coatings, etc., can solve the problems of cracking of the coating film, poor flexibility of the coating film, etc., and achieve the effect of loose reaction conditions, low cost and good flexibility

Inactive Publication Date: 2016-11-23
泉州市合创涂料科技有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One of the major factors limiting the practical application of transparent decorative fire retardant coatings is that the flexibility of the coating film is too poor, and the coating film will crack soon after it is applied to the substrate and cured.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Dissolve 50g of polyphosphoric acid in 200ml of dioxane, heat and stir until the polyphosphoric acid is evenly dissolved. 25 g of pentaerythritol was added to the system, and the temperature was raised to 80° C. for reaction. After 6 hours of reaction, the solvent was evaporated using a rotary evaporator. The product was grafted with 25g PEG200 under the reaction condition of 100°C for 8 hours to obtain polyethylene glycol grafted polyphosphate;

[0024] (2) Make a 50% aqueous solution of the prepared grafted polyphosphate, weigh 400g, and blend and stir for 30 minutes. After the stirring is completed, the bubbles in the paint will naturally dissipate, and it will be a two-component transparent finish. type fire retardant coating.

Embodiment 2

[0026] (1) Dissolve 40g of polyphosphoric acid in 300ml of tetrahydrofuran, heat and stir until the polyphosphoric acid is evenly dissolved. 40 g of pentaerythritol was added to the system, and the temperature was raised to 90° C. for reaction. After 10 h of reaction, the solvent was evaporated using a rotary evaporator. The product was grafted with 20g PEG300 under the reaction condition of 120°C for 12 hours to obtain polyethylene glycol grafted polyphosphate;

[0027] (2) Make the prepared grafted polyphosphate into 50% aqueous solution, weigh 400g of water-based hexamethylol melamine formaldehyde resin, blend and stir for 30min, and wait for the bubbles in the paint to dissipate naturally after stirring. It is a two-component transparent finish type fire retardant coating.

Embodiment 3

[0029] (1) Dissolve 45g of polyphosphoric acid in 250ml of dimethylformamide, heat and stir until the polyphosphoric acid is evenly dissolved. 32.5 g of pentaerythritol was added to the system, and the temperature was raised to 85° C. for reaction. After 8 hours of reaction, the solvent was evaporated using a rotary evaporator. The product was grafted with 22.5g PEG400 under the reaction condition of 110°C for 10 hours to obtain polyethylene glycol grafted polyphosphate;

[0030] (2) Make the prepared grafted polyphosphate into 50% aqueous solution, weigh 400g of water-based hexamethylol melamine formaldehyde resin, blend and stir for 30min, and wait for the bubbles in the paint to dissipate naturally after stirring. It is a two-component transparent finish type fire retardant coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a two-component transparent fireproof coating material preparation method, which specifically comprises that a polyglycol-grafted polyphosphate is prepared from polyphosphoric acid, pentaerythritol and polyethylene glycol through a solution synthesis method, an aqueous solution or absolute alcohol solution having a certain concentration is prepared from the polyglycol-grafted polyphosphate, and the obtained aqueous solution or absolute alcohol solution and an aqueous amino resin are subjected to blending stirring to obtain the two-component transparent facing fireproof coating material. According to the present invention, the preparation method is simple and feasible, and has the low in cost, and with the prepared two-component transparent facing fireproof coating material, the flexibility of the coating film is substantially improved on the basis of assurance of the excellent fire resistance of the coating material.

Description

technical field [0001] The invention relates to a preparation method of a two-component transparent fireproof coating. Background technique [0002] Coating decorative fire retardant paint is currently the best means of wood fire prevention. When wood is exposed to fire, it can achieve the purpose of prolonging the fire resistance of wood and slowing down the spread of fire, so that there is enough time for fighting and reducing the loss caused by fire as much as possible. Decorative fire retardant coatings are generally divided into two types: intumescent and non-expandable. Since the intumescent fireproof system can rapidly foam to form a porous carbonized layer tens or even hundreds of times the thickness of the original coating when it is exposed to fire, which effectively blocks the transfer of heat and isolates the substrate from the air. The fireproof performance is better than that of the non-expandable system. Therefore, it has been extensively researched and appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/32C09D5/18C09D7/12
Inventor 陈登龙
Owner 泉州市合创涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com