Black-base blue-spot compound Jun porcelain glaze material

A kind of glaze and black base technology, which is applied in the field of black base and blue spot composite Jun porcelain glaze, which can solve the problems of poor wear resistance and mechanical resistance of the glaze surface, insufficient jade feeling, and easy cracks on the surface, etc., and achieve good gloss , Good fluidity, not easy to foam

Inactive Publication Date: 2016-11-23
温书强
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, there are few formulations and preparation methods of the black-bottomed blue-spot composite Jun porcelain glaze, and the prepared black-bottomed blue-spot composite Jun porcelain glaze is prone to cracks, and the glaze surface has poor wear resistance and mechanical resistance. , lack of sense of jade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of composite Jun porcelain glaze with black base and blue spot, which is composed of black base glaze and blue spot glaze. The black base glaze is made of the following raw materials in parts by weight: 8 parts of ferric oxide, 70 parts of silicon dioxide, 12 parts of aluminum oxide, 8 parts of calcium oxide, 1.5 parts of magnesium oxide, 3 parts of potassium oxide, and 2 parts of sodium oxide;

[0031] The blue spot glaze is made of the following raw materials in parts by weight: 2 parts of copper oxide, 1.5 parts of phosphorus pentoxide, 1.5 parts of titanium oxide, 65 parts of silicon dioxide, 4 parts of aluminum oxide, calcium oxide 15 parts, magnesium oxide 1.5 parts, potassium oxide 2 parts, sodium oxide 3 parts, zinc oxide 3 parts.

[0032] A method for preparing black-bottomed blue-spotted Jun porcelain glaze with the above-mentioned black-bottomed blue-spotted composite Jun porcelain glaze:

[0033] (1) Glazing: Put the green body into the glaze slurry ...

Embodiment 2

[0039]A kind of composite Jun porcelain glaze with black base and blue spot, which is composed of black base glaze and blue spot glaze. The black base glaze is made of the following raw materials in parts by weight: 12 parts of ferric oxide, 80 parts of silicon dioxide, 15 parts of aluminum oxide, 10 parts of calcium oxide, 2 parts of magnesium oxide, 5 parts of potassium oxide, 3 parts of sodium oxide;

[0040] The blue spot glaze is made of the following raw materials in parts by weight: 3 parts of copper oxide, 2 parts of phosphorus pentoxide, 2 parts of titanium oxide, 70 parts of silicon dioxide, 5 parts of aluminum oxide, calcium oxide 20 parts, magnesium oxide 2 parts, potassium oxide 3 parts, sodium oxide 4 parts, zinc oxide 4 parts.

Embodiment 3

[0042] A kind of composite Jun porcelain glaze with black base and blue spot, which is composed of black base glaze and blue spot glaze. The black base glaze is made of the following raw materials in parts by weight: 5 parts of ferric oxide, 60 parts of silicon dioxide, 8 parts of aluminum oxide, 5 parts of calcium oxide, 1 part of magnesium oxide, 2 parts of potassium oxide, and 1 part of sodium oxide;

[0043] The blue spot glaze is made of the following raw materials in parts by weight: 1 part of copper oxide, 1 part of phosphorus pentoxide, 1 part of titanium oxide, 60 parts of silicon dioxide, 3 parts of aluminum oxide, calcium oxide 10 parts, 1 part magnesium oxide, 1 part potassium oxide, 2 parts sodium oxide, 2 parts zinc oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a black-base blue-spot compound Jun porcelain glaze material. The compound Jun porcelain glaze material comprises a black-base glaze material and a blue-spot glaze material, wherein the black-base glaze material is prepared from the following raw materials in parts by weight: 5-12 parts of iron sesquioxide, 60-80 parts of silicon dioxide, 8-15 parts of aluminum sesquioxide, 5-10 parts of calcium oxide, 1-2 parts of magnesium oxide, 2-5 parts of potassium oxide and 1-3 parts of sodium oxide. The black-base blue-spot compound Jun porcelain glaze material is very transparent, has third dimension and good liquidity and luster and is unlikely to bubble; and the black-base glaze material has stable color and uniform luster, after a blank is coated with the black-base glaze material, other place on the surface can be coated with the blue-spot glaze material, and the black-base blue-spot Jun porcelain glaze can be sintered with basically consistent pattern. Compared with the prior art, the black-base blue-spot compound Jun porcelain glaze material has the advantages that the great progress is made, the sintered black-base blue-spot compound Jun porcelain glaze has good luster, few cracks and strong mechanical resistance.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain manufacture, and in particular relates to a composite Jun porcelain glaze with blue spots on a black background. Background technique [0002] Jun porcelain is based on the thickness of the glaze. Its color is either sunken under the glaze, suspended in the glaze, or floating on the surface of the glaze. The glaze is thick and lively, and the glaze layer is opalescent and moist. Jun porcelain is transformed into a god by the kiln, and the natural transformation of the kiln is the essence of Jun porcelain art, and it is also the rarity of Jun porcelain that is famous all over the world and famous in the porcelain forest. The same kind of glaze is applied during firing, and once fired, it will be colorful, that is, "one color when entering the kiln, and many colors when leaving the kiln". The ever-changing kiln transformation effect forms the magic of infinitely changing colors, purple in red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/89C04B41/86
CPCC03C8/00C04B41/5022C04B41/52C04B41/86C04B41/89C04B41/504C04B41/4539C04B41/0072
Inventor 温书强
Owner 温书强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com