Modified bamboo fiber reinforced composite polypropylene-based aromatic cupboard board and preparation method thereof

A polypropylene-based, reinforced composite technology, applied in fiber treatment, plant fiber, fiber chemical characteristics, etc., can solve the problems of fiber damage, damage to the mechanical strength of materials, and failure to achieve reinforcement effects, etc., to achieve high bamboo-plastic ratio, mechanical High strength, improve the damage effect

Inactive Publication Date: 2016-11-09
ZBOM HOME COLLECTION CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The article "Surface Energy Analysis of Bamboo Fiber and Its Reinforced Mechanical Properties of PP Composite Materials" takes PP as an example. Bamboo fiber is subjected to alkali treatment-silane coupling agent treatment, and then it is composited with PP and hot-pressed. The bamboo fiber obtained by this method is Although the compatibility and wettability of fibers with PP has been improved, high-concentration alkaline solutions will damage the fibers and destroy the mechanical strength of the material, failing to achieve a satisfactory reinforcement effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A modified bamboo fiber-reinforced composite polypropylene-based aromatic cabinet board. The bamboo-plastic board is made of the following raw materials in parts by weight: modified bamboo fiber 50, polypropylene 20, polyphenylene sulfide 5, maleic anhydride grafted Polypropylene 4, guaiac wood oil 0.4, zinc methacrylate 1, hectorite 0.4, cetyltrimethylammonium bromide 0.1, hydrogenated castor oil 1, antioxidant 0.1, ionic liquid 5, deionized water 10.

[0019] Wherein the preparation method of the modified bamboo fiber is: first put the bamboo fiber into the sodium hydroxide solution with a concentration of 5% and soak it for 30 minutes, then filter and wash with water until it is neutral and completely dry, and the resulting product is put into titanic acid with a concentration of 1%. Ester coupling agent / ethanol solution was mixed and soaked for 2 hours, filtered after the treatment, and the obtained material was dried, and then put into a polyethyleneimine aqueous s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified bamboo fiber reinforced composite polypropylene-based aromatic cupboard board. The bamboo-plastic board is prepared from raw materials in parts by weight as follows: 50-60 parts of modified bamboo fibers, 20-30 parts of polypropylene, 5-10 parts of polyphenylene sulfide, 4-6 parts of maleic anhydride grafted polypropylene, 0.4-0.5 parts of guaiac wood oil, 1-2 parts of zinc methacrylate, 0.4-0.5 parts of hectorite, 0.1-0.2 parts of hexadecyl trimethyl ammonium bromide, 1-2 parts of hydrogenated castor oil, 0.1-0.2 parts of an antioxidant, 5-8 parts of an ionic liquid and 10-20 parts of deionized water.

Description

technical field [0001] The invention relates to the technical field of bamboo-plastic materials, in particular to a modified bamboo fiber-reinforced composite polypropylene-based aromatic cabinet board and a preparation method thereof. Background technique [0002] Cabinets are a very common type of storage furniture in daily homes, and they are also materials that are widely used in the market for home building materials. With the changes in the needs of consumers in different age groups, the requirements for cabinets are no longer just strong and durable, and the products are environmentally friendly. Sex, texture, etc. have gradually become the focus of consumers' attention. At the same time, rational use of resources and sustainable development of the industry are also the development direction of the production industry. [0003] Cabinet boards are an extremely important part of cabinet components, which directly affect consumers' purchase choices. At present, cabinet b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/12C08L81/02C08L51/06C08L91/00C08K13/06C08K9/04C08K3/34D06M11/38D06M13/503D06M15/61D01F8/06D01F8/16D01F1/10D04H1/541D06M101/06
CPCC08L97/02C08L2205/025C08L2205/035C08L2205/16D01F1/10D01F8/06D01F8/16D04H1/541D06M11/38D06M13/503D06M15/61D06M2101/06C08L23/12C08L81/02C08L51/06C08L91/00C08K13/06C08K9/04C08K3/34
Inventor 夏大庆孔令根王平王安勇戚明永王丹
Owner ZBOM HOME COLLECTION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap