Anticorrosion high-temperature-resistance artificial ebony and manufacturing method thereof

A technology of artificial ebony and high temperature resistance, applied in the field of artificial wood processing, can solve the problems of less development, gap in use performance, lack of ebony, etc., and achieve the effects of low synthesis cost, good economic value and beautiful appearance

Inactive Publication Date: 2016-11-09
TAICANG HONGSHAN ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] As ebony is a non-renewable resource, the amount of development is less and less. At present, no material that can completely replace ebony has been found, resulting in a serious shortage of ebony in the market.
[0006] At present, imitation ebony on the market is mainly through surface dyeing, multi-layer extrusion, injection of alloys to increase wood hardness and other means; but these methods have a certain gap with natural ebony in terms of appearance and performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An anti-corrosion and high-temperature-resistant artificial ebony, comprising the following raw materials in weight ratio:

[0034] Phenolic resin: 90 parts, sawdust: 42 parts, multi-wall carbon tube: 0.52 parts, glass fiber: 7.5 parts, dicumyl peroxide: 2 parts, azodicarbonamide: 6 parts, wood grain masterbatch: 0.3 Parts, zinc oxide: 1.5 parts, calcium carbonate: 2.5 parts, colorant: 1.6 parts, stabilizer: 4 parts, foaming agent: 2.54 parts, lubricant: 4.2 parts.

[0035] The invention provides an anti-corrosion and high-temperature resistant artificial ebony. The multi-walled carbon tube has good mechanical properties, increases the mechanical properties of the material and also increases the carbon content of the material, and optimizes the overall performance of the material; by adding glass The fiber increases the toughness and strength of the artificial ebony material, and the combination of the glass fiber and the phenolic resin is very high; the wood grain mast...

Embodiment 2

[0051] An anti-corrosion and high-temperature-resistant artificial ebony, comprising the following raw materials in weight ratio:

[0052] Phenolic resin: 80 parts, wood chips: 49 parts, multi-walled carbon tubes: 0.1 parts, glass fiber: 10 parts, dicumyl peroxide: 1.2 parts, azodicarbonamide: 7.8 parts, wood grain masterbatch: 0.1 parts Parts, zinc oxide: 1 part, calcium carbonate: 2.85 parts, coloring agent: 1.2 parts, stabilizer: 3 parts, foaming agent: 2.9 parts, lubricant: 3 parts.

[0053] The invention provides an anti-corrosion and high-temperature resistant artificial ebony. The multi-walled carbon tube has good mechanical properties, increases the mechanical properties of the material and also increases the carbon content of the material, and optimizes the overall performance of the material; by adding glass The fiber increases the toughness and strength of the artificial ebony, and the glass fiber has a very high combination with the phenolic resin; the wood grain m...

Embodiment 3

[0069] An anti-corrosion and high-temperature-resistant artificial ebony, comprising the following raw materials in weight ratio:

[0070] Phenolic resin: 100 parts, sawdust: 32 parts, multi-wall carbon tube: 0.9 parts, glass fiber: 5 parts, dicumyl peroxide: 3 parts, azodicarbonamide: 4.1 parts, wood grain masterbatch: 0.5 parts Parts, zinc oxide: 1.95 parts, calcium carbonate: 2 parts, colorant: 1.9 parts, stabilizer: 5 parts, foaming agent: 2 parts, lubricant: 5 parts.

[0071] The invention provides an anti-corrosion and high-temperature resistant artificial ebony. The multi-walled carbon tube has good mechanical properties, increases the mechanical properties of the material and also increases the carbon content of the material, and optimizes the overall performance of the material; by adding glass The fiber increases the toughness and strength of the artificial ebony material, and the combination of the glass fiber and the phenolic resin is very high; the wood grain mast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides anticorrosion high-temperature-resistance artificial ebony. The anticorrosion high-temperature-resistance artificial ebony is prepared from phenolic resin, sawdust, multi-walled carbon nanotubes, glass fibers, dicumyl peroxide, azodicarbonamide, wood grain master batches, zinc oxide, calcium carbonate, a colorant, a stabilizer, a foaming agent, and a lubricating agent. The invention further provides a manufacturing method of the anticorrosion high-temperature-resistance artificial ebony. The artificial ebony has large hardness, high specific gravity, excellent water resistance, acid resistance, freezing tolerance, and high temperature resistance; the artificial ebony provided by the present invention has attractive appearance and excellent toughness and strength, and the color thereof is similar to that of the natural ebony; furthermore, the manufacturing method of the anticorrosion high-temperature-resistance artificial ebony has simple process and lower synthesis costs, and is beneficial to large-scale popularization and application.

Description

technical field [0001] The invention relates to the field of artificial wood processing, in particular to an anti-corrosion and high-temperature resistant artificial ebony and a manufacturing method thereof. Background technique [0002] Ebony, also known as gloomy wood, has both the elegance of wood and the charm of stone, and is known as "Oriental godwood" and "plant mummy". In the past dynasties, ebony was used as a thing to ward off evil spirits, handicrafts, Buddha statues, and amulet pendants. The ancients said: "Having half a square of ebony at home is better than a box of treasures." [0003] Ebony is nanmu, red toon, camphor and hemp willow, which are all buried in low-lying places such as ancient river beds due to natural disasters such as earthquakes, floods, and mudslides. Under the action of microorganisms such as bacteria, ebony is formed after thousands of years of carbonization process, so it is also called "carbonized wood". [0004] The essence of ebony ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/10C08L97/02C08K13/04C08K7/24C08K7/14C08K3/22C08K3/26B29C44/04B29C44/34B29C44/42
CPCC08L61/06B29C44/04B29C44/3442B29C44/42C08K2201/011C08L2201/08C08L2203/14C08L2205/025C08L2205/03C08L2205/16C08L97/02C08K13/04C08K7/24C08K7/14C08K2003/2296C08K2003/265
Inventor 刘露
Owner TAICANG HONGSHAN ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com