A special water paint for high anti-corrosion and high weather resistance metal components and its preparation method

A metal component and water-based paint technology, which is applied in the field of special water-based paint for high-corrosion and high-weather-resistant metal components and its production, can solve the problems of difficult to achieve weather resistance and anti-corrosion performance, and achieve bright luster, excellent decoration, and high coating efficiency Effect

Active Publication Date: 2019-02-15
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] It is difficult to meet the requirements of weather resistance (artificial aging for 500 hours) and anti-corrosion performance (salt spray resistance for 240 hours) for existing domestic high-corrosion and high-weather-resistant metal components special water paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The special water paint for high anti-corrosion and high weather resistance metal components is prepared from the following materials: 30 parts of water-based epoxy modified thermoplastic acrylic resin, 10 parts of water-based multifunctional modified resin, 4 parts of co-solvent, 2 parts 1 part of environment-friendly neutralizer, 8 parts of deionized water, 0.5 part of wetting and dispersing agent, 0.1 part of defoamer, 0.2 part of substrate wetting agent, 15 parts of high whiteness rutile titanium dioxide, 5 parts of functional filler, 5 parts of superfine talcum powder, and 1 part of superfine calcium carbonate.

[0033] Wherein said co-solvent is formed by mixing propylene glycol, diethylene glycol and polyethylene glycol in a ratio of 1:1:1.

[0034] The functional filler is formed by mixing ultrafine hollow glass microspheres F200 and nano silicon dioxide in a ratio of 1:3.

[0035] After testing, the water-based paint of this embodiment has a salt spray resista...

Embodiment 2

[0037] The special water-based paint for high anti-corrosion and high weather-resistance metal components is prepared from the following materials: 39 parts of water-based epoxy modified thermoplastic acrylic resin, 13 parts of water-based multifunctional modified resin, 5 parts of cosolvent, 3 parts 10 parts of environmentally friendly neutralizer, 10 parts of deionized water, 1 part of wetting and dispersing agent, 0.3 parts of defoaming agent, 0.4 parts of substrate wetting agent, 20 parts of high whiteness rutile titanium dioxide, 8 parts of functional fillers, 8 parts of superfine talcum powder, and 3 parts of superfine calcium carbonate.

[0038] Wherein said co-solvent is formed by mixing propylene glycol, diethylene glycol and polyethylene glycol in a ratio of 1:1:2.

[0039] The functional filler is formed by mixing ultrafine hollow glass microspheres F200 and nano silicon dioxide in a ratio of 1:4.

[0040] After testing, the water-based paint of this embodiment has...

Embodiment 3

[0042] The special water-based paint for high anti-corrosion and high weather-resistance metal components is prepared from the following materials: 45 parts of water-based epoxy modified thermoplastic acrylic resin, 15 parts of water-based multifunctional modified resin, 6 parts of cosolvent, 4 parts 13 parts of environmentally friendly neutralizer, 13 parts of deionized water, 1.5 parts of wetting and dispersing agent, 0.5 parts of defoaming agent, 0.5 parts of substrate wetting agent, 25 parts of high whiteness rutile titanium dioxide, 10 parts of functional fillers, 10 parts of superfine talcum powder, and 5 parts of superfine calcium carbonate.

[0043] The co-solvent described therein is formed by mixing propylene glycol, diethylene glycol and polyethylene glycol in a ratio of 1:1:3.

[0044]The functional filler is formed by mixing ultrafine hollow glass microspheres F200 and nano silicon dioxide in a ratio of 1:5.

[0045] After testing, the water-based paint of this e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a special water paint for high anticorrosion and high weather resistance metal components and a preparation method thereof. The water paint comprises the following components in parts by weight: 30-45 parts of water-based epoxy modified thermoplastic acrylic resin, water-based multifunctional 10-15 parts of modified resin, 4-6 parts of co-solvent, 2-4 parts of neutralizer, 8-13 parts of deionized water, 0.5-1.5 parts of wetting and dispersing agent, 0.1-0.5 parts of defoaming agent, base material 0.2-0.5 parts of wetting agent, 15-25 parts of titanium dioxide, 5-10 parts of functional filler, 5-10 parts of superfine talcum powder and 1-5 parts of superfine calcium carbonate. The paint liquid of the present invention has good stability, can be sprayed and coated, has high coating efficiency, stable quality, uniform dip-coated paint film, smooth surface, good hardness, strong adhesion, good anti-corrosion performance, and paint-hanging property on edges and corners Good, no leaking phenomenon, salt spray resistance up to 240 hours, artificial aging resistance up to 500 hours, water-based environmental protection, low price, wide application range.

Description

technical field [0001] The invention relates to the field of industrial anticorrosion paints, in particular to a special water paint with high anticorrosion and high weather resistance for metal components and a manufacturing method thereof. Background technique [0002] With the increasing shortage of natural resources, people's demand for resources is increasing day by day. In today's society, the application of steel structures is becoming more and more extensive, and the requirements for high anti-corrosion and high weather resistance on the surface of steel structures are becoming more and more important. Due to the low surface energy of steel structures, there are certain difficulties in the adhesion of coatings on the surface, so most of the coatings used on the surface of steel structures are solvent-based coatings. A large proportion of solvent-based coatings are volatile solvents, which volatilize into the atmosphere after coating, causing a great degree of air po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/10C09D201/00C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2201/011C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D7/70C09D163/10C08L101/14C08K13/04C08K7/28C08K3/36C08K2003/2241C08K3/34C08K2003/265
Inventor 刘善江程璐李幕英花东栓董立志刘占川薛小倩郭京林
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com