Ultrasonic non-destructive abrasion-resistant coating thickness and elastic modulus measuring method

A wear-resistant coating, elastic modulus technology, used in measuring devices, using ultrasonic/sonic/infrasonic waves, using sonic/ultrasonic/infrasonic waves to analyze solids, etc.

Active Publication Date: 2016-10-12
DALIAN UNIV OF TECH
View PDF8 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method overcomes the complex operation of multi-probe combination or multiple angles of incidence in the conventional ultrasonic method, and also overcomes the insufficiency of the surface wave method that assumes Poisson's ratio as a fixed value, and solves the problem of ultrasonic quantitative measurement of the elastic modulus of the coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic non-destructive abrasion-resistant coating thickness and elastic modulus measuring method
  • Ultrasonic non-destructive abrasion-resistant coating thickness and elastic modulus measuring method
  • Ultrasonic non-destructive abrasion-resistant coating thickness and elastic modulus measuring method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] This ultrasonic non-destructive measurement method of wear-resistant coating thickness and elastic modulus adopts such as figure 1 The one shown includes the sink 1, the sample stage 2, the wear-resistant coating sample 3, the water immersion focusing probe 4, the XYZ three-dimensional stepping control device 5, the ultrasonic flaw detector 6, the digital oscilloscope 7 and the ultrasonic pulse echo of the computer 8. Method for measuring the thickness and elastic modulus of wear-resistant coatings. The specific implementation steps are as follows:

[0038] Step a. Determine the angle of incidence α: Put a stainless steel sample with a thickness of h = 1.62 mm on the sample table 2 in the sink 1, and use the XYZ three-dimensional stepping control device 5 to adjust the distance between the immersion focus probe 4 and the sample. Relative position, the focus of the water immersion focusing probe is vertically focused on the surface of the stainless steel sample. The USIP4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an ultrasonic non-destructive abrasion-resistant coating thickness and elastic modulus measuring method, which belongs to the technical field of ultrasonic non-destructive detection. The method is based on a pulse echo technology and uses a single immersion focusing probe to acquire an echo signal of an abrasion-resistant coating / metal matrix specimen once to effectively extract longitudinal wave and transverse wave signals of back and forth interfaces of the coating. Spectral analysis is carried out on longitudinal wave and transverse wave signals to acquire corresponding ultrasonic reflection coefficient amplitude spectrum (URCAS). A cross-correlation analysis two-parameter inversion technology is combined to measure the longitudinal wave sound velocity V2l and the thickness d of the coating at the same time. Through the inversion of the thickness d and the resonant frequency fnt of shear wave URCAS, the transverse wave sound velocity V2t of the coating is calculated. Density rho2 is corrected through the combination with the coating porosity counted by a metallographic method. According to an elastic modulus expression, the elastic modulus is measured. According to the method, complicated operation of conventional ultrasonic multi-probe combination or multi-angle incidence is overcome; the shortcoming that the poisson ratio is assumed to be fixed by a surface wave method is overcome; and the problem of ultrasonic quantitative measurement of the elastic modulus of the coating is solved.

Description

Technical field [0001] The invention relates to a method for ultrasonic nondestructive measurement of the thickness and elastic modulus of a wear-resistant coating, which belongs to the technical field of ultrasonic nondestructive testing. Background technique [0002] A1 2 O 3 Coating layers such as WC and WC have high hardness, strength, elasticity and thermal conductivity, and have extremely high wear resistance and erosion resistance. Therefore, they have become one of the focus of research on wear-resistant coating technology in recent years. Houdková et al. pointed out that for small-sized workpieces, especially in the inner cavity of the workpiece, the inability to achieve vertical spraying will result in unsatisfactory comprehensive properties such as coating microstructure, thickness, and elasticity. W. Tillmann and P. Chivavibul also pointed out that changes in the spraying process (particle size, spraying angle, etc.) will affect the thickness, hardness, elasticity and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01B17/02G01N29/07G01N29/28
CPCG01B17/025G01N29/07G01N29/28G01N2291/011G01N2291/023G01N2291/02827G01N2291/02854G01N2291/0421G01N2291/0422
Inventor 林莉马志远张伟雷明凯
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com