High-performance oxygen reduction MnO2-Mn3O4/carbon nanotube composite catalyst and preparation method and application thereof

A carbon nanotube composite and carbon nanotube technology, which is applied in the field of electrocatalysis, can solve the problems of low activity and conductivity, and achieve the effects of simple preparation method, obvious synergistic effect and good stability

Active Publication Date: 2016-09-28
CENT SOUTH UNIV
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the defect that single manganese dioxide has low activity and electrical conductivity as an ORR catalyst in the prior art, one of the purposes of the present invention is to provide a kind of catalyst that is used as an ORR catalyst and whose comprehensive catalytic performance is close to that of a 20wt% Pt / C commercial catalyst. Oxygen reduced MnO 2 -Mn 3 o 4 / Carbon nanotube composite catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance oxygen reduction MnO2-Mn3O4/carbon nanotube composite catalyst and preparation method and application thereof
  • High-performance oxygen reduction MnO2-Mn3O4/carbon nanotube composite catalyst and preparation method and application thereof
  • High-performance oxygen reduction MnO2-Mn3O4/carbon nanotube composite catalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] MnO 2 -Mn 3 O 4 / The preparation of carbon nanotubes is divided into two steps, as follows:

[0028] (1) Preparation of oxidized carbon nanotubes

[0029] Oxidized carbon nanotubes were synthesized using a modified Hummers method. Weigh 1 g of multi-walled carbon nanotubes into a 250 mL round-bottomed flask, slowly add 23 mL of concentrated sulfuric acid, and stir for 24 h. Transfer the round bottom flask to a 35 °C water bath and add 0.2 g NaNO 3 and keep stirring. To be NaNO 3 After dissolving, add 1g KMnO very slowly 4 , to be KMnO 4 After the addition, the stirring was continued for 120 min. Slowly add 46 mL of deionized water, transfer to a 98°C water bath and heat for 30 min, remove and cool to room temperature and stir continuously, add 140 mL of deionized water and 10 mL of 30% hydrogen peroxide in sequence and stir for 5 min. The oxidized carbon nanotubes in the suspension were collected by centrifugation. During the centrifugation process, they were...

Embodiment 2

[0036] According to the method of Example 1, in MnO 2 -Mn 3 O 4 25 mg of oxidized carbon nanotubes were added to the preparation of carbon nanotubes.

[0037] The evaluation method of catalytic performance is the same as that of Example 1.

[0038] The obtained MnO 2 -Mn 3 O 4 The onset potential of the composite / carbon nanotube composite as ORR catalyst is -0.09V (vs.Hg / HgO), the half-wave potential is -0.22V (vs.Hg / HgO), and the limiting current density is -5.6mA / cm 2 . In the galvanometric evaluation, the current density retention rate was about 90% after continuous operation for 7200 s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Limiting current densityaaaaaaaaaa
Limiting current densityaaaaaaaaaa
Limiting current densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance oxygen reduction MnO2-Mn3O4 / carbon nanotube composite catalyst and a preparation and an application thereof. The composite catalyst is prepared by embedding MnO2 nanorods and Mn3O4 nanoparticles into meshes of a carbon nanotube network and / or depositing the MnO2 nanorods and the Mn3O4 nanoparticles on the surface of a carbon nanotube. The preparation method comprises the steps of: dissolving or dispersing potassium permanganate, ammonium chloride and oxidized carbon nanotube into water for hydrothermal reaction; and carrying out cooling, suction filtration, washing and drying on the hydrothermal reaction product to obtain the high-performance oxygen reduction MnO2-Mn3O4 / carbon nanotube composite catalyst. The preparation method is simple and beneficial to industrial production; and the prepared MnO2-Mn3O4 / carbon nanotube composite catalyst is applied to a fuel cell, has the characteristics of high activity and good stability, has approximate overall performance in comparison with a 20wt%Pt / C commercial catalyst and has a good application prospect.

Description

technical field [0001] The invention relates to an oxygen reduction (ORR) catalyst and its preparation and application method, in particular to a high-performance oxygen reduction MnO for fuel cells 2 -Mn 3 o 4 The invention discloses a carbon nanotube composite catalyst and a preparation method thereof, belonging to the technical field of electrocatalysis. Background technique [0002] Due to the excessive use of traditional fossil energy, human beings are facing more and more serious energy shortages and environmental pollution crises, and it is imminent to develop green and safe new energy sources. As an environment-friendly and efficient energy conversion device, fuel cells have attracted more and more researchers' attention. Pt and its alloys are currently commercialized ORR catalysts for fuel cells. Although they have high activity, the high price and unsatisfactory stability limit the wide commercial application of fuel cells. Therefore, the key to the wide applic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/90
CPCH01M4/9016H01M4/9083Y02E60/50
Inventor 钱东刘昆王喜鹏闵紫嫣李军
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com