Preparation method of n-substituted carboxyl polyaniline/cadmium sulfide quantum dot composite material

A composite material and polyaniline technology, applied in chemical instruments and methods, luminescent materials, etc., can solve the problems of poor separation effect of electrons and holes, large interface distance, and low purity of products, and achieve easy agglomeration and extremely easy photocorrosion The effect of defect improvement, interfacial force strengthening, and high cycle stability

Inactive Publication Date: 2018-02-06
EAST CHINA JIAOTONG UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composite materials prepared by these methods have a large interfacial distance due to the weak force between different components, and the separation effect of electrons and holes is poor, and the purity of the product is not high, and the photocorrosion resistance is poor.
In order to promote the rapid movement of electrons between the two materials, and at the same time improve the defect that cadmium sulfide is prone to photocorrosion under visible light, a common improvement method is to form a core-shell structure of cadmium sulfide and polyaniline, and wrap cadmium sulfide quantum dots It is used as a protective layer in organic conductive polyaniline, but this method will reduce the light conversion efficiency and cycle stability of cadmium sulfide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of n-substituted carboxyl polyaniline/cadmium sulfide quantum dot composite material
  • Preparation method of n-substituted carboxyl polyaniline/cadmium sulfide quantum dot composite material
  • Preparation method of n-substituted carboxyl polyaniline/cadmium sulfide quantum dot composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This example will illustrate the method of the present invention to generate a cadmium-containing precursor by in-situ polymerization with a molar ratio of N-phenylglycine and cadmium acetate of 1:2, and then in an ice-water bath, use the cadmium precursor and sodium sulfide nonahydrate The molar ratio is 1:1, the reaction time is 2h, and it is realized according to the reaction path of two-step synthesis.

[0045] Weigh 0.756g of N-phenylglycine and 2.66g of cadmium acetate and dissolve in 40ml of HCl solution with a concentration of 1M, and ultrasonicate for 30min until the mixed solution is dispersed to form a homogeneous solution, labeled as A; weigh 1.427g of ammonium persulfate and dissolve in In 60ml of HCl solution with a concentration of 1M, ultrasonically disperse for 5 minutes to form a uniform solution, labeled as B; in an ice-water bath, keep liquid A continuously stirring, slowly drop liquid B into liquid A, react for 6 hours, and then Leave it for 18 hour...

Embodiment 2

[0049] This example will illustrate that the molar ratio of N-phenylglycine and cadmium acetate is 1:2 in the method of the present invention to generate a cadmium-containing precursor through in-situ polymerization, and then in an ice-water bath, the cadmium precursor and nonahydrate sulfide The sodium molar ratio is 1:0.5, the reaction time is 2h, and the reaction path of the two-step synthesis is realized.

[0050]Weigh 0.756g of N-phenylglycine and 2.66g of cadmium acetate and dissolve in 40ml of HCl solution with a concentration of 1M, and ultrasonicate for 30min until the mixed solution is dispersed to form a homogeneous solution, labeled as A; weigh 1.427g of ammonium persulfate and dissolve in In 60ml of HCl solution with a concentration of 1M, ultrasonically disperse for 5 minutes to form a uniform solution, labeled as B; in an ice-water bath, keep liquid A continuously stirring, slowly drop liquid B into liquid A, react for 6 hours, and then Leave it for 18 hours, af...

Embodiment 3

[0053] This example will illustrate that the molar ratio of N-phenylglycine and cadmium acetate is 1:2, and the cadmium-containing precursor is generated by in-situ polymerization, and then in an ice-water bath, the molar ratio of cadmium acetate and sodium sulfide nonahydrate is The ratio is 1:1, the reaction time is 0.5h, and it is realized according to the reaction path of two-step synthesis.

[0054] Weigh 0.756g of N-phenylglycine and 2.66g of cadmium acetate and dissolve in 40ml of HCl solution with a concentration of 1M, and ultrasonicate for 30min until the mixed solution is dispersed to form a homogeneous solution, labeled as A; weigh 1.427g of ammonium persulfate and dissolve in In 60ml of HCl solution with a concentration of 1M, ultrasonically disperse for 5 minutes to form a uniform solution, labeled as B; in an ice-water bath, keep liquid A continuously stirring, slowly drop liquid B into liquid A, react for 6 hours, and then Leave it for 18 hours, after the react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of N-substituted carboxyl polyaniline grafted cadmium sulfide quantum dot composite material, the method uses N-phenylglycine as a monomer, and generates a cadmium-containing precursor by introducing a cadmium source in its in-situ polymerization system , and then by introducing a sulfur source, using the nucleation mechanism between cadmium and sulfur to prepare chemically grafted N-substituted carboxypolyaniline cadmium sulfide quantum dot composites. Compared with cadmium sulfide and polyaniline, the electronic transport rate of the composite material prepared by the method of the present invention is greatly improved, the light corrosion resistance of cadmium sulfide is improved, photoelectric conversion and photocatalytic degradation of organic dyes can be performed under visible light, The solubility and stability of the material are improved. The obtained composite material can be applied in photocatalyst, sensor, solar cell and other fields.

Description

technical field [0001] The invention relates to a preparation method of an N-substituted carboxyl polyaniline / cadmium sulfide quantum dot composite material, which belongs to the technical field of conductive polymer materials. Background technique [0002] Energy shortage and environmental pollution are the most urgent problems facing today. All countries in the world are looking for an emerging industry that can effectively deal with the energy crisis, relieve environmental pressure, develop a low-carbon economy, and achieve sustainable development. Due to its cleanliness, safety, convenience, and high efficiency, solar photovoltaics are flourishing all over the world, and are known as a sunrise industry that welcomes the arrival of the new energy era. At the same time, with the gradual maturity of organic solar cells and photocatalytic degradation technologies, the preparation of photoactive materials by polymer composite semiconductor quantum dots has become more and mor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G73/02C09K11/56
CPCC08G73/0266C09K11/565
Inventor 章家立杨标宋琦郭赞如程光尤鸿蒲周帅丰
Owner EAST CHINA JIAOTONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com