Quantitative analysis method of polyether ether ketone in polyetheretherketone composite material
A technique for quantitative analysis of polyetheretherketone, applied in the field of quantitative analysis of polyetheretherketone in polyetheretherketone composite materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment approach 1
[0053] Embodiment 1, a quantitative analysis method of polyether ether ketone in a polyether ether ketone composite material, the quantitative analysis method includes the following steps:
[0054] 1) Raw material pulverization: pulverize the polyetheretherketone composite material, and the average particle diameter of the obtained fine powder is 50-200 μm;
[0055] 2) Purification treatment: Mix the fine powder in step 1) with an organic solvent and a surfactant, heat up to the glass transition temperature of polyetheretherketone and the boiling point of the organic solvent under normal pressure and stirring, and perform purification treatment. After completion, cooling down, suction filtration, washing, and drying to obtain purified fine powder;
[0056] 3) Sulfonation: Sulfonate the purified fine powder in step 2) with concentrated sulfuric acid, filter the reacted solution, pour the filtrate into ice-water mixture, stir, let it stand, and wash until the pH of the solution ...
Embodiment approach 2
[0058] Embodiment 2 is the same as Embodiment 1, except that the organic solvent in step 2) is liquid and measured in milliliters; the surfactant is liquid or solid and measured in grams; the fine powder is measured in grams Metering; the mass ratio of the volume of the organic solvent to the fine powder is 25-40:1; the mass ratio of the surfactant to the fine powder is 1-5:1.
Embodiment approach 3
[0059] Embodiment 3 is the same as Embodiment 1, except that the organic solvent in step 2) is hexamethylphosphoric triamide and / or N-methyl-2-pyrrolidone.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
glass transition temperature | aaaaa | aaaaa |
boiling point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com