Spinning sizing agent composition and preparing method and application thereof

A textile size and composition technology, applied in the field of textile size composition and its preparation, can solve the problems of inconvenient industrial production, small laboratory test, and difficult operation, and achieve improved sizing performance, good water solubility, Good permeability effect

Active Publication Date: 2016-09-07
青岛纺友纺织科技股份有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Emulsion polymerization demulsification method: first use emulsion polymerization to obtain a polyacrylate emulsion with a glass transition temperature > 37 ° C, and then use Na 2 SO 4 or concentrated H 2 SO 4 Demulsification; this method is difficult to operate in a small laboratory test, and it is not convenient for industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spinning sizing agent composition and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) Preparation of solid acrylate:

[0045] Add 100kg of hydrogenated polybutadiene di(meth)acrylate, 150kg of 1-adamantane (meth)acrylate and 250kg of acrylonitrile into the head tank, stir evenly and set aside;

[0046] Add 200kg of xylene, 100kg of cyclohexane, and 100kg of absolute ethanol to a 1000L high-level tank with stirring, mix well, weigh 5.6kg of benzoyl peroxide and 2.8kg of azobisisobutyronitrile and put them into the high-level tank respectively, and stir Uniform spare;

[0047] Add 1400kg of toluene, 700kg of cyclohexane, and 700kg of absolute ethanol in sequence to a 5000L glass-lined reactor equipped with a reflux condenser and mix them uniformly as a reaction solvent, then add 0.4kg of n-dodecanethiol and stir evenly, and heat up to 95°C , Add the monomers and initiators in the above two elevated tanks dropwise into the 5000L reaction kettle at the same time, and the dropwise addition is completed within 3 hours. After stirring for 0.5h, nitrogen g...

Embodiment 2

[0053] (1) Preparation of solid acrylate:

[0054] Add 200kg of hydrogenated polybutadiene di(meth)acrylate, 100kg of 1-adamantane(meth)acrylate and 200kg of acrylonitrile into the head tank, stir evenly and set aside;

[0055] Add 200kg of xylene, 100kg of cyclohexane, and 100kg of absolute ethanol to a 1000L high-level tank with stirring, mix well, weigh 5.6kg of benzoyl peroxide and 2.8kg of azobisisobutyronitrile and put them into the high-level tank respectively, and stir Uniform spare;

[0056] Add 1400kg of toluene, 700kg of cyclohexane, and 700kg of absolute ethanol in sequence to a 5000L glass-lined reactor equipped with a reflux condenser and mix them uniformly as a reaction solvent, then add 0.4kg of n-dodecanethiol and stir evenly, and heat up to 95°C , Add the monomers and initiators in the above two elevated tanks dropwise into the 5000L reaction kettle at the same time, and the dropwise addition is completed within 3 hours. After stirring for 0.5h, nitrogen ga...

Embodiment 3

[0062] (1) Preparation of solid acrylate:

[0063] Add 120kg hydrogenated polyisoprene di(meth)acrylate, 170kg norbornyl (meth)acrylate and 210kg acrylonitrile into the head tank, stir evenly for subsequent use;

[0064] Add 200kg of xylene, 100kg of cyclohexane, and 100kg of absolute ethanol to a 1000L high-level tank with stirring, mix well, weigh 5.6kg of benzoyl peroxide and 2.8kg of azobisisobutyronitrile and put them into the high-level tank respectively, and stir Uniform spare;

[0065]Add 1400kg of toluene, 700kg of cyclohexane, and 700kg of absolute ethanol in sequence to a 5000L glass-lined reactor equipped with a reflux condenser and mix them uniformly as a reaction solvent, then add 0.4kg of n-dodecanethiol and stir evenly, and heat up to 95°C , Add the monomers and initiators in the above two elevated tanks dropwise into the 5000L reaction kettle at the same time, and the dropwise addition is completed within 3 hours. After stirring for 0.5h, nitrogen gas was in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to a spinning sizing agent composition and a preparing method and application thereof. The composition is prepared by mixing an acrylate composition and a nanometer SiO2 composite modified starch, wherein the acrylate composition is prepared from a (methyl) acrylate compound selected from one or more of (methyl) acrylate-modified silicone oil, alkyl (methyl) acrylate with alkyl with the number of carbon atoms being 12 or above and poly alkylene glycol (methyl) acrylate with the number-average molecular weight being 400 or above, a (methyl) acrylate compound in ester linkage with alicyclic alkyl with the number of carbon atoms being 6 or above, acrylonitrile, a composite initiator and a chain transfer agent, and the nanometer SiO2 composite modified starch is obtained by carrying out acidification, cross-linking and oxidation on starch, introducing surface-modified nano-scale SiO2 and then carrying out ultrasonic dispersing. The sizing agent can remarkably improve the sizing performance of warp yarns and the spinning efficiency and can be widely applied to sizing of warp yarns made of pure cotton, polyamide, fibers and blended yarns.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a textile slurry composition and a preparation method and application thereof. Background technique [0002] There are four main types of size widely used for textile sizing: modified starch, polyvinyl alcohol, polyester and polyacrylate size. Modified starch sizing has good film-forming properties, strong affinity with natural fibers, and is easy to desizing. It is the main sizing component of textile sizing; not enough. Polyvinyl alcohol size film has high strength, good flexibility, and good slurry fluidity; however, polyvinyl alcohol is difficult to desizing, and because polyvinyl alcohol is difficult to degrade, it is easy to cause white environmental pollution, and the European Union has banned its use by legislation. The chemical structure of polyester size is similar to that of polyester, so it has strong affinity with polyester fiber, especially suitable for polyester...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/11D06M11/79D06M15/263D06M15/31D06M101/06D06M101/32
CPCD06M11/79D06M15/11D06M15/263D06M15/31D06M2101/06D06M2101/32D06M2200/35D06M2200/50
Inventor 缪建良
Owner 青岛纺友纺织科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com