Flexible transparent thin-film electrode and manufacturing method thereof
A technology of transparent film and manufacturing method, which is applied in hybrid capacitor electrodes, hybrid/electric double layer capacitor manufacturing, etc., to achieve excellent photoelectric performance, superior photoelectric performance, and improved photoelectric performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0012] PEDOT:PSS was doped with a volume ratio of 6% ethylene glycol and 2% surface active (Triton), which was spin-coated onto a plasma-treated PDMS substrate. Place it on a heating platform and anneal at 120°C for 15min. The number of spin coats is 1 to 5 layers.
Embodiment 2
[0014] PEDOT:PSS was doped with a volume ratio of 6% ethylene glycol and 2% surface active (triton), and the dot spacing was controlled to be 40 μm, and it was inkjet printed onto a plasma-treated PDMS substrate. Place it on a heating platform and anneal at 120°C for 15min. The number of printing layers is 1 to 3 layers.
Embodiment 3
[0016] PEDOT:PSS was doped with 6% ethylene glycol and 1% surface active (Triton) at a volume ratio of 40 μm, and inkjet printed it onto a plasma-treated PDMS substrate. Place it on a heating platform and anneal at 120°C for 15min. The number of printing layers is 1 to 3 layers.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com