Semidull POY polyester fiber and processing method thereof

A technology of polyester fiber and processing method, applied in the field of semi-dull POY polyester fiber and its processing, to achieve good matting effect, excellent matting effect, and good dispersion

Active Publication Date: 2016-08-31
福建百宏聚纤科技实业有限公司
View PDF12 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Chinese Patent Application No. 201020194579.7 relates to a synthetic fiber, specifically a polyester semi-dull round-hole monofilament, which solves the problems in the prior art in terms of texture, feel, softness, and vividness of clothing fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of processing method of semi-dull POY polyester fiber, its concrete steps are:

[0039] The preparation of the first step modified titanium dioxide:

[0040] Using nano-titanium dioxide powder as raw material, under normal temperature, high-speed stirring and ultrasonic dispersion are carried out in cyclohexane solution, the dispersion time is 2-3 hours, the high-speed stirring speed is 2000-3000 rpm, and then in nitrogen atmosphere, Add toluene diisocyanate, react at a reaction temperature of 85-95°C for 45-60 minutes, after the reaction is completed, then distill under reduced pressure for 45 minutes at 110°C, and then dry the product under reduced pressure at 120°C for 48 hours , to prepare modified titanium dioxide.

[0041] The average particle size of the nano-titanium dioxide powder is 45-65 nanometers, the mass concentration of the nano-titanium dioxide powder in cyclohexane is 35g / L, and the molar ratio of toluene diisocyanate toluene diisocyanate to ti...

Embodiment 2

[0058] A kind of processing method of semi-dull POY polyester fiber, its concrete steps are:

[0059] The preparation of the first step modified titanium dioxide:

[0060] Using nano-titanium dioxide powder as raw material, under normal temperature, high-speed stirring and ultrasonic dispersion are carried out in cyclohexane solution. The dispersion time is 2-3 hours, and the high-speed stirring speed is 2000-3000 rpm, and then in nitrogen atmosphere, Add toluene diisocyanate, react at a reaction temperature of 85-95°C for 45-60 minutes, after the reaction is completed, then distill under reduced pressure at 110°C for 45 minutes, and then dry the product under reduced pressure at 120°C for 48 hours , to prepare modified titanium dioxide.

[0061] The average particle size of the nano-titanium dioxide powder is 45-65 nanometers, the mass concentration of the nano-titanium dioxide powder in cyclohexane is 40 g / L, and the molar ratio of toluene diisocyanate toluene diisocyanate ...

Embodiment 3

[0078] A kind of processing method of semi-dull POY polyester fiber, its concrete steps are:

[0079] The preparation of the first step modified titanium dioxide:

[0080] Using nano-titanium dioxide powder as raw material, under normal temperature, high-speed stirring and ultrasonic dispersion are carried out in cyclohexane solution, the dispersion time is 2-3 hours, the high-speed stirring speed is 2000-3000 rpm, and then in nitrogen atmosphere, Add toluene diisocyanate, react at a reaction temperature of 85-95°C for 45-60 minutes, after the reaction is completed, then distill under reduced pressure for 45 minutes at 110°C, and then dry the product under reduced pressure at 120°C for 48 hours , to prepare modified titanium dioxide.

[0081] The average particle size of the nano-titanium dioxide powder is 45-65 nanometers, the mass concentration of the nano-titanium dioxide powder in cyclohexane is 50 g / L, and the molar ratio of toluene diisocyanate toluene diisocyanate to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to semidull POY polyester fiber and a processing method thereof. The method specifically includes the steps that melt is online added into a front-of-pump injecting system through direct spinning, prepared semidull polyester slices serve as the front-of-pump injecting raw material, conventional polyester melt serves as main melt, and the semidull polyester melt and the main melt are mixed through the front-of-pump injecting system, are then subjected to before-spinning filtering, enter a spinning assembly to be subjected to melting and spinning, and are subjected to annular air blowing cooling, oiling, stretching and rolling to obtain the semidull POY polyester fiber. The semidull POY polyester fiber has excellent delustering effect, and the polyester POY fiber prepared with low addition content of titanium dioxide is high in tensile strength, high in inorganic powder dispersity and good in delusteirng effect, and has the advantages of preventing see-through, being high in luster and the like when used for preparing clothes fabric and home textile fabric.

Description

technical field [0001] The invention relates to the technical field of textile production, in particular to a semi-dull POY polyester fiber and a processing method thereof. Background technique [0002] Due to its excellent mechanical properties and heat resistance, polyester fiber has a very wide range of applications in clothing, home textiles, industrial use and other fields; as a high-end clothing fabric, polyester filaments are required due to their excellent light transmission The matting treatment of its light transmission has achieved the effect of shading and luminescence, making the fabric opaque or reducing its light transmission; titanium dioxide is a commonly used matting agent for polyester filaments, and it is usually beaten by copolymerization at present. The process of adding titanium dioxide as a matting agent for copolymerization to prepare a matting titanium dioxide product; POY polyester filament itself has a highly oriented structure, due to its re-draw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10D01D1/06D01D1/09D01D5/092D01D5/12C08G63/183C08G63/86
CPCC08G63/183C08G63/866D01D1/065D01D1/09D01D5/092D01D5/12D01F1/10D01F6/92
Inventor 谌建国刘智敏鲁传旺陈文阳李艺龙
Owner 福建百宏聚纤科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com