Preparation method of sulfide solid electrolyte material

A solid electrolyte and sulfide technology, which is applied in cable/conductor manufacturing, circuits, electrical components, etc., can solve the problems affecting the electrical performance of all-solid-state batteries and the thickness of the electrolyte sheet, and achieve a small shape, low impedance, and complete shape. Effect

Inactive Publication Date: 2016-08-17
新余赣锋新能源产业投资合伙企业(有限合伙)
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above problems, the object of the present invention is to provide a method for preparing a sulfide solid electrolyte material, so as to solve the problem that the thickness of the electrolyte sheet is relatively thick in the preparation method of the existing all-solid electrolyte sheet, which will affect the performance of the all-solid electrolyte sheet. The problem of the electrical performance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of sulfide solid electrolyte material
  • Preparation method of sulfide solid electrolyte material
  • Preparation method of sulfide solid electrolyte material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only part of the embodiments of the present invention, not all of them. Based on the implementation manners in the present invention, all other implementation manners obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0028] See figure 1 , the embodiment of the present invention provides a preparation method of a sulfide solid electrolyte material, comprising the following steps:

[0029] Step S1: Mix the sulfide lithium ion conductor electrolyte powder, binder and solvent to obtain electrolyte slurry. Wherein, calculated according to the mass ratio ratio, the sulfide lithium ion conductor electrolyte powder in the electrolyte slurry accounts f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a sulfide solid electrolyte material. The preparation method comprises the following steps: sulfide lithium ion conductor electrolyte powder, an adhesive and a solvent are mixed, and electrolyte slurry is obtained; the electrolyte slurry is uniformly stirred and dispersed, and uniform electrolyte slurry is obtained; the uniform electrolyte slurry is uniformly coated on a PET film, the electrolyte slurry which is coated on the PET film is dried at a set drying temperature, in order to evaporate the solvent part, and an electrolyte film is obtained; the electrolyte film is taken from the PET film, and the electrolyte film is cut according to a certain specification; the adhesive and the residual solvent in the cut electrolyte film are discharged, and a compact sulfide lithium ion conductor electrolyte sheet is obtained. The preparation method of the sulfide solid electrolyte material can effectively solve the problem that when an electrolyte sheet is prepared according to the prior preparation method of the all solid state electrolyte sheet, the electrolyte sheet which is thicker influences electrical performance of an all solid state battery.

Description

technical field [0001] The invention relates to the technical field of sulfide solid electrolyte materials, in particular to a preparation method of a sulfide solid electrolyte material. Background technique [0002] Because lithium secondary batteries have many advantages such as large output power, high energy density, long service life, high average output voltage, small self-discharge, no memory effect, fast charge and discharge, excellent cycle performance and no environmental pollution, it has become It is the first choice of rechargeable power source for portable electronic products today, and it is also considered to be the most competitive vehicle power battery. Therefore, at present, lithium secondary batteries have entered thousands of households and become an inseparable part of society. In general, lithium secondary batteries mainly include liquid lithium secondary batteries and solid lithium secondary batteries. Among solid-state lithium secondary batteries, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0562H01B13/00H01B1/06
CPCY02E60/10
Inventor 许晓雄朱骏高超黄冰心刘登
Owner 新余赣锋新能源产业投资合伙企业(有限合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products