Early-strength polycarboxylate superplasticizer and preparation method and application thereof

A polycarboxylic acid and early-strength technology, which is used in the field of early-strength polycarboxylate water reducer and its preparation, can solve the problems of long concrete setting time, insignificant early-strength effect, and poor dispersibility, and achieve early-strength effect. Good, ensure the strength, the effect of high compressive strength

Inactive Publication Date: 2016-07-13
SHANDONG JINGJIN NEW ENERGY CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional naphthalene-based early-strength water-reducer can no longer meet the requirements of concrete due to factors such as poor dispersion, low water-reducing rate, insignificant early-strength effect, and long concrete setting time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Early-strength polycarboxylate superplasticizer and preparation method and application thereof
  • Early-strength polycarboxylate superplasticizer and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] In the embodiment of the present invention, an early-strength polycarboxylate water reducer is composed of the following raw materials in parts by weight: 55 parts of polyacrylic acid, 33 parts of ethylenediaminetetraacetic acid, 5 parts of rectorite, and 15 parts of woody fragrance , 8 parts of polyethyleneimine.

[0021] Add deionized water 10 times its mass to polyacrylic acid, stir for 5 minutes, then add polyethyleneimine, then raise the temperature to 55°C, and treat at this temperature for 300 minutes to prepare a polyacrylic acid mixture for use. Grind and pass through an 80-mesh sieve, add 8 times the mass of absolute ethanol, heat to 70°C and stir for 20 minutes, then perform ultrasonic treatment for 30 minutes with an ultrasonic power of 800W to obtain ultrasonic treatment solution A. Crush the rectorite and pass through a 200-mesh sieve, then add ethylenediaminetetraacetic acid and mix with deionized water 4 times the mass of the rectorite, and then heat up ...

Embodiment 2

[0023] In the embodiment of the present invention, an early-strength polycarboxylate water reducer is composed of the following raw materials in parts by weight: 63 parts of polyacrylic acid, 42 parts of ethylenediaminetetraacetic acid, 12 parts of rectorite, and 23 parts of woody , 14 parts of polyethyleneimine.

[0024] Add 12 times the mass of deionized water to polyacrylic acid, stir for 10 minutes, then add polyethyleneimine, then raise the temperature to 60°C, and treat at this temperature for 40 minutes to prepare a polyacrylic acid mixture for use. Grind and pass through a 120-mesh sieve, add 10 times the mass of absolute ethanol, heat to 75°C and stir for 30 minutes, then perform ultrasonic treatment for 40 minutes with an ultrasonic power of 1000W to obtain ultrasonic treatment solution A. Crush the rectorite and pass through a 200-mesh sieve, then add ethylenediaminetetraacetic acid and mix with deionized water 5 times the mass of the rectorite, and then heat up to ...

Embodiment 3

[0026] In the embodiment of the present invention, an early-strength polycarboxylate water reducer is composed of the following raw materials in parts by weight: 57 parts of polyacrylic acid, 35 parts of ethylenediaminetetraacetic acid, 7 parts of rectorite, and 17 parts of woody fragrance , 10 parts of polyethyleneimine.

[0027] Add 11 times the mass of deionized water to polyacrylic acid, stir for 8 minutes, then add polyethyleneimine, then raise the temperature to 60°C, and treat at this temperature for 40 minutes to prepare a polyacrylic acid mixture for use. Grind and pass through a 120-mesh sieve, add 9 times the mass of absolute ethanol, heat to 75°C and stir for 30 minutes, then perform ultrasonic treatment for 40 minutes with an ultrasonic power of 1000W to obtain ultrasonic treatment solution A. Crush the rectorite and pass through a 200-mesh sieve, then add ethylenediaminetetraacetic acid and mix with deionized water 4.5 times the mass of the rectorite, and then he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an early-strength polycarboxylate superplasticizer and a preparation method and application thereof. The early-strength polycarboxylate superplasticizer is prepared from, by weight, 55-63 parts of polyacrylic acid, 33-42 parts of ethylene diamine tetraacetic acid, 5-12 parts of rectorite, 15-23 pats of radix aucklandiae and 8-14 parts of polyethyleneimine. Deionized water is added to polyacrylic acid, then polyethyleneimine is added, and polyacrylic acid mixed liquor is prepared after heat treatment; radix aucklandiae is ground and screened, absolute ethyl alcohol is added for heat treatment, and then ultrasonic treatment is carried out to prepare ultrasonic treatment fluid A; rectorite is smashed and screened, then ethylene diamine tetraacetic acid and deionized water are added, and ultrasonic treatment is carried out to prepare ultrasonic treatment fluid B; the ultrasonic treatment fluid A and the ultrasonic treatment fluid B are mixed for heat treatment and filtration, supernatant liquid is taken, the polyacrylic acid mixed liquor is added, and heat treatment is conducted to obtain the early-strength polycarboxylate superplasticizer. The early-strength polycarboxylate superplasticizer has the advantages of being low in agent content, good in early strength effect, capable of preventing steel bars from being rusted, high in compressive strength and the like.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an early-strength polycarboxylate water reducer and its preparation method and application. Background technique [0002] Water reducer is a concrete admixture that can reduce the amount of mixing water while maintaining the slump of concrete. Most of them are anionic surfactants, such as lignosulfonate, naphthalenesulfonate formaldehyde polymer, etc. After being added to the concrete mixture, it can disperse the cement particles, improve its workability, reduce the unit water consumption, improve the fluidity of the concrete mixture; or reduce the unit cement consumption and save cement. Among them, the polycarboxylate high-performance water reducer (liquid) is the third generation of high-performance water reducer developed after the ordinary water reducer represented by wood calcium and the high-efficiency water reducer represented by naphthalene. At present, it i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/32C04B103/30
CPCC04B40/0039C04B2103/302C04B24/2641C04B24/123C04B14/10C04B16/02C04B24/32C04B28/04
Inventor 董明
Owner SHANDONG JINGJIN NEW ENERGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com