Songguan Yuebai Ge kiln glaze material

A kind of glaze and kiln technology, applied in the field of porcelain, can solve the problems of unknowable principle, ice cracking, low chance of eel blood, etc.

Inactive Publication Date: 2016-07-06
LONGQUAN NANSONG GE KILN PORCELAIN CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, in the porcelain of Fangge Kiln, the probability of ice cracking and eel blood is very low, and most of them are fine grains. The mechanism is still unknown

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A Songguan Yue Baige kiln glaze, in parts by weight, the glaze comprises 200 parts of Baoxiwutou glaze soil, 70 parts of quartz powder, 20 parts of Mudaikou Zijin Earth, 180 parts of limestone, and 150 parts of potash feldspar , 100 parts of kaolin, 80 parts of talc, the glaze also includes 1 part of graphene and 1 part of dysprosium oxide.

Embodiment 2

[0017] A Songguanyue Baige kiln glaze, in parts by weight, the glaze comprises 350 parts of Baoxiwutou glaze soil, 100 parts of quartz powder, 50 parts of Mudaikou Zijin soil, 230 parts of limestone, and 200 parts of potash feldspar , 170 parts of kaolin, 100 parts of talc, and the glaze further includes 100 parts of graphene and 100 parts of dysprosium oxide.

Embodiment 3

[0019] A Songguanyue Baige kiln glaze, in parts by weight, the glaze comprises 250 parts of Baoxiwutou glaze soil, 80 parts of quartz powder, 30 parts of Mudaikou Zijin Earth, 200 parts of limestone, and 180 parts of potash feldspar , 130 parts of kaolin, 90 parts of talc, the glaze also includes 60 parts of graphene and 40 parts of dysprosium oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to porcelain, in particular to a preparation method of Ge porcelain, comprising the steps: preparing glaze material: according to parts by weight, comprising 200-500 parts of Baoxi Wutou glaze earth, 70-100 parts of quartz powder, 20-50 parts of Mudaikou purple clay, 180-230 parts of limestone, 150-200 parts of potassium feldspar, 100-170 parts of kaolin and 80-100 parts of talcum powder, ball-milling to obtain powder 120-200 in mesh; preparing a clay base, forming a porcelain base, drying, biscuiting, applying inner and outer glaze, and burning the glaze to obtain a finished product. The method is characterized in that the glaze material in step 1 also comprises 1-100 parts of graphene and 1-100 parts of dysprosium oxide.

Description

technical field [0001] The invention belongs to the field of porcelain, and in particular relates to a Song Guanyue Baige kiln glaze. Background technique [0002] Ge Kiln is one of the five famous kilns in the Song Dynasty. There is such a description in "Ge Gu Yao Lun" in the Ming Dynasty: "Ge Kiln patterns take ice cracks and eel blood as the top, followed by plum blossom ink patterns. "Unfortunately, the kiln site of Song Ge Kiln has not been discovered by people so far. We can only interpret the history of Ge Kiln from the handed down works. The important feature of Ge glaze porcelain is the glaze cracking, which is a natural cracking phenomenon that occurs on the glaze. Cracking was originally a defect in the firing of porcelain. Later, people mastered the law of cracking and consciously made it crack, thus producing a unique aesthetic feeling. The enamel of the Ge glaze porcelain in the Song Dynasty is shiny and smooth, and the glaze surface of the whole body is int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 金逸瑞卓鑫伟陈江海
Owner LONGQUAN NANSONG GE KILN PORCELAIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products