A preparation method and application of modified superparamagnetic iron tetraoxide nanoparticles

A nanoparticle, superparamagnetic technology, applied in chemical instruments and methods, alkali metal oxides/hydroxides, inorganic chemistry, etc., can solve problems such as environmental pollution, mercury metal loss, secondary pollution, etc., and meet the preparation conditions Low requirements, simple preparation process and large specific surface area

Active Publication Date: 2018-04-06
KUNMING UNIV OF SCI & TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There is a large amount of mercury in many industrial wastewaters. The existence of these mercury compounds will not only cause environmental pollution, threaten human health, but also cause a large amount of mercury metal loss
Due to the existence of many forms in mercury-containing wastewater, it is difficult to remove it by general methods
At present, the precipitation method is the main method for removing mercury in industry. Its principle is to use a precipitant to precipitate mercury in mercury-containing wastewater, but the precipitate generated in this process is not easy to separate, and the used precipitant will also cause Secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The preparation method of the sulfoamino modified superparamagnetic nanomaterial is as follows:

[0017] (1) Add 20 mol of FeCl 3 .6H 2 O and 10mol FeCl 2 .4H 2 Dissolve O in 1L of deionized water, then drop 3L of NH 4 OH solution (0.50 mol / L), mechanically stirred at 60℃; use a magnet to remove Fe 3 O 4 The nanoparticles are separated from the suspension and washed repeatedly with deionized water to obtain nano-Fe 3 O 4 particle.

[0018] (2) According to the ratio of 16g / L, nano Fe 3 O 4 Disperse ultrasonically in a mixed solution of ethanol and water (the volume ratio of ethanol and water is 20:1) to obtain a suspension. Add an aqueous ammonia solution (commercially available; 25 wt%) to the suspension at a ratio of 17 ml / L. During the stirring process, add ethyl orthosilicate to the mixed solution at a ratio of 20ml / L, and keep stirring at 60℃ for 4h to obtain Fe 3 O 4 @SiO 2 Nanoparticles, then use a magnet to transfer Fe 3 O 4 @SiO 2 The nanoparticles are separated from...

Embodiment 2

[0023] The preparation method of the sulfoamino modified superparamagnetic nanomaterial is as follows:

[0024] (1) Put 21mol FeCl 3 .6H 2 O and 10.5mol FeCl 2 .4H 2 Dissolve O in 1L of deionized water, and then drop 3.1L of NH 4 OH solution (0.55 mol / L), mechanically stirred at 70 ℃; Fe 3 O 4 The nanoparticles are separated from the suspension and washed repeatedly with deionized water to obtain nano-Fe 3 O 4 particle.

[0025] (2) According to the ratio of 17g / L, nano-Fe 3 O 4 Disperse ultrasonically in a mixed solution of ethanol and water (the volume ratio of ethanol and water is 10:1) to obtain a suspension. Add an aqueous ammonia solution (commercially available; 25 wt%) to the suspension at a ratio of 20 ml / L. During the stirring process, add ethyl orthosilicate to the mixed solution at the ratio of 21ml / L, and keep stirring at 55℃ for 5h to obtain Fe 3 O 4 @SiO 2 Nanoparticles, then use a magnet to transfer Fe 3 O 4 @SiO 2 The nanoparticles are separated from the suspension,...

Embodiment 3

[0030] The preparation method of the sulfoamino modified superparamagnetic nanomaterial is as follows:

[0031] (1) Put 22 mol of FeCl 3 .6H 2 O and 11mol FeCl 2 .4H 2 Dissolve O in 1L of deionized water, then drop 3.5L of NH 4 OH solution (0.55 mol / L), mechanically stirred at 80 ℃; Fe 3 O 4 The nanoparticles are separated from the suspension and washed repeatedly with deionized water to obtain nano-Fe 3 O 4 particle.

[0032] (2) According to the ratio of 16.5g / L, nano-Fe 3 O 4 Disperse ultrasonically in a mixed solution of ethanol and water (the volume ratio of ethanol to water is 20:1.5) to obtain a suspension. Add an aqueous ammonia solution (commercially available; 25 wt%) to the suspension at a ratio of 18 ml / L. During the stirring process, add ethyl orthosilicate to the mixed solution at a ratio of 22ml / L, and keep stirring at 50℃ for 6h to obtain Fe 3 O 4 @SiO 2 Nanoparticles, then use a magnet to transfer Fe 3 O 4 @SiO 2 The nanoparticles are separated from the suspension, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and application of a modified superparamagnetic Fe3O4 nanoparticle, belonging to the field of treatment of industrial wastewater. The method comprises the following steps of preparing the superparamagnetic Fe3O4 nanoparticle by adopting a coprecipitation method; by taking superparamagnetic Fe3O4 as a core, coating the surface of Fe3O4 with one or more layers of silica shells by adopting hydrolysis; modifying coated silica by applying a coupled reaction principle; by taking 3-aminopropyl trimethoxysilane as a modification reagent, modifying on a core-shell structure and connecting to an amino group; finally, using chloromethyl thiirane to synthesize a chelate which simultaneously contains nitrogen and sulfur by a nucleophilic substitution reaction; then using the chelate to adsorb heavy metal mercury, and in particular to selectively adsorb Hg<2+> at normal temperature, wherein the adsorption efficiency of the chelate is significantly higher than that of a chelate which is previously synthesized and only contains a sulfur ligating atom. The modified superparamagnetic Fe3O4 nanoparticle has the advantage of easiness in recovery and regeneration.

Description

Technical field [0001] The invention relates to a modified superparamagnetic Fe 3 O 4 The preparation method and application of nano particles belong to the field of industrial wastewater treatment. Background technique [0002] A large amount of mercury is present in many industrial wastewaters. The presence of these mercury compounds will not only cause environmental pollution and threaten human health, but also cause a large amount of mercury metal loss. Because there are many forms in mercury-containing wastewater, it is difficult to remove it by general methods. At present, the precipitation method is the main method for removing mercury in industry. The principle is to use a precipitant to precipitate mercury in mercury-containing wastewater, but the precipitate produced in this process is not easy to separate, and the used precipitant will also cause Secondary pollution. Summary of the invention [0003] The purpose of the present invention is to provide a modified superp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/28C02F1/28C02F101/20
CPCB01J20/223B01J20/28009B01J20/28016C02F1/285C02F1/288C02F2101/20
Inventor 汤立红包双友李凯宁平张冬冬孙鑫郭惠斌朱婷婷宋辛金旭张秀英
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap