Pure aloe fiber warp and weft double-elasticity yarn-dyed fabric and production technology thereof

A kind of aloe vera fiber and production process technology, applied in fiber processing, plant fiber, textile and other directions, can solve the problems affecting production efficiency and product quality, yarn performance damage, serosal film is easy to fall off, etc., to achieve a clear and elegant overall effect of the cloth. , Light texture, simple pattern loop effect

Inactive Publication Date: 2016-06-08
IANGSU COLLEGE OF ENG & TECH
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the traditional production process, the fine aloe fiber yarn and aloe ammonia core-spun yarn have to go through scouring, bleaching or dyeing processes, and the yarn performance is damaged, especially the pure aloe fiber yarn absorbs dye after dyeing, which is prone to brittleness. beheaded
[0003] After the pure aloe fiber yarn is dyed, its slurry absorption performance is enhanced. To obtain a good soaking effect, the viscosity of the slurry should not be too high. At the same time, if the viscosity is too high, the serous film will become hard, and the serous film will easily fall off during spinning and weaving, which will affect production. efficiency and product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pure aloe fiber warp and weft double-elasticity yarn-dyed fabric and production technology thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0035] A kind of production technology according to described pure aloe fiber warp and weft double-elastic yarn-dyed wrinkle cloth, comprises the steps:

[0036] Step (1), winding process:

[0037] Autoconer338 winding machine is adopted, the winding speed is set to 1100m / min, the winding tension is 33cN, and the winding density is 0.41g / cm 3 , in order to improve the yarn quality, the machine is equipped with USTERQUANTUM-2 electronic yarn clearer to improve the accuracy of removing harmful yarn defects such as neps, thick places, and fine details. The yarn clearing process parameters are set to neps + 350%, Short thick place +220%×2.0cm, long thick place +40%×40cm, long thick place -35%×40cm;

[0038] Step (2), warping process:

[0039] Since there are only two types of fabric dyed yarns and the pattern cycle is simple, Swiss BENNINGER (BENNINGER) ZDA batch warping machine is used; in order to enable the shed to be opened and cleared with a small tension on the machine dur...

specific Embodiment 2

[0047] A kind of production technology according to described pure aloe fiber warp and weft double-elastic yarn-dyed wrinkle cloth, comprises the steps:

[0048] Step (1), winding process:

[0049] Autoconer338 winding machine is adopted, the winding speed is set to 1400m / min, the winding tension is 36cN, and the winding density is 0.44g / cm 3 , in order to improve the yarn quality, the machine is equipped with USTERQUANTUM-2 electronic yarn clearer to improve the accuracy of removing harmful yarn defects such as neps, thick places, and fine details. The yarn clearing process parameters are set to neps + 350%, Short thick place +220%×2.0cm, long thick place +40%×40cm, long thick place -35%×40cm;

[0050] Step (2), warping process:

[0051] Since there are only two types of fabric dyed yarns and the pattern cycle is simple, Swiss BENNINGER (BENNINGER) ZDA batch warping machine is used; in order to enable the shed to be opened and cleared with a small tension on the machine dur...

specific Embodiment 3

[0059] A kind of production technology according to described pure aloe fiber warp and weft double-elastic yarn-dyed wrinkle cloth, comprises the steps:

[0060] Step (1), winding process:

[0061] Autoconer338 winding machine is adopted, the winding speed is set to 1300m / min, the winding tension is 35cN, and the winding density is 0.42g / cm 3 , in order to improve the yarn quality, the machine is equipped with USTERQUANTUM-2 electronic yarn clearer to improve the accuracy of removing harmful yarn defects such as neps, thick places, and fine details. The yarn clearing process parameters are set to neps + 350%, Short thick place +220%×2.0cm, long thick place +40%×40cm, long thick place -35%×40cm;

[0062] Step (2), warping process:

[0063] Since there are only two types of fabric dyed yarns and the pattern cycle is simple, Swiss BENNINGER (BENNINGER) ZDA batch warping machine is used; in order to enable the shed to be opened and cleared with a small tension on the machine dur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensionaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses pure aloe fiber warp and weft double-elasticity yarn-dyed fabric and a production technology thereof. The pure aloe fiber warp and weft double-elasticity yarn-dyed fabric comprises a warp yarn, a weft yarn and an elastic yarn, wherein 60S aloe fiber yarns are adopted as the warp yarn and the weft yarn; aloe 50S / 20D is adopted as the elastic yarn; a plain fancy cellular structure is adopted as a fabric structure; a bottom structure formed by plain as main material and triple fancy cellular structures in the transverse direction and longitudinal direction; an edge structure is the plain; and a jacquard part is formed by the fancy cellular structure as main part in transverse direction and horizontal direction matched with the shrinkage action of an aloe fiber spandex core-spun yarn. The production technology comprises a spooling step, a warping step, a slashing step, a drafting step and a weaving step. The fabric is reasonable in color match, light and thin in texture and slight in wrinkle, and gives a casual feeling to a consumer. Meanwhile, the pattern is relatively large in cycle, and is matched with unique plain fancy cellular structure, so that the fabric is high in third dimension and good in breathability. The weaving efficiency reaches 91%; and the first grade percentage put in storage reaches 99%.

Description

technical field [0001] The invention belongs to the field of textile textiles, and in particular relates to a yarn-dyed crepe cloth with double elastic warp and latitude of pure aloe fibers and a production process thereof. Background technique [0002] In the traditional production process, the fine aloe fiber yarn and aloe ammonia core-spun yarn have to go through scouring, bleaching or dyeing processes, and the yarn performance is damaged, especially the pure aloe fiber yarn absorbs dye after dyeing, which is prone to brittleness. beheaded. [0003] After the pure aloe fiber yarn is dyed, its slurry absorption performance is enhanced. To obtain a good soaking effect, the viscosity of the slurry should not be too high. At the same time, if the viscosity is too high, the serous film will become hard, and the serous film will easily fall off during spinning and weaving, which will affect production. efficiency and product quality. Contents of the invention [0004] Purpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/08D03D9/00D03D13/00D06M15/285D06M13/148D06M13/02D06M101/04D03D15/56
CPCD03D9/00D03D13/008D06M13/02D06M13/148D06M15/285D06M2101/04D10B2201/20D10B2331/08D03D15/56
Inventor 马顺彬
Owner IANGSU COLLEGE OF ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products