Bowlder imitation ceramic tile
A technology of stone tiles and imitation jade, which is applied in the field of building decoration materials, can solve the problems that the decorative effect is not as good as that of natural jade stones, the glossiness of polished tiles is not ideal, and the radiation is low, so as to achieve natural and simple patterns and broad market economic benefits , Good antifouling effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] Add 50-60% by weight of medium- and low-temperature porcelain sand to 20-30% by weight of stone powder (flux), stir evenly at room temperature, then add 15-25% by weight of clay, and mix evenly at room temperature to form The blank is used as a mixture for use, and the weight percentage of the powder particle size is: 40 mesh sieve or less: 30%; 40 to 80 mesh sieve: 11 to 49%; 80 to 100 mesh sieve: 15%; 100 mesh The excess of 3.8% is sieved, and then processed by ball milling, spray granulation, and press pressing. The forming pressure of the blank is 250 to 300 bar. The pressed blank is dried and soaked. The drying temperature is: 180~230℃; drying time: 50~80min. Add 78-90% by weight of penetrating agent to 8-20% by weight of soluble coloring salt and 1-2.5% by weight of CMC, stir evenly at room temperature to make a glaze, and pass the blank through the process of glazing and granulation Processing, the blanks treated by the above-mentioned process are then processed...
Embodiment 2
[0028] Add 50% by weight of medium and low temperature porcelain sand to 30% by weight of stone powder (flux), stir evenly at room temperature, then add 20% by weight of clay, mix evenly at room temperature, and form a mixture for billet for use , the weight percentage of the powder particle size is: 35 mesh sieves: 30%; 42 mesh sieves: 11%; 81 mesh sieves: 15%; 105 mesh sieves 3.8%, then through ball milling, spray granulation, The pressing process of the press, the forming pressure of the blank: 250bar, and the drying and bleeding process of the pressed blank, the drying temperature: 180°C; drying time: 50min. Add 90% by weight of penetrating agent to 8% by weight of soluble coloring salt and 1% by weight of CMC, stir evenly at room temperature to make a glaze, and process the blank through the process of glazing and grain distribution. The blanks treated by the above process are then processed by the shaping process, and finally the blanks treated by the above process are p...
Embodiment 3
[0031] Add 53% by weight of medium- and low-temperature porcelain sand to 29% by weight of stone powder (flux), stir evenly at room temperature, then add 18% by weight of clay, mix evenly at room temperature, and form a mixture for billet for use , the weight percentage of the powder particle size is: 30 mesh sieves: 30%; 50 mesh sieves: 19%; 90 mesh sieves: 15%; 110 mesh sieves 3.8%, then through ball milling, spray granulation, The pressing process of the press, the forming pressure of the blank: 260bar, the drying and flowering process of the pressed blank, the drying temperature: 190°C; drying time: 56min, 88% by weight of the penetrating agent Add 10% by weight of soluble coloring salt and 1.1% by weight of CMC, stir evenly at room temperature to make a glaze, process the blank through the process of glazing and cloth granulation, and then process the blank through the aforementioned process. After the shaping process, the blanks treated by the above process are finally p...
PUM
Property | Measurement | Unit |
---|---|---|
flexural strength | aaaaa | aaaaa |
flexural strength | aaaaa | aaaaa |
flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com