Bowlder imitation ceramic tile

A stone tile and jade imitation technology, applied in the field of building decoration materials, can solve the problems that the decorative effect is not as good as natural jade rhyme stone, the gloss of polished tiles is not ideal, high radiation and other problems, and achieves realistic and delicate patterns, clear lines, crystal clear effect

Active Publication Date: 2012-12-19
广东金科陶瓷有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the glossiness of polished tiles is not ideal, and its decorative effect is not as good as that of natural jade rhyme stones. Natural jade rhyme stones are favored by certain customer groups because of their natural texture and good gloss; but because of their higher radiation It is prohibitive for people. Customers need new products with the same decorative effect and gloss as jade rhyme stones, but lower radiation than jade rhyme stones. It is close to natural jade rhyme, but there is still a certain gap. Various companies have been researching new technologies for polished tiles, trying to develop products with better performance and higher quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 3

[0025] Add 53% by weight of medium- and low-temperature porcelain sand to 29% by weight of stone powder (flux), stir evenly at room temperature, then add 18% by weight of clay, mix evenly at room temperature, and form a mixture for billet for use , the weight percentage of the powder particle size is: 30 mesh sieves: 30%; 50 mesh sieves: 27%; 90 mesh sieves: 15%; 110 mesh sieves 3.8%, then through ball milling, spray granulation, The pressing process of the press, the forming pressure of the blank: 260bar, the drying and flowering process of the pressed blank, the drying temperature: 190°C; drying time: 56min, 88% by weight of the penetrating agent Add 10% by weight of soluble coloring salt and 1.1% by weight of CMC, stir evenly at room temperature to make a glaze, process the blank through the process of glazing and cloth granulation, and then process the blank through the aforementioned process. After the shaping process, the blanks treated by the above process are finally p...

Embodiment 4

[0028] Add 53% by weight of medium- and low-temperature porcelain sand to 30% by weight of stone powder (flux), stir evenly at room temperature, then add 19% by weight of clay, mix evenly at room temperature, and form a mixture for billet for use , the weight percentage of the powder particle size is: 25 mesh sieves: 30%; 48 mesh sieves: 28%; 90 mesh sieves: 15%; 110 mesh sieves 3.8%, then through ball milling, spray granulation, The pressing process of the press, the forming pressure of the blank: 280bar, and the drying and bleeding process of the pressed blank, the drying temperature: 200°C; drying time: 70min. Add 78% by weight of penetrating agent to 20% by weight of soluble coloring salt and 1.5% by weight of CMC, stir evenly at room temperature to make glaze, and process the blank through the process of glazing and grain distribution. The blanks treated by the above process are then processed by the shaping process, and finally the blanks treated by the above process are...

Embodiment 5

[0031] Add 60% by weight of medium and low-temperature porcelain sand to 25% by weight of stone powder (flux), stir evenly at room temperature, then add 15% by weight of clay, mix evenly at room temperature, and form a mixture for billet for use , the weight percentage of the powder particle size is: 20 mesh sieve: 30%; 60 mesh sieve: 25%; 93 mesh sieve: 15%; 115 mesh sieve 3.8%, then through ball milling, spray granulation, The pressing process of the press, the forming pressure of the blank: 300bar, and the drying and bleeding process of the pressed blank, the drying temperature: 230°C; drying time: 80min. Add 89% by weight of penetrant to 10% by weight of soluble coloring salt and 1% by weight of CMC, and stir evenly at room temperature to make a glaze. The blanks treated by the above process are then processed by the shaping process, and finally the blanks processed by the above process are placed in the kiln, and the finished product is calcined at a firing temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a rhyme stone tile of artificial jade. The weight percentages of main materials are as follows: 50-60 percent of porcelain sand of medium-low temperature, 20-30 percent of stone powder and 15-25 percent of clay, wherein, the stone powder acts as flux; the weight percentages of glazes are as follows: 78-90 percent of penetrating agent, 8-20 percent of soluble coloring salt and 1-2.5 percent of CMC; the weight percentages of powder by particle size are as follows: 30 percent of powder with 40 mesh, 19-30 percent of powder with 40 to 80 mesh, 15 percent of powder with 80 to 100 mesh, and 3.8 percent of powder with 100 mesh; the molding pressure of blank pieces is 250-300bar; the sintering temperature is 1,160-1,220 DEG C; the sintering period is 60-90 minutes. The rhyme stone tile of artificial jade integrates a seep curlicue technology, a fine powder technology and an artificial jade technology into a whole; the product has the advantages of smooth body, lifelike and fine patterns and decorative designs, rich changes, clear lines, jade texture similar to that of natural jade, crystal qualitative sense, as well as fresh and generous shape.

Description

technical field [0001] The invention relates to a building decoration material, in particular to a jade imitation stone tile. Background technique [0002] With the industrialization of housing and the improvement of people's living standards, the market share of high-quality and multi-functional green building materials will gradually increase, and the development of products will tend to be diversified, personalized, fashionable, environmentally friendly and healthy. In order to meet the needs of people in today's society, various new building decoration materials have emerged as the times require. All products are developed to meet market demand. From the early gorgeous decorative effects to the present, they are becoming more and more natural, elegant and unique Personality element. [0003] Ceramic products have high density, various varieties, rich designs and colors, good decorative effects, and easy maintenance. The designs and colors of the products are becoming mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/16C04B35/622
Inventor 林海荣
Owner 广东金科陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products