Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Diester-type semisynthetic cutting fluid with high lubrication and high hard water resistance and preparation method thereof

A technology of hard water resistance and double ester type, which is applied in the direction of lubricating composition and petroleum industry, can solve the problems of insufficient lubricity and hard water resistance, reduce tool temperature and cutting resistance, avoid delamination and demulsification, and resist Excellent bacterial effect

Inactive Publication Date: 2016-06-08
SHANGHAI INST OF TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the above-mentioned technical problems in the prior art, the present invention provides a high-lubrication and high-hard-water-resistant diester semi-synthetic cutting fluid and a preparation method thereof. The preparation method thereof solves the technical problem of insufficient lubricity and hard water resistance of the semi-synthetic cutting fluid in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A high-lubrication and high-hard-water-resistant double-ester semi-synthetic cutting fluid, wherein each raw material component is calculated by weight percentage, and its composition and content are as follows:

[0059] Synthetic ester 40%;

[0060] Surfactant 3%;

[0061] Rust inhibitor 12%;

[0062] Solubilizer 2%;

[0063] Corrosion and scale inhibitor 1%;

[0064] Aluminum corrosion inhibitor 0.2%;

[0065] 0.5% defoamer;

[0066] Fungicide 2%;

[0067] water balance;

[0068]The synthetic ester is composed of trimethylolpropane oleate and trimellitate; the surfactant is fatty alcohol polyoxyethylene ether, or capric acid; the rust inhibitor is boric acid, or three Ethanolamine; the solubilizer is glycerol; the corrosion and scale inhibitor is fatty acid amide; the aluminum corrosion inhibitor is phosphoric acid ester; the defoamer is polyether; Copper pyridine sulfate.

[0069] The preparation method of the above-mentioned a kind of high lubricating high ...

Embodiment 2

[0072] A high-lubrication and high-hard-water-resistant double-ester semi-synthetic cutting fluid, wherein each raw material component is calculated by weight percentage, and its composition and content are as follows:

[0073] Synthetic ester 35%;

[0074] Surfactant 5%;

[0075] Antirust agent 20%;

[0076] Solubilizer 5%;

[0077] Corrosion and scale inhibitor 5%;

[0078] Aluminum corrosion inhibitor 0.5%;

[0079] Defoamer 1%;

[0080] Fungicide 5%;

[0081] water balance;

[0082] The synthetic ester is composed of pentaerythritol fatty acid ester and fatty acid diester; the surfactant is vinyl ether succinic acid derivative, or caprylic acid; the rust inhibitor is naphthenic acid, monoethanolamine, or diethanolamine The solubilizer is isomeric stearyl alcohol; the corrosion and scale inhibitor is fatty acid diethanolamide; the aluminum corrosion inhibitor is 2-amino-2 methyl-1 propanol; The defoamer is emulsified silicone oil; the bactericide is methylisothiazol...

Embodiment 3

[0086] A high-lubrication and high-hard-water-resistant double-ester semi-synthetic cutting fluid, wherein each raw material component is calculated by weight percentage, and its composition and content are as follows:

[0087] Synthetic ester 37%;

[0088] Surfactant 4%;

[0089] Antirust agent 16%;

[0090] Solubilizer 4%;

[0091] Corrosion and scale inhibitor 4%;

[0092] Aluminum corrosion inhibitor 0.3%;

[0093] Defoamer 0.7%;

[0094] Fungicide 4%;

[0095] water balance;

[0096] The synthetic ester is composed of trimethylolpropane fatty acid ester and fatty acid diester; the surfactant is fatty alcohol alkoxylate, capric acid; the rust inhibitor is naphthenic acid, monoethanolamine , triethanolamine; the solubilizer is isomerized cetyl alcohol; the corrosion and scale inhibitor is amide caproic acid cyclohexylamine salt; the aluminum corrosion inhibitor is 3-amino-4-octanol; The defoamer is polyether; the bactericide is hydroxymethylethanolamine.

[0097] W...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a diester-type semisynthetic cutting fluid with high lubrication and high hard water resistance. The cutting fluid comprises, by weight, 30-40% of synthetic ester, 3%-5% of a surface active agent, 12%-20% of an antirust, 2%-5% of a solubilizer, 1%-5% of a corrosion inhibitor, 0.2%-0.5% of an aluminum corrosion inhibitor, 0.5%-1% of a defoaming agent, 2%-5% of a bactericidal agent and the balance of water. The invention also provides a preparation method of the semisynthetic cutting fluid. The method is as below: adding the surface active agent, antirust agent, corrosion inhibitor, solubilizer, aluminum corrosion inhibitor, defoaming agent, bactericidal agent and water in the synthetic diester in order, and mixing evenly to obtain the diester-type semisynthetic cutting fluid with high lubrication and high hard water resistance. The diester-type semisynthetic cutting fluid with high lubrication and high hard water resistance has superior performances in lubrication, hard water resistance, aluminum corrosion inhibition, corrosion resistance, rust proof and defoaming.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a cutting fluid, in particular to a high-lubrication and high-hard-water-resistant diester semi-synthetic cutting fluid and a preparation method thereof. Background technique [0002] Semi-synthetic cutting fluid is the trend and trend of metalworking fluid development today. Its advantages and disadvantages are between emulsion and fully synthetic fluid. It has good cooling, cleaning and rust resistance. The disadvantage is that its lubricity is not as good as Emulsion, hard water resistance is not as good as fully synthetic fluid. [0003] At present, the shortcomings of semi-synthetic cutting fluids used in large-scale machinery, automobiles, bearings and other manufacturing industries at home and abroad are fully exposed. The hard water property is not good, so it cannot be used for the water quality requirements of some areas with high hard water. Seriously restrict the devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10N30/12C10N30/16C10N30/18C10N40/22
CPCC10M173/02C10N2030/12C10N2030/16C10N2030/18C10N2040/22
Inventor 蔺华林韩生王爱民周祖新吴志桥余焓于飞卢德力蒋继波李原婷邱丰裴素鹏祝俊何忠义熊丽萍
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com