Novel stainless steel negative ion healthcare material and manufacturing technology thereof

A technology of health care material and preparation process, which is applied in metal processing equipment, transportation and packaging, etc., to achieve the effect of unique preparation process and high precision of process control

Inactive Publication Date: 2016-06-01
FOSHAN SUCCESS JEWELRY CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on utilizing stainless steel to manufacture health care materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The invention provides a novel stainless steel negative ion health care material and a preparation process thereof, comprising the steps of:

[0021] 1) Weigh 150g of negative ion far-infrared master powder particles with a particle diameter of 1000 mesh, 850g of fine stainless steel powder with a particle diameter of 400 mesh, and 20g of cation exchange powder resin micropowder;

[0022] 2) Put the raw materials into the mixing drum, rotate and mix for 3 hours;

[0023] 3) Put the mixed material into the metal mold assembly, and stamp it on the oil pressure for preliminary forming;

[0024] 4) Put the preliminarily formed material in a vacuum automatic furnace, sinter and smelt at 1250° C. for 35 minutes, and after solidification and molding, cool down and come out of the furnace.

Embodiment 2

[0026] The invention provides a novel stainless steel negative ion health care material and a preparation process thereof, comprising the steps of:

[0027] 1) Weigh 20g of negative ion far-infrared master powder particles with a particle diameter of 500 mesh, 980g of fine stainless steel powder with a particle diameter of 600 mesh, and 20g of cation exchange powder resin micropowder;

[0028] 2) Put the raw materials into the mixing drum, rotate and mix for 3 hours;

[0029] 3) Put the mixed material into the metal mold assembly, and stamp it on the oil pressure for preliminary forming;

[0030] 4) Place the preliminarily formed material in a vacuum automatic furnace, sinter and smelt at 1200°C for 40 minutes, and after solidification and molding, cool and come out of the furnace.

Embodiment 3

[0032] The invention provides a novel stainless steel negative ion health care material and a preparation process thereof, comprising the steps of:

[0033] 1) Weighing 250g of negative ion far-infrared master powder particles with a particle diameter of 1500 mesh, 750g of fine stainless steel powder with a particle diameter of 150 mesh, and 20g of cation exchange powder resin micropowder;

[0034] 2) Put the raw materials into the mixing drum, rotate and mix for 3 hours;

[0035] 3) Put the mixed material into the metal mold assembly, and stamp it on the oil pressure for preliminary forming;

[0036] 4) Place the preliminarily formed material in a vacuum automatic furnace, sinter and smelt at 1300°C for 30 minutes, and after solidification and molding, cool and take out the furnace.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a novel stainless steel negative ion healthcare material and a manufacturing technology thereof. The novel stainless steel negative ion healthcare material is machined through components which include, by mass, 2-25 parts of negative ion far infrared mother powder particles, 73-96 parts of fine stainless steel powder and 2 parts of cation exchange powder resin micropowder. The manufacturing technology includes the steps of raw material weighing, rotating mixing, compressing molding and sintering smelting. On the basis of adopting a conventional stainless steel material, a negative ion raw material is added, on the basis that the stainless steel material is reserved as the structural material, the negative ion raw material can release negative ion energy, the healthcare functions of strengthening, adjusting and balance assisting of all the systems of a human body are achieved, in addition, the manufacturing technology is unique, and the technology control precision is high.

Description

technical field [0001] The invention relates to the technical field of novel material manufacture, in particular to a novel stainless steel anion health care material and a preparation process thereof. Background technique [0002] As a material with excellent corrosion resistance, oxidation resistance, formability and welding performance, stainless steel is widely used in people's daily life, industrial construction, municipal engineering and many other fields, and is also very popular among people. At present, my country is not only a big producer of stainless steel, but also a big user. In addition to iron and carbon, stainless steel also contains other metal elements such as chromium and nickel. These added metal elements are mainly used to improve the performance of stainless steel, improve its heat resistance, corrosion resistance, mechanical properties, etc. However, there are few reports on utilizing stainless steel to manufacture health care materials. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F3/02B22F3/10
CPCB22F3/02B22F3/10B22F2998/10B22F1/10
Inventor 张庆团
Owner FOSHAN SUCCESS JEWELRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products