Water-foamed, antibacterial and air-permeable microporous film masterbatch, film and preparation method thereof

A technology of microporous film and water foaming, which is applied in the fields of water foaming antibacterial and breathable microporous film masterbatch, plastic film and its preparation, which can solve the problem of long time for filler particles to dissolve out, open porosity affecting film strength, uncertain There are many factors to achieve the effect of excellent comprehensive mechanical properties, controllable micropore density, and small and uniform cell size

Active Publication Date: 2016-05-11
深圳市环美盛科技有限公司
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is relatively simple and easy, but the dissolution of filler particles takes a long time
[0006] 2. The mechanical method is the method of mechanical hole making, such as drilling with a roller with needles, etc., and the mechanical stretching method is one of the new methods for manufacturing microporous breathable films, but this method is complicated in process and has many uncertain factors. not easy to control
This foaming method must control the foaming process to be open foaming, and too much open cell foaming will affect the film strength, and the chemical foaming agent will bring environmental health problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A water-foaming antibacterial and breathable microporous film masterbatch, consisting of the following materials in parts by weight: 90 parts of polyethylene, 3 parts of EVA, 10 parts of sepiolite powder + calcium sulfate whiskers, tert-butyl peroxycarbonate-2-ethyl 0.04 part of hexyl ester, 0.08 part of acrylate, 1 part of silane coupling agent, 0.5 part of plastic antioxidant.

[0031] The preparation method of the water-foaming antibacterial and breathable microporous film containing the above-mentioned water-foaming antibacterial and breathable microporous film masterbatch comprises the following steps:

[0032] S1. Put the microporous water-absorbing inorganic foaming material into a high-speed mixer, add a surfactant and mix for 15 minutes, then put in polyethylene raw materials, modifiers, initiators, antioxidants, premix for 25 minutes, and then mix the premix Put into twin-screw extruder to granulate into water-foaming antibacterial and breathable microporous f...

Embodiment 2

[0037] A water-foaming antibacterial and breathable microporous film, made of the following materials in parts by weight: 80 parts of polypropylene, 5 parts of POE, 20 parts of ultrafine microporous calcium carbonate+zinc oxide whiskers, 0.03 parts of benzoyl peroxide, 0.15 parts of divinylbenzene, 2 parts of aluminum-titanium composite coupling agent, and 3 parts of plastic antioxidant.

[0038] The preparation method of the water-foaming antibacterial and breathable microporous film containing the above-mentioned water-foaming antibacterial and breathable microporous film masterbatch comprises the following steps:

[0039] S1. Put the water-absorbing microporous inorganic foaming material into the high-speed mixer, add the surfactant and mix for 20 minutes, then put in the raw materials, modifiers, initiators, antioxidants, pre-mix for 30 minutes, and then put the premix into the double Screw extruder granulation into water foaming to prepare antibacterial breathable micropo...

Embodiment 3

[0044]A water-foaming antibacterial and breathable microporous film, made of the following materials by weight: 70 parts of ethylene-vinyl acetate copolymer, 2 parts of polyvinyl alcohol, 30 parts of diatomaceous earth+calcium sulfate whiskers, benzoyl peroxide Acyl 0.02 parts, styrene 0.2 parts, surfactant 1.5 parts, plastic antioxidant 2 parts.

[0045] The preparation method of the water-foaming antibacterial and breathable microporous film containing the above-mentioned water-foaming antibacterial and breathable microporous film masterbatch comprises the following steps:

[0046] S1. Put the water-absorbing microporous inorganic foaming material into the high-speed mixer, add the surfactant and mix for 20 minutes, then put in the raw materials, modifiers, initiators, antioxidants, pre-mix for 25 minutes, and then put the premix into the double Screw extruder granulation into water foaming to prepare antibacterial breathable microporous film masterbatch;

[0047] S2. Put t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to air-permeable microporous film masterbatch and further relates to a masterbatch containing plastic film and a preparation method thereof. The water-foamed, antibacterial and air-permeable microporous film masterbatch contains a polyolefin polymer, a modifier, a microporous water-absorbing inorganic expanded material, an initiator, a surfactant and a plastic antioxidant. The water-foamed, antibacterial and air-permeable microporous film contains the water-foamed, antibacterial and air-permeable microporous film masterbatch and blow-molded film plastics. The preparation method comprises the steps of granulating the masterbatch, then, carrying out water absorbing aging, adding the blow-molded film plastics, carrying out mixing, and adding the mixture into a foaming and extruding film blowing machine for extrusion, thereby preparing the film. The water-foamed, antibacterial and air-permeable microporous film provided by the invention has the characteristics of simple and stable preparation process, good processability and the like; a water foamer is adopted, is environment-friendly and safe and has an antibacterial function, and the extruded antibacterial and air-permeable film is controllable in micropore density, has the characteristics of fine and uniform open porous texture and cell size, and the like and has the characteristics of excellent comprehensive mechanical properties, environment-friendliness, easiness in recovery, and the like.

Description

technical field [0001] The invention relates to a breathable microporous film masterbatch, in particular to a water-foaming antibacterial and breathable microporous film masterbatch, and also to a plastic film containing the water-foaming antibacterial and breathable microporous film masterbatch and a preparation method thereof. Specifically, it relates to the preparation of an antibacterial and breathable microporous film masterbatch of a thermoplastic polyolefin and inorganic material mixture and the direct addition of this masterbatch to plastics to prepare an antibacterial microporous film, and this film has the effect of breathability, antibacterial and anticorrosion . Background technique [0002] With the development of the scientific level and the improvement of living standards, people use the air-permeable and impervious properties of the breathable microporous film to make rainproof clothes, disposable protective clothes for hospitals, baby diapers, women's hygien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/06C08L51/00C08K3/34C08K7/08C08K7/24C08F255/02C08F220/10C08F212/36C08F291/08C08F212/08C08J5/18C08J9/08B29C47/92B29C48/92
CPCB29C48/92B29C2948/9259B29C2948/92704C08F255/02C08F255/026C08F261/04C08J5/18C08J9/08C08J2203/02C08J2205/044C08J2351/00C08J2351/06C08K3/34C08K3/346C08K7/08C08K7/24C08K2201/014C08L2203/14C08L2203/16C08L51/06C08L51/003C08F220/10C08F212/36C08F212/08
Inventor 廖道权谢太和赵良知林道宏
Owner 深圳市环美盛科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products