A kind of polylactic acid/polycaprolactone/polypropylene composite pelvic floor patch and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polycaprolactone and polylactic acid technology, which is used in prosthesis, tissue regeneration, medical science, etc., can solve problems such as stiff hand feeling, and achieve the effect of good bonding fastness, strong flexibility, and improved quality of life.
Inactive Publication Date: 2018-10-23
DONGHUA UNIV
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Since the hernia mesh requires greater mechanical properties such as stretching and bursting, the mesh structure is tighter and feels stiffer
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] 1. Preparation of Polypropylene Rhomboid Mesh Patch
[0031] (1) Patch weaving: Use polypropylene monofilament with a diameter of 0.1mm as the raw material, and weave it on a three-bar Raschel warp knitting machine with a machine number of 20E to make a patch with a rhombic mesh structure. The yarn motion numbers are:
[0035] (2) Washing of patches: Gently rinse in cold water to remove surface impurities, and dry naturally at room temperature.
[0036] (3) Heat setting of the patch: the heat setting temperature is 130°C, and the heat setting time is 15 minutes.
[0037] 2. Configuration of polylactic acid / polycaprolactone solution
[0038]Weigh 0.84g of polylactic acid granules and 0.36g of polycaprolactone granules into a screw-top glass bottle with a sealed cover, mix the DMC and DMF so...
Embodiment 2
[0049] 1. Preparation of polypropylene hexagonal mesh patch
[0050] (1) Patch weaving: use polypropylene monofilament with a diameter of 0.1mm as the raw material, and weave it on a three-bar Raschel warp knitting machine with a machine number of 16E to make a patch with a hexagonal mesh structure. The yarn motion numbers are:
[0054] (2) Washing of patches: Gently rinse in cold water to remove surface impurities, and dry naturally at room temperature.
[0055] (3) Heat setting of the patch: the heat setting temperature is 130°C, and the heat setting time is 10 minutes.
[0056] 2. Configuration of polylactic acid / polycaprolactone solution
[0057] Weigh 0.84g of polylactic acid granules and 0.36g of polycaprolactone granules into a screw-top glass bottle with a sealed cover, mix the DMC and DMF solutions ev...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
pore size
aaaaa
aaaaa
Basis weight
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a polylactic acid / polycaprolactone / polypropylene composite pelvic floor patch and a preparation method thereof. The composite pelvic floor patch is a three-layer coated patch consisting of an upper coating layer, a lower coating layer and a middle support layer, wherein the coating layers are degradable films, and the support layer is a warp-knitted mesh patch. The preparation method comprises the following steps: knitting polypropylene monofilaments to obtain a polypropylene warp-knitted mesh patch, washing and naturally air-drying the polypropylene warp-knitted mesh patch at room temperature, and then performing heat setting, cooling and cutting; mixing polylactic acid and polycaprolactone, dissolving the mixture in a solvent, and performing heating and stirring to obtain a mixed solution; impregnating the polypropylene warp-knitted mesh patch in the mixed solution, taking out and horizontally arranging the polypropylene warp-knitted mesh patch, and performing volatilization and sterilization to obtain the polylactic acid / polycaprolactone / polypropylene composite pelvic floor patch. According to the composite pelvic floor patch and the preparation method thereof, an absorbable material is combined with a nonabsorbable material, and an impregnation and coating forming process is utilized, so that the prepared coated patch has the advantages of small thickness, strong strength, high flexibility and biocompatibility and the like. The method is simple and convenient to implement, and use of an adhesive is not required.
Description
technical field [0001] The invention belongs to the field of pelvic floor patch and its preparation, in particular to a polylactic acid / polycaprolactone / polypropylene composite pelvic floor patch and a preparation method thereof. Background technique [0002] Female pelvic floor dysfunction (PFD) is characterized by stress urinary incontinence (stress urinary incontinence, SUI), pelvic organ prolapse (pelvic organ prolapse, POP) and chronic pelvic pain (chronic pelvic pain, C Propylene) etc. as a kind of gynecological disease of main symptom. A large number of studies have shown that pelvic floor mesh is an important pelvic floor tissue replacement, which can replace the weak and damaged pelvic floor fascia tissue. Compared with traditional hysterectomy, mesh has been gradually proven to improve the safety of surgery and the quality of life of patients [ACHTARI C, HISCOCK R, O'REILLY B A, et al. Risk factors for mesh erosion after transvaginal surgery using polypropylene(A...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more