Recycling method of acid ammonium salt precipitating vanadium waste water

An acid ammonium salt precipitation vanadium and wastewater technology, applied in metallurgical wastewater treatment, chemical instruments and methods, flocculation/sedimentation water/sewage treatment, etc., can solve the problems of underutilization of acid and ammonia and waste of resources.

Inactive Publication Date: 2016-04-27
PANGANG GRP PANZHIHUA STEEL & VANADIUM
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with this method is that the acid and ammonia in the wastewater are not fully utilized, resulting in a waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Take 1000mL of vanadium precipitation wastewater, in which Na + Content 20.65g / L, SO 4 2- Content 83.74g / L, NH 4 + Content 9.58g / L, pH=2.5, add 670mL of sodium polyvanadate solution with a vanadium concentration of 60g / L, mix well; adjust the pH of the solution to 5.2 with 30% sulfuric acid solution, stir the reaction for 1h at room temperature, and let stand for 1h; filter , get 82.0g of vanadium raw material, 1560ml of waste water, the main component of waste water is Na + Content 31.85g / L, SO 42- Content 65.23g / L, NH 4 + Content 2.46g / L, pH=5.2.

Embodiment 2

[0041] Take 1000mL of vanadium precipitation wastewater, Na + Content 21.38g / L, SO 4 2- Content 85.67g / L, NH 4 + Content 9.03g / L, pH=2.5, add 1000mL of sodium polyvanadate solution with a vanadium concentration of 30g / L, mix well; add 25% sulfuric acid solution to adjust the solution pH=5.4, at room temperature, stir for 1h, let stand for 3h ; Filtrate to obtain vanadium raw material 60.05g, waste water 1920ml, the main component of waste water is Na + Content 27.5g / L, SO 4 2- Content 58.46g / L, NH 4 + Content 3.02g / L.

Embodiment 3

[0043] Take 1000mL of vanadium precipitation wastewater, Na + Content 22.37g / L, SO 4 2- Content 87.64g / L, NH 4 + Content 8.87g / L, pH=2.5, add 750mL of sodium polyvanadate solution with a vanadium concentration of 47g / L, and mix well; add 30% sulfuric acid solution to adjust the pH of the solution to 5.5, stir and react for 1h at room temperature, and let it stand for 2h; Filtrate, obtain vanadium raw material 71.59g, waste water 1650ml, the main component of waste water is Na + Content 30.61g / L, SO 4 2- Content 62.62g / L, NH 4 + The content is about 2.45g / L.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of chemical engineering and metallurgy, and particularly relates to a recycling method of acid ammonium salt precipitating vanadium waste water. The recycling method comprises the following steps that a, the acid ammonium salt precipitating vanadium waste water is added to and is uniformly mixed with a polyoxovanadium sodium solution to form a mixed solution; b, the pH value of the mixed solution is adjusted to 5-6, the mixed solution is subjected to standing crystallization and filtration, a vanadium-containing raw material and new waste water are obtained; c, a reducing agent is added to the new waste water for reduction, after the reduction, alkali is added for neutralization, pressure filtration is carried out, and pressure filtration water and vanadium and chromium residues are obtained; and d, the pressure filtration water is subjected to evaporation and concentration, crystals of sodium salt and ammonium salt and condensation water are obtained. According to the recycling method of the acid ammonium salt precipitating vanadium waste water, after alkaline polyoxovanadium solution is mixed with the acid ammonium salt precipitating vanadium waste water, the pH value is adjusted to 5-6, the solution is crystallized sufficiently, and parts of ammonium and acid in the waste water can be recycled.

Description

technical field [0001] The invention belongs to the fields of chemical industry and metallurgy, and relates to a method for reusing waste water, in particular to a method for reusing acid ammonium salt vanadium precipitation waste water. Background technique [0002] Except for the Tula plant in Russia, no matter what vanadium resources are used, the rest of the vanadium plants use sodium oxide roasting-water immersion-acid ammonium salt precipitation vanadium-vanadium oxide (V 2 o 5 and V 2 o 3 ) - Vanadium alloy process to produce vanadium products. Obviously, vanadium oxide is an essential intermediate process for the production of vanadium products, and every ton of V 2 o 5 or V 2 o 3 Discharge about 50~150m 3 The vanadium precipitation wastewater contains not only vanadium and chromium, but also a large amount of Na + , SO 4 2- , NH 4 + Plasma and a small amount of suspended solids. [0003] In the prior art, for example, the wastewater treatment process o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B7/00C22B34/22C02F9/10C02F103/16C02F101/16C02F101/10
CPCC02F1/001C02F1/04C02F1/52C02F1/66C02F1/70C02F9/00C02F2001/5218C02F2101/101C02F2101/16C02F2103/16C22B7/006C22B34/22Y02P10/20
Inventor 潘少彦李千文黄锦宁吴封张毅许娟娟王彬彬
Owner PANGANG GRP PANZHIHUA STEEL & VANADIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com