Cold-rolled aluminum work roll with good grinding properties and manufacturing method thereof
A manufacturing method and technology of work rolls, applied in the field of roll manufacturing, can solve the problems of labor intensity, production efficiency, grinding cost, production organization, failure to meet surface quality requirements, low roughness value, etc., to solve the problem of low grinding efficiency, The effect of promoting the amount of carbide dissolution and reducing the consumption of grinding amount
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] The manufacturing method of the cold-rolled aluminum work roll with good grindability of the present embodiment comprises the following process steps:
[0045] 1) According to the chemical composition and weight percentage of the work roll material, the steel material is prepared, and the roll blank is obtained according to a certain production process.
[0046] Specifically, the steel raw materials are smelted in an electric arc furnace and a refining furnace, and molded into electrode ingots. The chemical composition and weight percentage of the final electrode ingot are tested. After passing the test, it is forged into a forging billet. The forging billet is subjected to post-forging heat treatment, and finally turned to obtain a roll billet.
[0047] The test results of the main chemical components in the material of the cold-rolled aluminum work roll of this embodiment are shown in the column of Example 1 in Table 1, and the rest are Fe and unavoidable impurities. ...
Embodiment 2
[0058] The cold-rolled aluminum work roll with good grindability of the present embodiment, the weight percentage of the main chemical components in its material is tested, and the content of the main chemical components is shown in column 2 of Example 1 in Table 1, and the rest For Fe and unavoidable impurities.
[0059] The manufacturing method of the cold-rolled aluminum work roll with good grindability of the present embodiment, its process step is similar to that of embodiment 1, and the specific heat treatment parameters different from embodiment 1 are shown in column 2 of embodiment 2 in table 2, specifically Grinding treatment parameters are the same as in Example 1.
[0060] The roll surface hardness of the cold-rolled aluminum work roll prepared in this embodiment is 96-98 HSD, and the roll surface roughness obtained after grinding the cold-rolled roll is Ra0.581-0.615 μm.
Embodiment 3
[0062] The cold-rolled aluminum work roll with good grindability of the present embodiment, the weight percentage of the main chemical components in its material is tested, and the content of the main chemical components is shown in column 3 of Example 1 in Table 1, and the rest For Fe and unavoidable impurities.
[0063] The manufacturing method of the cold-rolled aluminum work roll with good grindability of the present embodiment, its processing steps are similar to that of embodiment 1, and the specific heat treatment parameters different from embodiment 1 are shown in column 3 of embodiment in table 2, specifically Grinding treatment parameters are the same as in Example 1.
[0064] The roll surface hardness of the cold-rolled aluminum work roll prepared in this embodiment is 97-99HSD, and the roll surface roughness obtained after grinding the cold-rolled roll is Ra0.599-0.633 μm.
PUM
Property | Measurement | Unit |
---|---|---|
width | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com