A kind of photocurable prepolymer adhesive and preparation method thereof

A prepolymer, light-curing technology, used in adhesives, polyurea/polyurethane adhesives, adhesive types, etc., can solve the problems of limiting the application of thiol/ene light-curing system and short storage period of finished products. Improved chemical stability, longer storage time, improved curing effect

Inactive Publication Date: 2018-02-02
TONSAN ADHESIVES INC
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thiol / ene system also has some disadvantages, such as less prepolymers suitable for the system and short shelf life of the finished product. These limitations limit the application of the thiol / ene photocuring system.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of photocurable prepolymer adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Synthesis of prepolymer PreP-1: 200 grams of polyester diol with a molecular weight (Mn) of 2000 and a hydroxyl value of about 56 was vacuum dehydrated at 120°C for 1 hour, and the dehydrated polyether diol, 44.46 Put 1,6-gram 1,6-diisocyanate together into the reactor, add 0.1 gram of dibutyltin dilaurate, react at 78°C for 4 hours, add 23.2 grams of 4-hydroxybutyl vinyl ether, 0.1 gram of hydroquinone to make As a polymerization inhibitor, continue to react at 78°C for 2 hours, cool to 45°C and discharge. It is called PreP-1.

Embodiment 2

[0046] Synthesis of prepolymer PreP-2: get 300 grams of polyether diol with a molecular weight (Mn) of 3000 and a hydroxyl value of about 37, and add C 12 -C 16 The proportion of alkyl alkoxy sulfate 10g will polyether glycol and C 12 -C 16 The alkyl alkoxy sulfate is fully mixed and reacted, the reaction temperature is 70°C, and the reaction time is 2 hours, the pretreatment process is completed. The modified polyether diol was vacuum dehydrated at 130°C for 2 hours, the dehydrated polyether diol and 45 grams of methylcyclohexyl diisocyanate were put into the reaction kettle together, and 0.2 grams of dilauric acid was added Dibutyltin, react at 80°C for 3 hours, add 26 grams of 4-hydroxybutyl vinyl ether, 0.1 gram of hydroquinone as a polymerization inhibitor, continue to react at 78°C for 2 hours, cool to 45°C and discharge Yes, call it PreP-2.

Embodiment 3

[0048] Synthesis of prepolymer PreP-3: 200 grams of polyether diol with a molecular weight (Mn) of 2000 and a hydroxyl value of about 56 was vacuum dehydrated at 120°C for 1 hour, and the dehydrated polyether diol, 44.46 Put 1 gram of isophorone diisocyanate into the reactor together, add 0.1 gram of dibutyltin dilaurate, react at 78°C for 3 hours, add 26 grams of hydroxyethyl methacrylate, and 0.1 gram of hydroquinone as a polymerization inhibitor agent, continue to react at 78°C for 2 hours, cool to 45°C and discharge, which is called PreP-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a photocuring prepolymer tackiness agent. The photocuring prepolymer tackiness agent is prepared from, by weight, 80%-98% of photocuring prepolymer, 2%-10% of modified polymercaptan and 0.005%-1% of photoinitiator. The photocuring prepolymer is prepared from, by weight, 70%-85% of polymer polyhydric alcohol, 10%-25% of diisocyanate, 1%-10% of vinyl ether containing hydroxyl and 0.01%-1% of addition agent. According to the photocuring prepolymer tackiness agent, the polyhydric alcohol in the prepolymer is pretreated, and the polymercaptan is modified, so that under the conditions that the content of the initiator is low and the amount of ultraviolet light energy needed by surface curing is small, it is guaranteed that the curing thickness is still kept large under the low ultraviolet light energy, the storage time is long, the production cost is greatly lowered, and application in actual production can be better facilitated.

Description

technical field [0001] The invention relates to a photocurable adhesive, in particular to a prepolymer containing vinyl ether and a photocurable adhesive composed of mercaptan. Background technique [0002] Photocurable adhesives, also known as UV adhesives, are basically composed of: (1) prepolymers; (2) reactive monomers; (3) photoinitiators; (4) additives. The basic principle of light-curing adhesives is: the main glue is irradiated with ultraviolet light for tens of seconds, and the photoinitiator decomposes to generate free radicals to polymerize and cure, and make it change from a linear structure to a network structure. [0003] Photocurable prepolymers, also known as oligomers, are low-molecular polymers containing unsaturated functional groups, mostly acrylate-terminated oligomers. Prepolymers are the main body of photocurable resins, and their properties basically determine the curing process. The main properties of the material. Photocurable adhesives prepared f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/67C08G18/50C08G18/48C08G18/42C09J175/14C09J11/06
CPCC08G18/4018C08G18/4825C08G18/5072C08G18/6715C08G18/672C08K5/37C09J11/06C09J175/14C08G18/40C08G18/50C08G18/48
Inventor 何利军胡建琪李守平黄金亮侯峰赵应波
Owner TONSAN ADHESIVES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com