Fire-proof coating used for die casting

A technology for refractory coatings and molds, applied in coatings, casting molding equipment, casting molds, etc., to achieve good wettability and adhesion, good coating and hanging properties, and easy drying

Inactive Publication Date: 2016-02-17
广西博白县三田机械制造有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under the action of negative pressure, liquid metal can easily penetrate into the gap between dry sand and form mechanical sticky sand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fire-proof coating used for die casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A refractory coating for mold casting, which is composed of the following raw materials: bauxite 4kg, quartz powder 3kg, corundum 1kg, diatomite 1kg, talcum powder 1kg, cryolite 0.1kg, CMC 0.8kg, polyethylene Alcohol 0.3kg, water glass 0.3kg, sodium phosphate 0.1kg.

[0030] The preparation method is that water is used as a carrier, and all raw materials are mixed evenly in proportion.

Embodiment 2

[0032] A refractory coating for mold casting, which is composed of the following raw materials: bauxite 6kg, quartz powder 1kg, corundum 0.5kg, diatomite 0.5kg, talcum powder 0.5kg, cryolite 0.3kg, CMC 0.3kg , polyvinyl alcohol 0.1kg, water glass 0.8kg, sodium phosphate 0.3kg.

[0033] The preparation method is that water is used as a carrier, and all raw materials are mixed evenly in proportion.

Embodiment 3

[0035] A refractory coating for mold casting is composed of the following raw materials: 4.5kg of bauxite, 2.5kg of quartz powder, 0.8kg of corundum, 0.6kg of diatomaceous earth, 0.8kg of talcum powder, 0.1kg of cryolite, CMC0 .4kg, polyvinyl alcohol 0.1kg, water glass 0.6kg, sodium phosphate 0.1kg, fatty alcohol polyoxyethylene ether 0.02kg.

[0036] The preparation method is that water is used as a carrier, and all raw materials are mixed evenly in proportion.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fire-proof coating used for die casting. The fire-proof coating is prepared from bauxite, quartz powder, corundum powder, kieselguhr, talcum powder, cryolite, CMC, polyvinyl alcohol, water glass and sodium phosphate. The fire-proof coating is suitable for evaporative pattern casting, is high in breathability, and has the beneficial effects of having good wettability and adhesivity and being resistant to high temperature, good in coating performance, easy to dry, and the like.

Description

technical field [0001] The invention relates to the field of casting, in particular to a refractory coating for mold casting. Background technique [0002] Mold casting is a part of casting tooling, and it is the necessary equipment to shape the casting and obtain the required casting. Lost foam casting, also known as solid casting, is to bond and combine paraffin or foam models similar in size and shape to castings to form a model cluster. After brushing with refractory paint and drying, it is buried in dry sand for vibration modeling, and poured under negative pressure. , the model is vaporized, the liquid metal occupies the position of the model, solidified and cooled to form a new casting method of castings. [0003] Because after foam molding, the surrounding area is covered with molding sand. On the one hand, since the molding sand is approximately spherical, there is actually point contact between the molding sand and the surface of the model, and there are many tin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00B22C9/04
CPCB22C3/00B22C9/04
Inventor 陈杰陈智强凌丽英陈勇
Owner 广西博白县三田机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com