600mpa grade high yield strength ratio high plasticity cold-rolled steel plate and its manufacturing method

A high yield ratio, cold-rolled steel plate technology, applied in the field of cold-rolled high-strength thin plates for automobiles, can solve the problems of no comparability, no practical operability, and difficulty in annealing lines

Active Publication Date: 2017-04-26
ANGANG STEEL CO LTD
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to obtain such a steel plate with a strength greater than 600MPa and a yield ratio greater than 0.80, during the annealing process, the steel plate is heated to 780-850°C and then cooled to below 200°C through two-stage rapid cooling. Cooling is easy to control, and the second stage is rapidly cooled from a lower temperature of 400-500°C to below 200°C, which is very difficult for an annealing line that relies on gas-vapor cooling, and is not practical.
[0004] CN101558178A provides a kind of cold-rolled steel plate with high yield strength ratio and excellent weather resistance, the alloy elements such as Nb, Ni, Co, Cr, Cu and B have been added in the steel composition, and the steel plate after cold rolling is heated at 500 ℃ Continuous annealing within the temperature range to the A1 transition point, the yield ratio of the steel plate is greater than 0.85, and the tensile strength is greater than 800MPa. It is mainly used in construction, rail vehicles and containers, and products with high yield ratio cold-rolled high-strength steel plates for automobiles Not comparable to the annealing process
However, this annealing process requires a higher cooling rate in the overaging section of the continuous annealing furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 600mpa grade high yield strength ratio high plasticity cold-rolled steel plate and its manufacturing method
  • 600mpa grade high yield strength ratio high plasticity cold-rolled steel plate and its manufacturing method
  • 600mpa grade high yield strength ratio high plasticity cold-rolled steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention is further illustrated by some examples below. The composition of the steel in the example is shown in Table 1, the hot rolling process parameters are shown in Table 2, the continuous annealing process parameters are shown in Table 3, and the mechanical properties of the continuous annealed steel plate are shown in Table 4. The hot-rolled sheet microstructure of embodiment 1 sees figure 1 , the microstructure of cold-rolled annealed sheet see figure 2 , see the precipitates in the hot-rolled fire plate image 3 , cold-rolled annealed sheet transmission electron microscope photos see Figure 4 .

[0034] Chemical composition (mass fraction) % of table 1 embodiment steel

[0035] Example C Si mn P S Al N Nb Ti Nb+Ti 1 0.06 0.02 1.90 0.010 0.007 0.10 0.0050 0.020 0.025 0.045 2 0.08 0.09 1.72 0.009 0.010 0.02 0.0030 0.025 0.035 0.060 3 0.09 0.05 1.80 0.007 0.006 0.05 0.0020 0.030 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A disclosed 600 MPa grade high-yield-ratio high-plasticity cold-rolled steel plate is characterized by comprising the following compositions in percent by mass: 0.06%-0.12% of C, 0.02-0.10% of Si, 1.40%-2.00% of Mn, 0.015% or less of P, 0.010% or less of S, 0.02%-0.10% of Al, 0.0050% or less of N, 0.015-0.045% of Nb, 0.020-0.055% of Ti, at the same time 0.035%<= Nb+Ti<= 0.100%, and the ferrite balance is Fe and other some unavoidable impurities.

Description

technical field [0001] The invention belongs to the technical field of cold-rolled high-strength thin plates for automobiles, and provides a 600MPa grade high-yield ratio high-plasticity cold-rolled steel plate and a manufacturing method thereof. Background technique [0002] Low energy consumption, weight reduction and high safety have become the development trend of modern and future automobiles. In order to adapt to this development trend of the automobile industry, automobile manufacturers, steel companies and research institutes are actively working on the "lightweight" design and development of automobile bodies. Research and development of high-strength steel for automobiles. At present, the developed cold-rolled high-strength steels for automobiles, such as dual-phase (DP) steels and phase transformation-induced plasticity (TRIP) steels with strengths ranging from 590MPa to 980MPa, have been industrialized and mass-produced, and are used in automobile skeleton member...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C21D8/02
Inventor 王科强刘仁东王旭郭金宇徐荣杰孙成钱李新黄大鹏林利徐鑫
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products