High-transparency, high-hardness and anti-yellowing epoxy resin AB glue for surfaces of environment-friendly building materials

A technology for changing the surface of epoxy resin and building materials, applied in the direction of epoxy resin glue, adhesive, polymer adhesive additives, etc., can solve the problems of poor weather resistance, poor UV resistance, cracking of the adhesive layer, etc., and achieve UV resistance Good, anti-yellowing time, high adhesion effect

Active Publication Date: 2016-01-20
SHENCAI TECH SHENZHEN CO LTD
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the effect of transparent epoxy AB glue applied on the surface of renewable resource ceramic boards, artificial marble, and artistic ceramic boards is not good. The main reason is that the transparency is not enough, and the Shore hardness cannot reach 85-90D, and Poor UV resistance
Even if the hardness of some products can reach Shore hardness 85D, there will be insufficient adhesion between the cured epoxy AB glue and the substrate, and the glue layer will crack
In addition, the yellowing resistance in the indoor environment cannot reach 2 years; in the outdoor environment, the weather resistance is poor, the UV resistance is not good, and the yellowing resistance cannot reach 1 year.
The transparent glue of the surface coating / coating of the existing technology cannot meet the aesthetic and lightweight development needs of future energy-saving and environmentally friendly building materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-transparency, high-hardness and anti-yellowing epoxy resin AB glue for surfaces of environment-friendly building materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A high-transparency, high-hardness, anti-yellowing epoxy resin AB glue for the surface of environmentally friendly building materials, which consists of components A and B, and the components contained in component A and their mass parts are:

[0024] 80 parts of bisphenol A epoxy resin, 20 parts of nano-scale silica / epoxy polymer toughening agent, 0.05 part of wetting and anti-cratering additive, 0.2 part of nanometer anti-UV blocker, 0.5 part of silane coupling agent part; wherein, the epoxy equivalent of the bisphenol A epoxy resin is 184-190g / eq; the epoxy equivalent of the epoxy polymer in the nano-scale silica / epoxy polymer toughening agent is 220 -230g / eq, the particle size of the nano-scale silicon dioxide is 10-50nm, the mass percentage of the nano-scale silicon dioxide is not more than 45%; the wetting and anti-cratering additive is organic silicon The twin-structure surfactant, the nano anti-UV blocker is a transparent liquid with a viscosity of 10-15CPS.

...

Embodiment 2

[0033] A high-transparency, high-hardness, anti-yellowing epoxy resin AB glue for the surface of environmentally friendly building materials, which consists of components A and B, and the components contained in component A and their mass parts are:

[0034] 82.5 parts of bisphenol A epoxy resin, 17.5 parts of nano-scale silica / epoxy polymer toughening agent, 0.08 part of wetting and anti-cratering additive, 0.35 part of nano-scale anti-UV blocker, 0.6 part of silane coupling agent part; wherein, the epoxy equivalent of the bisphenol A epoxy resin is 184-190g / eq; the epoxy equivalent of the epoxy polymer in the nano-scale silica / epoxy polymer toughening agent is 220 -230g / eq, the particle size of the nano-scale silicon dioxide is 10-50nm, the mass percentage of the nano-scale silicon dioxide is not more than 45%; the wetting and anti-cratering additive is organic silicon The twin-structure surfactant, the nano anti-UV blocker is a transparent liquid with a viscosity of 10-15CP...

Embodiment 3

[0043] A high-transparency, high-hardness, anti-yellowing epoxy resin AB glue for the surface of environmentally friendly building materials, which consists of components A and B, and the components contained in component A and their mass parts are:

[0044]85 parts of bisphenol A epoxy resin, 15 parts of nano-scale silica / epoxy polymer toughening agent, 0.12 part of wetting and anti-cratering additive, 0.5 part of nano-anti-UV blocker, 0.7 part of silane coupling agent part; wherein, the epoxy equivalent of the bisphenol A epoxy resin is 184-190g / eq; the epoxy equivalent of the epoxy polymer in the nano-scale silica / epoxy polymer toughening agent is 220 -230g / eq, the particle size of the nano-scale silicon dioxide is 10-50nm, the mass percentage of the nano-scale silicon dioxide is not more than 45%; the wetting and anti-cratering additive is organic silicon The twin-structure surfactant, the nano anti-UV blocker is a transparent liquid with a viscosity of 10-15CPS.

[0045]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
epoxy equivalentaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-transparency, high-hardness and anti-yellowing epoxy resin AB glue for the surfaces of environment-friendly building materials, which consists of a component A and a component B; the component A consists of the following ingredients in parts by weight: 80 to 90 parts of bisphenol A epoxy resin, 10 to 20 parts of nanoscale silicon dioxide / epoxy polymer toughener, 0.05 to 0.2 parts of wetting and anti-cratering additive, 0.2 to 0.8 parts of anti-ultraviolet barrier and 0.5 to 1.0 part of coupling agent; the component B consists of the following ingredients in parts by weight: 95 to 97 parts of polyether amine, 3 to 5 parts of alicyclic amine and 0.2 to 0.6 parts of coupling agent; the mass ratio of the component A to the component B is (2 to 2.5):1. The epoxy resin AB glue adopting the technical solution of the invention has high transparency and high Shore hardness, moreover, yellowing resistance reaches more than 3 years, and the epoxy resin AB glue can be applied in surface coating or coating for renewable resource ceramic plates, artificial marble, artistic ceramic plates and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-transparency, high-hardness and anti-yellowing epoxy resin AB glue for the surface of environmentally friendly building materials. Background technique [0002] At present, the effect of transparent epoxy AB glue applied on the surface of renewable resource ceramic boards, artificial marble, and artistic ceramic boards is not good. The main reason is that the transparency is not enough, and the Shore hardness cannot reach 85-90D, and Poor UV resistance. Even if the hardness of some products can reach the Shore hardness of 85D, there will be insufficient adhesion between the cured epoxy AB glue and the substrate, and the glue layer will crack. In addition, the yellowing resistance in the indoor environment cannot reach 2 years; in the outdoor environment, the weather resistance is poor, the UV resistance is not good, and the yellowing resistance canno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J11/08C09J11/04
Inventor 秦建
Owner SHENCAI TECH SHENZHEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com