Cracked glaze and making process thereof

A cracked glaze and glaze technology, applied in the field of cracked glaze and production technology, can solve the problems of single glaze effect, high production cost and high firing temperature, achieve stable glaze effect, reduce production cost and low firing temperature Effect

Inactive Publication Date: 2016-01-06
DEHUA HENGHAN ARTS
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Crackle glaze makes the corresponding products favored by many consumers with its unique crackle effect, but the glaze effect of the existing crackle glaze is unstable, and the glaze effect is single, the variety is monotonous, and it cannot cater to the needs of consumers with different personalities; in addition, the current Most of the cracked glazes have long firing time and high firing temperature, which consume more fuel for production, relatively low production efficiency and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Crackle glaze is made of the following raw materials according to mass percentage: 10% albite feldspar, 11% kaolin, 1% quartz, 7% zinc oxide, 8% barium carbonate, and 63% frit;

[0016] Described frit is made up of following raw material by mass percentage: quartz 8%, red lead 45%, feldspar 10%, dolomite 12%, barium carbonate 25%, wherein feldspar is made of potassium feldspar and albite by 2~ 3:1 mass ratio composition.

[0017] The production process of crackle glaze, the specific production steps are as follows:

[0018] (1) Preparation of frit: separately pulverize quartz, red lead, potassium feldspar, albite, dolomite and barium carbonate, and mix them uniformly in proportion to smelt to prepare frit;

[0019] (2) Preparation of glaze: crush each raw material and frit separately, mix them uniformly in proportion to obtain a mixture, then add water according to the mass ratio of mixture:water 1:0.6, stir for 3 hours, ball mill for 7 hours, pass 400 ~600-mesh sieve...

Embodiment 2

[0023] Crackle glaze is made of the following raw materials according to mass percentage: albite 12%, kaolin 10%, quartz 2%, zinc oxide 6%, barium carbonate 10%, frit 60%;

[0024] The frit is composed of the following raw materials by mass percentage: 10% quartz, 40% red lead, 15% feldspar, 10% dolomite, and 25% barium carbonate. The feldspar is composed of potassium feldspar and albite at a ratio of 2.5:1 mass ratio composition.

[0025] The manufacturing process of the above-mentioned crackle glaze, the specific manufacturing steps are as follows:

[0026] (1) Preparation of frit: separately pulverize quartz, red lead, potassium feldspar, albite, dolomite and barium carbonate, and mix them uniformly in proportion to smelt to prepare frit;

[0027] (2) Preparation of glaze: crush each raw material and frit separately, mix uniformly in proportion to obtain a mixture, then add water according to the mass ratio of mixture:water 1:0.65, stir for 3 hours, ball mill for 7 hours, ...

Embodiment 3

[0031] The crackle glaze is made of the following raw materials according to the mass percentage: 14% albite feldspar, 10% kaolin, 3% quartz, 5% zinc oxide, 12% barium carbonate, and 56% frit;

[0032] The frit is composed of the following raw materials by mass percentage: 12% quartz, 40% red lead, 20% feldspar, 8% dolomite, and 30% barium carbonate, wherein the feldspar is potassium feldspar and albite feldspar at a ratio of 3:1 mass ratio composition.

[0033] The manufacturing process of the above-mentioned crackle glaze, the specific manufacturing steps are as follows:

[0034] (1) Preparation of frit: separately pulverize quartz, red lead, potassium feldspar, albite, dolomite and barium carbonate, and mix them uniformly in proportion to smelt to prepare frit;

[0035] (2) Preparation of glaze: crush each raw material and frit separately, mix uniformly in proportion to obtain a mixture, then add water according to the mass ratio of mixture:water 1:0.7, stir for 3 hours, b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cracked glaze and a making process thereof. The cracked glaze is composed of albite, kaolin, quartz, zinc oxide, barium carbonate and frits, wherein the frits are composed of quartz, red lead, feldspar, dolomite and barium carbonate, and the feldspar is composed of potassium feldspar and albite according to the mass ratio. The making process comprises the steps of smashing quartz, red lead, potassium feldspar, albite, dolomite and barium carbonate, uniformly mixing, and smelting to prepare the frits; and respectively smashing all the raw materials and the frits, uniformly mixing according to a certain ratio, then, adding water to stir, sieving by using a mesh screen after ball milling, coating the prepared glaze on the surface of a ceramic blank, firing in a roasting kiln, and cooling after taking the glaze out of the kiln. The cracked glaze disclosed by the invention is simple in component and reasonable in formula, the glaze surface effect of the prepared cracked glaze is stable, glaze surfaces with different effects can be made through changing the contents of the components, and the crack is good in effect and more uniform and attractive; and the making process is short in firing time and low in firing temperature, so that the energy consumption is reduced, the energy is saved, the environment is protected, and the production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of glaze preparation, in particular to a cracked glaze and a manufacturing process. Background technique [0002] Crackle glazes are favored by many consumers for their unique crackle effects. However, the glaze effect of existing crackle glazes is unstable, and the glaze effect is single, and the variety is monotonous, which cannot meet the needs of consumers with different personalities; Most of the cracked glazes have long firing time and high firing temperature, which consume more fuel for production, relatively low production efficiency and high production cost. Contents of the invention [0003] The object of the present invention is to provide a cracked glaze and its manufacturing process to solve the problems raised in the above-mentioned background technology. [0004] To achieve the above object, the present invention provides the following technical solutions: [0005] A crackle glaze, which i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 林锦明
Owner DEHUA HENGHAN ARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products