Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High-tenacity and shock-proof bactericidal diatom ooze coating

A diatom mud coating and impact-resistant technology, applied in the coating field, can solve problems such as inability to paint large areas, negative impact on the impact resistance of diatom mud coatings, and insufficient toughness, so as to enhance the body's immunity, improve the sterilization effect, and mechanically good strength effect

Inactive Publication Date: 2015-12-16
TIANCHANG YINHU PAINT
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] When diatom mud is made into coatings, it often has insufficient toughness and cannot be painted on a large area. At the same time, because auxiliary materials are often added during production and processing to expand the volume and reduce costs, this also has a negative effect on the impact resistance of diatom mud coatings. influences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of high toughness anti-impact sterilization diatom mud coating that the present invention proposes, its raw material comprises by weight: 50 parts of natural diatomite, 14 parts of negative ion powder, 12 parts of polylactic acid chelated silver ion bactericide, light calcium carbonate 12 parts, 12 parts of bentonite, 5 parts of talc, 2.2 parts of sodium oleate, 1.2 parts of film-forming aids, 1.8 parts of emulsifiers, 3 parts of pigments, 1.9 parts of wetting agents, 1.1 parts of leveling agents, rheological additives 1.7 parts, 1.6 parts of defoamer, 65 parts of deionized water;

[0017] The preparation method of the polylactic acid chelated silver ion bactericide is as follows: 130 parts by weight of dehydrated lactic acid are subjected to temperature rise and pressure reaction, and the reaction pressure is 1.8×10 4 Pa, the reaction temperature is 150°C, the reaction time is 2h, then put in 0.05 parts of tin chloride, 0.04 parts of toluenesulfonic acid monohyd...

Embodiment 2

[0019] A kind of high toughness anti-impact sterilization diatom mud coating that the present invention proposes, its raw material comprises by weight: 40 parts of natural diatomite, 16 parts of negative ion powder, 8 parts of polylactic acid chelated silver ion bactericide, 15 parts of light calcium carbonate 9 parts of bentonite, 8 parts of talc, 1.8 parts of sodium sulfate, 1.5 parts of film-forming aids, 1.5 parts of emulsifiers, 6 parts of pigments, 1.6 parts of wetting agents, 1.5 parts of leveling agents, and 1.4 parts of rheological additives part, 1.9 parts of defoamer, 60 parts of deionized water;

[0020] The preparation method of the polylactic acid chelated silver ion bactericide is as follows: 150 parts by weight of dehydrated lactic acid are subjected to temperature rise and pressure reaction, and the reaction pressure is 1.5×10 4 Pa, the reaction temperature is 155°C, the reaction time is 1.5h, then put in 0.08 parts of tin chloride, 0.01 parts of toluenesulfon...

Embodiment 3

[0022] A kind of high-toughness anti-impact sterilization diatom mud coating that the present invention proposes, its raw material comprises by weight: 46 parts of natural diatomites, 14.5 parts of negative ion powders, 10 parts of polylactic acid chelated silver ion bactericides, light calcium carbonate 13 parts, 11 parts of bentonite, 6 parts of talc, 2.1 parts of sodium sulfonate, 1.3 parts of film-forming aid, 1.7 parts of emulsifier, 4 parts of pigment, 1.8 parts of wetting agent, 1.2 parts of leveling agent, rheology additive 1.6 parts, 1.7 parts of defoamer, 63 parts of deionized water;

[0023] The preparation method of the polylactic acid chelated silver ion bactericide is as follows: 140 parts by weight of dehydrated lactic acid are subjected to temperature rise and pressure reaction, and the reaction pressure is 1.7×10 4Pa, the reaction temperature is 152°C, the reaction time is 1.8h, and then 0.06 parts of tin chloride, 0.03 parts of toluenesulfonic acid monohydrat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-tenacity and shock-proof bactericidal diatom ooze coating, which comprises the following raw materials in parts by weight: 40 to 50 parts of nature diatomite, 14 to 16 parts of negative ion powder, 8 to 12 parts of polylactic acid chelated silver ion bactericide, 12 to 15 parts of light calcium carbonate, 9 to 12 parts of bentonite, 5 to 8 parts of talcum powder, 1.8 to 2.2 parts of dispersing agent, 1.2 to 1.5 parts of coalescing agent, 1.5 to 1.8 parts of emulsifier, 3 to 6 parts of pigment, 1.6 to 1.9 parts of wetting agent, 1.1 to 1.5 parts of smoothing agent, 1.4 to 1.7 parts of smoothing assistant, 1.6 to 1.9 parts of defoamer and 60 to 65 parts of deionized water. The high-tenacity and shock-proof bactericidal diatom ooze coating disclosed by the invention has good bactericidal performance, is environmental friendly and durable, and is good indoor coating.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-toughness, impact-resistant and sterilized diatom mud coating. Background technique [0002] Diatom mud has the functions of adjusting humidity, releasing negative oxygen ions, fire retardant, sterilization and deodorization, etc. It is an excellent indoor coating. China is the country with the largest content and export of diatom mud in the world. The composition of diatom mud is A regular and neatly arranged circular or needle-shaped micron-scale porous material, with a porosity of up to 90%, and thousands of times more micropores per unit area than charcoal, with extremely strong physical adsorption properties and ion exchange performance. [0003] Negative ion powder is a kind of composite mineral that is artificially synthesized or proportioned by human beings using the principle of negative ions produced in nature. The negative ions released by negative ion powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/14C09D7/12
Inventor 戴宇钧汪鹏程孙巨福祝秀凤
Owner TIANCHANG YINHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com