Ganoderma lucidum spore powder wall breaking method
A technology of Ganoderma lucidum spore powder and spore powder, which is applied in the fields of pharmaceutical formulation, food science, plant raw materials, etc., can solve the problems of small wall-breaking effect, complicated process, and high harmful residues, so as to improve hygienic and safety properties, improve nutritional value, The effect of improving the wall breaking rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] A method for breaking the wall of ganoderma lucidum spore powder, according to the following steps:
[0034] (1) The ganoderma lucidum spore powder is roughly broken into a 80-mesh sieve with a wall breaking machine;
[0035] (2) Mix the spore powder and water pretreated in step (1) into a dual-frequency ultrasonic wave for processing, the weight ratio of spore powder and water is 1:20, the processing condition is 37kHz / 22kHz alternating ultrasonic, and the ultrasonic alternate working time 3s, electric power 180W, 35°C ultrasonic treatment for 35min;
[0036] (3) The spore powder after the ultrasonic treatment in step (2) was vacuum freeze-dried at -20°C for 4 hours; the spore powder was dried to a moisture content of <6%;
[0037] (4) The spore powder after freeze-drying is subjected to wall-breaking treatment in a high-frequency oscillating wall crusher. The working system of the high-frequency oscillating wall crusher is intermittent, charging volume: 100L, feeding...
Embodiment 2
[0040] A method for breaking the wall of ganoderma lucidum spore powder, according to the following steps:
[0041] (1) The ganoderma lucidum spore powder is roughly broken into a 80-mesh sieve with a wall breaking machine;
[0042] (2) Mix the spore powder and water pretreated in step (1) into a dual-frequency ultrasonic wave for processing, the weight ratio of spore powder and water is 1:22, the processing condition is 40kHz / 25kHz alternating ultrasonic, and the ultrasonic alternate working time 3s, electric power 200W, ultrasonic treatment at 40°C for 30min;
[0043] (3) The spore powder after the ultrasonic treatment in step (2) was vacuum freeze-dried at -18°C for 4.5 hours; the spore powder was dried to a moisture content of <6%;
[0044] (4) The spore powder after freeze-drying is subjected to wall-breaking treatment in a high-frequency oscillating wall crusher. The working system of the high-frequency oscillating wall crusher is intermittent. : 5mm, crushing method: ...
Embodiment 3
[0047] A method for breaking the wall of ganoderma lucidum spore powder, according to the following steps:
[0048] (1) The ganoderma lucidum spore powder is roughly broken into a 80-mesh sieve with a wall breaking machine;
[0049](2) Mix the spore powder and water pretreated in step (1) into a dual-frequency ultrasonic wave for processing, the weight ratio of spore powder and water is 1:20, the processing condition is 40kHz / 25kHz alternating ultrasonic, and the ultrasonic alternate working time 3s, electric power 200W, ultrasonic treatment at 40°C for 30min;
[0050] (3) The spore powder after the ultrasonic treatment in step (2) was vacuum freeze-dried at -14°C for 4.5 hours; the spore powder was dried to a moisture content of <6%;
[0051] (4) The spore powder after freeze-drying is subjected to wall-breaking treatment in a high-frequency oscillating wall crusher. The working system of the high-frequency oscillating wall crusher is intermittent. : 5mm, crushing method: v...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com