Tea flavor shoe pad material

A technology for insoles and tea fragrance, which is applied in the field of preparing insole materials with tea fragrance, can solve the problems of insole sales such as adverse effects, and achieve the effect of large market value and low production cost

Inactive Publication Date: 2015-11-04
XTEPCHINA
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the EVA material is foamed into the insole, some auxiliary agents are added, which causes the odorless EVA material to have a rubber or glue smell after foaming, so that the foamed insole has a peculiar smell. It can only be gradually removed after being placed in a ventilated place for a long time, which will undoubtedly have a negative impact on the sales of insoles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A tea-flavored insole material of the present invention is prepared from the following raw materials in proportion by weight: 8 parts of POE elastomer, 65 parts of EVA plastic particles, 12 parts of low-density polyethylene, 5 parts of thermoplastic rubber, and 5 parts of talcum powder 5 parts, 5 parts of tea stem powder, 0.8 part of stearic acid, 1.5 parts of zinc oxide, 7 parts of foaming agent, 0.5 part of odorless bridging agent, 0.5 part of color masterbatch; 9107 is the DuPont elastomer produced by DuPont Company of the United States. The model of the EVA plastic particles is 7350M, the model of the low-density polyethylene is 2426, and the thermoplastic rubber is Japanese Asahi Kasei SEBS produced by the Japanese Asahi Kasei Company with the brand name JT-83. Thermoplastic elastomer, the talcum powder is 1250 mesh stone powder, and the color masterbatch is black masterbatch.

Embodiment 2

[0016] A tea-flavored insole material of the present invention is prepared from the following raw materials in proportion by weight: 10 parts of POE elastomer, 60 parts of EVA plastic particles, 10 parts of low-density polyethylene, 10 parts of thermoplastic rubber, and 3 parts of talcum powder Parts, 7 parts of tea stem powder, 1.2 parts of stearic acid, 1.2 parts of zinc oxide, 10 parts of foaming agent, 0.6 part of odorless bridging agent, 0.7 part of color masterbatch; 9107 is the DuPont elastomer produced by DuPont Company of the United States. The model of the EVA plastic particles is 7350M, the model of the low-density polyethylene is 2426, and the thermoplastic rubber is Japanese Asahi Kasei SEBS produced by the Japanese Asahi Kasei Company with the brand name JT-83. Thermoplastic elastomer, the talcum powder is 1250 mesh stone powder, and the color masterbatch is black masterbatch.

Embodiment 3

[0018] A tea-flavored insole material of the present invention is prepared from the following raw materials in proportion by weight: 12 parts of POE elastomer, 55 parts of EVA plastic particles, 10 parts of low-density polyethylene, 10 parts of thermoplastic rubber, and 3 parts of talcum powder 10 parts, 10 parts of tea stem powder, 1.5 parts of stearic acid, 1 part of zinc oxide, 12 parts of foaming agent, 0.8 part of odorless bridging agent, 1 part of color masterbatch; 9107 is the DuPont elastomer produced by DuPont Company of the United States. The model of the EVA plastic particles is 7350M, the model of the low-density polyethylene is 2426, and the thermoplastic rubber is Japanese Asahi Kasei SEBS produced by the Japanese Asahi Kasei Company with the brand name JT-83. Thermoplastic elastomer, the talcum powder is 1250 mesh stone powder, and the color masterbatch is black masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tea flavor shoe pad material. The tea flavor shoe pad material is prepared form, by weight, 5-15 parts of POE elastomer, 55-75 parts of EVA plastic pellets, 10-25 parts of low density polyethylene, 5-20 parts of thermoplastic rubber, 3-5 parts of talcum powder, 5-10 parts of tea stalk powder, 0.8-1.5 parts of stearic acid, 0.4-1.5 parts of zinc oxide, 4-10 parts of a foaming agent, 0.5-1.0 part of a tasteless bridging agent and 0.5-1.0 part of a color master; and the POE elastomer is DuPont elastomer with the trade name of I NFUSE and the grade of 9107, the model of the EVA plastic pellets is 7350M, the model of the low density polyethylene is 2426, and the thermoplastic rubber is Asahi Kasei SEBS thermoplastic elastomer with the grade of JT-83. Compared with shoe pad materials in the prior art, the tea flavor shoe pad material has the characteristics of light tea flavor, antibiosis, mildew resistance and color fixation; and waste tea stalk powder is adopted to prepare the tea flavor shoe pad material without individually purchasing tea stalk powder, so tea leaf wastes are effectively used, and the tea flavor shoe pad material responses to national waste reuse call.

Description

technical field [0001] The invention relates to a material for preparing insoles, in particular to a material for preparing insoles with tea fragrance. Background technique [0002] As we all know, EVA material is widely used in the insole manufacturing industry due to its good flexibility and wear resistance. However, when the EVA material is foamed into the insole, some auxiliary agents are added, which causes the odorless EVA material to have a rubber or glue smell after foaming, so that the foamed insole has a peculiar smell. It can only be gradually removed after being placed in a ventilated place for a long time, which will undoubtedly have a negative impact on the sales of insoles. [0003] In view of this, the inventor has carried out in-depth research on the above-mentioned problem, and this case arises therefrom. Contents of the invention [0004] The object of the present invention is to provide a tea-scented insole material, which can emit tea fragrance, is b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L53/02C08L97/02C08K3/34C08K5/09C08K3/22C08J9/04A43B17/14
CPCC08L23/0853A43B17/14C08J9/04C08J2323/08C08L2203/14C08L2205/02C08L2205/035C08L2207/066C08L23/0815C08L23/06C08L53/02C08L97/02C08K5/09C08K3/34C08K2003/2296
Inventor 马成曾理想陈青泉郭联敏叶东晓邓安明汤勋飞
Owner XTEPCHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products