Automotive alloying hot-dip galvanized steel with tensile strength of 440 MPa and production method

A tensile strength, hot-dip galvanizing technology, applied in hot-dip galvanizing process, metal material coating process, coating, etc., can solve the problems of high production cost, less micro-cracks, slow cooling speed, etc., and achieve uniform size distribution , fine surface structure and improved cooling uniformity

Inactive Publication Date: 2015-10-14
武汉钢铁有限公司
View PDF10 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the tensile strengths of the above-mentioned documents are all at 440 MPa, in order to achieve high strength, a large amount of alloying elements are added, resulting in high production costs; After fast cooling and alloying, the cooling rate is slow, so it is difficult to obtain a high-strength alloyed hot-dip galvanized steel sheet with fine grains, dense and uniform coating surface structure, less micro-cracks, and excellent powdering resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automotive alloying hot-dip galvanized steel with tensile strength of 440 MPa and production method
  • Automotive alloying hot-dip galvanized steel with tensile strength of 440 MPa and production method
  • Automotive alloying hot-dip galvanized steel with tensile strength of 440 MPa and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The present invention will be described in detail below:

[0041] Table 1 is a list of values ​​of various embodiments and comparative examples of the present invention;

[0042] Table 2 is a list of main process parameters of each embodiment and comparative example of the present invention;

[0043] Table 3 is a list of performance detection conditions of various embodiments of the present invention and comparative examples.

[0044] Each embodiment of the present invention is produced according to the following steps:

[0045] 1) Pre-treat the molten iron, control the S≤0.005% of the molten iron after pre-desulfurization treatment, and remove the slag;

[0046] 2) Conduct converter smelting and RH furnace treatment, and control the content of each element after refining to be within the set value range;

[0047] 3) Continuous casting: control the drawing speed at 1.2~1.4m / min, and the cooling speed of the cast slab surface shall not exceed 180℃ / m;

[0048] 4) Heating the slab, con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

Automotive alloying hot-dip galvanized steel with tensile strength of 440 MPa comprises, by weight, 0.08%-0.11% of C, smaller than or equal to 0.03% of Si, 1.10%-1.40% of Mn, 0.015 wt%-0.030% of P, smaller than or equal to 0.010% of S and 0.020%-0.070 of Als. A production method comprises the production steps of hot metal pretreatment, converter refining and RH furnace treatment, continuous casting, casting blank heating, hot rolling, the first time of rapid cooling, reeling, acid pickling, cold rolling, continuous annealing, hot galvanizing, the second time of rapid cooling, alloying, the third time of rapid cooling and finishing. The yield strength of the automotive alloying hot-dip galvanized steel is 330-360 MPa, the tensile strength of the automotive alloying hot-dip galvanized steel is not lower than 440 MPa, the ductility of the automotive alloying hot-dip galvanized steel is larger than or equal to 32%, the roughness of the alloying hot-dip galvanized steel is 0.6-1.5 [u]m, and the PC value of the automotive alloying hot-dip galvanized steel is not smaller than 90 / cm; a galvannealed coating of the automotive alloying hot-dip galvanized steel is small, even and compact in tissue, the pulverization degree is not larger than 2, and the pulverization resisting capability is excellent. Meanwhile, ingredients and technology of the automotive alloying hot-dip galvanized steel are simple, cost is low, and production efficiency is high.

Description

Technical field [0001] The invention relates to a galvanized steel for automobiles and a production method thereof, in particular to a hot-dip galvanized steel for automobiles with a tensile strength of 440MPa and a production method thereof. Background technique [0002] Alloyed hot-dip galvanized steel sheet (GA sheet) has excellent performance in terms of stamping formability, corrosion resistance, paintability and weldability. It meets the development requirements of automobile lightweight and strong safety, which has increasingly caused the automobile industry Attention. This is because to meet the anti-corrosion requirements of the car body, the quality of the coating must be controlled at 40g / m 2 As mentioned above, the production cost of electro-galvanized sheets increases sharply as the thickness of the coating increases. Therefore, how to ensure the corrosion resistance of the steel surface without excessively increasing production costs has become an important issue. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/06C21D8/02C23C2/06C23C2/28
Inventor 杜小峰孙方义潘立波陈宇王立辉冯冠文刘祥东方芳
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products