Anticorrosive amino resin paint and preparation method thereof

An amino resin and anti-corrosion technology, applied in the field of paint, can solve the problems of not meeting consumers' requirements for paint use, not being environmentally friendly, easy to corrode, etc., and achieve the effect of low cost, strong paint film adhesion, and full gloss

Inactive Publication Date: 2015-09-16
上海元邦化工制造有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Paint can be seen everywhere in daily life. It mainly plays the role of protection and decoration. According to different use environments, there are various types of paint. Traditional paints generally have heavy odor, easy to fall off, easy to corrode, and not environmentally friendly, etc. The problem is that it can no longer meet the requirements of consumers for the use of paint. Therefore, it is necessary to improve the formula of the original paint, increase the practicability and durability of the paint, reduce its harm to the environment and human body, and make it adaptable to various use environments. condition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] In the embodiment of the present invention, a kind of anti-corrosion amino resin paint, the raw material according to weight part comprises: 100 parts of amino resin, 45 parts of phenolic resin, 10 parts of aluminum tripolyphosphate, 10 parts of zinc phosphate, 10 parts of zinc oxide, dehydrogenation 10 parts of sodium acetate, 1 part of isopropanol, 1 part of ethoxylated trimethylolpropane triacrylate, 1 part of tetrabutylphosphine chloride, 1 part of naphthenic dicarboxylic acid monoester, 1 part of styrene, N- 5 parts of cyclohexylthiophthalimide, 5 parts of glycidyl acrylate, 5 parts of butyl acetate, 5 parts of trimellitic anhydride, 5 parts of maleic anhydride, 5 parts of sodium hexametaphosphate, isophthalic acid 3 parts of amine, 3 parts of activated calcium carbonate, 3 parts of m-p-cresol, 3 parts of ditetradecyl alcohol ester, 1 part of methyl acrylate, 1 part of 2-hydroxysuccinic acid, 1 part of wollastonite powder, and 1 part of carbon black share.

[0017...

Embodiment 2

[0019] In the embodiment of the present invention, a kind of anti-corrosion amino resin paint, the raw material according to weight part comprises: 120 parts of amino resin, 53 parts of phenolic resin, 15 parts of aluminum tripolyphosphate, 15 parts of zinc phosphate, 15 parts of zinc oxide, dehydrogenation 15 parts of sodium acetate, 5 parts of isopropanol, 5 parts of ethoxylated trimethylolpropane triacrylate, 5 parts of tetrabutylphosphine chloride, 5 parts of naphthenic dicarboxylic acid monoester, 5 parts of styrene, N- 10 parts of cyclohexylthiophthalimide, 10 parts of glycidyl acrylate, 10 parts of butyl acetate, 10 parts of trimellitic anhydride, 10 parts of maleic anhydride, 10 parts of sodium hexametaphosphate, isophthalic acid 8 parts of amine, 8 parts of activated calcium carbonate, 8 parts of m-p-cresol, 8 parts of ditetradecyl alcohol ester, 3 parts of methyl acrylate, 3 parts of 2-hydroxysuccinic acid, 3 parts of wollastonite powder, and 3 parts of carbon black ...

Embodiment 3

[0022] In the embodiment of the present invention, a kind of anti-corrosion amino resin paint, the raw material according to weight part comprises: 105 parts of amino resin, 48 parts of phenolic resin, 12 parts of aluminum tripolyphosphate, 12 parts of zinc phosphate, 12 parts of zinc oxide, dehydrogenation 12 parts of sodium acetate, 2 parts of isopropanol, 2 parts of ethoxylated trimethylolpropane triacrylate, 2 parts of tetrabutylphosphine chloride, 2 parts of naphthenic dicarboxylic acid monoester, 2 parts of styrene, N- 7 parts of cyclohexylthiophthalimide, 7 parts of glycidyl acrylate, 7 parts of butyl acetate, 7 parts of trimellitic anhydride, 7 parts of maleic anhydride, 7 parts of sodium hexametaphosphate, isophthalic acid 5 parts of amine, 5 parts of activated calcium carbonate, 5 parts of m-p-cresol, 5 parts of ditetradecyl alcohol ester, 1 part of methyl acrylate, 1 part of 2-hydroxysuccinic acid, 1 part of wollastonite powder, and 1 part of carbon black share.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses anticorrosive amino resin paint and a preparation method thereof. The anticorrosive amino resin paint is prepared from the following raw materials in parts by weight: 100 to 120 parts of amino resin, 45 to 53 parts of phenolic resin, 10 to 15 parts of aluminium triphosphate, 10 to 15 parts of zinc phosphate, 10 to 15 parts of zinc oxide, 10 to 15 parts of sodium dehydroacetate, 1 to 5 parts of isopropanol, 1 to 5 parts of ethylate trimethylolpropane triacrylate, 1 to 5 parts of tetrabutylphosphonium chloride, 1 to 5 parts of naphthenic dicarboxylic acid monoester, 1 to 5 parts of styrene, 5 to 10 parts of N-cyclohexylthiophthalimide, 5 to 10 parts of glycidyl acrylate, 5 to 10 parts of butyl acetate, 5 to 10 parts of trimellitic anhydride, 5 to 10 parts of maleic anhydride, 5 to 10 parts of sodium hexametaphosphate, 3 to 8 parts of m-xylylenediamine, 3 to 8 parts of activated calcium carbonate, 3 to 8 parts of cresol, 3 to 8 parts of bi-tetradecanol polycarbonate, 1 to 3 parts of methyl acrylate, 1 to 3 parts of 2-malic acid, 1 to 3 parts of wollastonite in powder, and 1 to 3 parts of carbon black. The preparation method is simple; the cost is small; a paint film is high in attaching performance, resistant to corrosion, resistant to ageing, and long in service life.

Description

technical field [0001] The invention relates to the field of paints, in particular to an anti-corrosion amino resin paint and a preparation method thereof. Background technique [0002] Paint can be seen everywhere in daily life. It mainly plays the role of protection and decoration. According to different use environments, there are various types of paint. Traditional paints generally have heavy odor, easy to fall off, easy to corrode, and not environmentally friendly, etc. The problem is that it can no longer meet the requirements of consumers for the use of paint. Therefore, it is necessary to improve the formula of the original paint, increase the practicability and durability of the paint, reduce its harm to the environment and human body, and make it adaptable to various use environments. condition. Contents of the invention [0003] The object of the present invention is to provide an anti-rust and anti-corrosion, full luster, long-lasting color and anti-corrosion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D161/10C09D5/08C08F283/00
Inventor 翁国华
Owner 上海元邦化工制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products