A transfer type decorative film

A decorative film and transfer-type technology, applied in the direction of layered products, metal layered products, synthetic resin layered products, etc., can solve the problems of denaturation, coating elasticity reduction, stickiness, etc., achieve soft and comfortable touch, improve Effects using persistent, rich color effects

Active Publication Date: 2017-03-01
BAODING LUCKY INNOVATIVE MATERIALS
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After long-term application, spraying such products can have a soft touch effect. Over time, the elasticity of the coating decreases, gradually aging, the soft touch disappears or turns into a sticky feeling, and in severe cases, stickiness occurs, that is, the soft touch effect has a short life. , affecting comfort and durability
[0004] In the process of thermal transfer printing or IMD transfer printing, decorative film products with high temperature shock resistance and certain pressure are required as supporting consumables. When traditional materials are subjected to high temperature and pressure, the spherical collagen is easily damaged, denatured, and loses its proper softness. It is not suitable for thermal transfer fields such as hot stamping and IMD

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A transfer type decorative film
  • A transfer type decorative film
  • A transfer type decorative film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] A PET carrier film with a thickness of 70 μm is used, and a release layer with a thickness of 0.5 μm, a tactile functional layer with a thickness of 30 μm, and a colored layer with a thickness of 0.5 μm are sequentially coated on one side of the carrier film.

[0074] ①The components and parts by weight in the release layer are as follows:

[0075]

[0076] ②The tactile functional layer adopts UV curing system, and the components and their parts by weight are as follows:

[0077]

[0078]

[0079] ③The components of the coloring layer and their parts by weight are as follows

[0080]

[0081] ④A vacuum evaporation process is adopted on the colored layer to evaporate an aluminum layer with a thickness of 40nm.

[0082] ⑤The adhesive layer is configured as a coating solution according to the conventional method, and coated on the aluminum-coated layer;

[0083] The decorative film prepared according to the above scheme was applied and processed, and the perf...

Embodiment 2

[0085] A PET carrier film with a thickness of 50 μm is used, and a release layer with a thickness of 0.8 μm, a tactile functional layer with a thickness of 25 μm, and a colored layer with a thickness of 0.8 μm are sequentially coated on one side of the carrier film.

[0086] ①The components and parts by weight in the release layer are as follows:

[0087]

[0088] ②The tactile functional layer adopts UV curing system, and the components and their parts by weight are as follows:

[0089]

[0090] ③The components and parts by weight of the coloring layer are as follows:

[0091]

[0092] ④A vacuum evaporation process is adopted on the coloring layer to evaporate a silver layer with a thickness of 45nm.

[0093] ⑤ The adhesive layer is configured as a coating solution according to the conventional method, and coated on the silver-plated layer;

[0094] The decorative film prepared according to the above scheme was applied and processed, and the performance test was car...

Embodiment 3

[0096] A PET carrier film with a thickness of 35 μm is used, and a release layer with a thickness of 1.0 μm, a tactile functional layer with a thickness of 20 μm, and a colored layer with a thickness of 0.5 μm are sequentially coated on one side of the carrier film.

[0097] ①The components and parts by weight in the release layer are as follows:

[0098]

[0099]

[0100] ②The tactile functional layer adopts UV curing system, and the components and their parts by weight are as follows:

[0101]

[0102] ③The components of the coloring layer and their parts by weight are as follows

[0103]

[0104] ④A vacuum evaporation process is adopted on the coloring layer to evaporate a copper layer with a thickness of 30nm.

[0105] ⑤ The adhesive layer is configured as a coating solution according to the conventional method, and coated on the copper plating layer;

[0106] The decorative film prepared according to the above scheme was applied and processed, and the performa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to transfer decoration film. The decoration film is formed by carrier film, a separation layer, a touch function layer, a coloring layer, a metal layer and a bonding layer. After the decoration film is used, work-piece surfaces touch soft like velvet, a good self-repair function is provided after scratches are produced on the surfaces, and the use durability of the comfort effect is improved. The decoration film is applied to indoor decoration materials, such as car interiors, household appliances, cosmetic containers, covers, bags, clothes, furniture wooden products, plastic fabricated products, in-mold formed products, artware and surface decoration of electronic products of mobile phones, laptops and the like.

Description

technical field [0001] The invention relates to a decorative film, in particular to a transfer type decorative film. Background technique [0002] With the gradual improvement of modern people's living standards, electronic products such as mobile phones, tablet computers, notebook computers, household appliances, and automobile products have begun to become popular, and people's pursuit of personalized appearance and quality of these products is becoming more and more diverse. In addition, the personalized decoration of interior decoration materials such as furniture, door walls and door handles is becoming more and more abundant. The external surfaces of these products usually have personalized 2D, 3D patterns or special color effects, such as the appearance of special effects such as high-end car interiors, imitation wood grain, soft touch, and metallization of furniture. To achieve these personalized appearances, it usually needs to be realized through special coating s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/08B32B7/06B32B7/12B32B27/06B32B27/04B32B27/18B41M5/40
CPCB32B7/06B32B7/12B32B15/08B32B27/06B32B27/18B32B2264/0214B41M5/40
Inventor 任卫强刘彦峰
Owner BAODING LUCKY INNOVATIVE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com