A fast repair paint for reducing chromatic aberration of car body repair and preparation method thereof

A technology for refinishing paint and color difference, applied in the field of paint, can solve the problems of color difference, difficult to control the direction of paint mica particles, inconsistent direction, etc., to prevent silver powder from blooming, provide interlayer adhesion, and reduce color difference.

Active Publication Date: 2017-04-05
ZHANGZHOU XIN ZHAN WANG CHEM IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because it is difficult to control the directionality of the paint mica particles that are added later, or it is almost impossible to be consistent with the original direction. If the direction is not consistent, the color will be significantly different.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The repair paint, its raw material counts by weight 40 parts of resin, 30 parts of additive resin, 6 parts of metallic pigment, 17 parts of copolymer, 6 parts of solvent, 1 part of auxiliary agent.

[0032] The resin is selected from amino resins.

[0033] The additive resin is selected from hydroxyl modified resins.

[0034] The metal pigment is aluminum silver powder.

[0035] The copolymer is selected from ethyl acetate.

[0036] The solvent is selected from methyl isobutyl ketone.

[0037] Auxiliaries are selected from leveling agents.

[0038] The preparation method comprises the following process steps:

[0039] (1) Put all the solvents into the reaction kettle according to the formula requirements, and heat to 30°C for stirring;

[0040] (2) Keep stirring and put the resins into the reaction kettle one by one, stirring and dissolving for 0.5 hours;

[0041] (3) Slowly put the additive resin and copolymer into the reaction kettle after being dissolved;

[0...

Embodiment 2

[0048] A rapid repair paint for reducing color difference in car body repair, the raw materials of which are 32 parts by weight of resin, 38 parts of additive resin, 8 parts of metallic pigment, 12 parts of copolymer, 8 parts of solvent and 2 parts of auxiliary agent.

[0049] The resin is selected from thermoplastic resins.

[0050] The additive resin is selected from cellulose acetate butyrate.

[0051] The metal pigment is copper gold powder.

[0052] The copolymer is selected from ethylene-vinyl acetate.

[0053] The solvent is selected from butanone.

[0054] Auxiliaries are selected from defoamers.

[0055] The preparation method is characterized in that: the method comprises the following process steps:

[0056] (1) Put all the solvents into the reaction kettle according to the formula requirements, and heat to 45°C for stirring;

[0057] (2) Keep stirring and put the resin into the reaction kettle one by one, stir and dissolve for 1.5 hours;

[0058] (3) Slowly p...

Embodiment 3

[0065] A rapid repair paint for reducing color difference in car body repair, the raw materials of which are 25 parts by weight of resin, 31 parts of additive resin, 9 parts of metallic pigment, 20 parts of copolymer, 10 parts of solvent and 5 parts of auxiliary agent.

[0066] The resin is selected from hydroxyl resin, saturated polyester resin.

[0067] The additive resin is selected from cellulose acetate butyrate, vinyl resins.

[0068] The metal pigments are aluminum silver powder and pearl powder.

[0069] The copolymer is selected from ethyl acetate, complex polyolefin compounds.

[0070] The solvent is selected from butanone and n-butanol.

[0071] Auxiliaries are selected from leveling agents, defoamers, wetting and dispersing agents.

[0072] The preparation method for reducing the chromatic aberration fast repair paint of car body repair comprises the following process steps:

[0073] (1) Put all the solvents into the reaction kettle according to the formula requi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention provides rapid repair paint for reducing the repair chromatic aberration of a car body and a preparation method of the rapid repair paint. The repair paint comprises the ingredients in parts by weight: 20-40 parts of resin, 20-40 parts of additive resin, 5-10 parts of a metal pigment, 10-20 parts of a copolymer, 5-10 parts of a solvent, and 1-5 parts of an additive. The preparation process is simple, through the application of the obtained repair paint, the repair chromatic aberration of the car body can be reduced effectively, and the repair efficiency can be improved; after repair, particles of metal paint looks more three-dimensional, metallic and brilliant, the product performance is excellent, the hardness is equal to and higher than H, and the adhesive force is 0-1 level.

Description

technical field [0001] The invention belongs to the field of paints, and in particular relates to a rapid repair paint for reducing color difference in car body repair and a preparation method thereof. Background technique [0002] Automotive flash paint has a metallic flash texture, which can improve the grade of the paint film and fully demonstrate the effect of noble and elegant temperament. Flash paint includes metallic paint and pearlescent paint. The monochrome paint reflects the incident light through the pigment particles. Since the scattered light is the main body, there is no color flop effect, so the color difference is easy to control. For metallic paint, when the flake aluminum powder is arranged parallel to the substrate in the paint film, it looks like a small mirror. , different shades of metallic color and sparkle can be observed. The aluminum powder content and the size of the aluminum powder in the metallic paint have a great influence on the lightness....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D161/20C09D201/00C09D101/14C09D123/08C09D167/00C09D7/12
Inventor 张信露谢平展张秋虹
Owner ZHANGZHOU XIN ZHAN WANG CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com