Self-stress and self-leveling grouting material for equipment

A technology of self-leveling and grouting materials, applied in the field of building materials

Inactive Publication Date: 2015-08-26
LINYI UNIVERSITY
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a grouting material for self-stressed self-leveling equipment, which solves the coordination problem of early expansion, mid-term expansion and late expansion of the grouting material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-stress and self-leveling grouting material for equipment
  • Self-stress and self-leveling grouting material for equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: a self-stress self-leveling equipment grouting material, the proportion of each component is as follows (mass percentage):

[0031] The mass percent composition of main materials is:

[0032] Ordinary 42.5 grade Portland cement 35%

[0033] Mineral admixture 18.5%

[0034] River sand 45%

[0035] Steel Fiber 1.5%

[0036] The mass percent of each component of the auxiliary material in the cementitious material is:

[0037] Bulking agent composition 4%

[0038] Toughener 6%

[0039] Water retention thickener 0.03%

[0040] Early strength agent 3%

[0041] Powder polycarboxylate superplasticizer 0.3%

Embodiment 2

[0042]Embodiment 2: a self-stress self-leveling equipment grouting material, the proportion of each component is as follows (mass percentage):

[0043] The mass percent composition of main materials is:

[0044] Ordinary 52.5 Portland cement 30%

[0045] Mineral admixture 23.5%

[0046] River sand 45%

[0047] Steel Fiber 1.5%

[0048] The mass percent of each component of the auxiliary material in the cementitious material is:

[0049] Bulking agent composition 6%

[0050] Toughener 8%

[0051] Water retention thickener 0.02%

[0052] Early strength agent 2%

[0053] Powder polycarboxylate superplasticizer 0.3%

Embodiment 3

[0054] Embodiment 3: a self-stress self-leveling equipment grouting material, the proportion of each component is as follows (mass percentage):

[0055] The mass percent composition of main materials is:

[0056] Ordinary 42.5 Portland cement 45%

[0057] Mineral admixture 10%

[0058] River sand 43%

[0059] Steel Fiber 2%

[0060] The mass percent of each component of the auxiliary material in the cementitious material is:

[0061] Bulking agent composition 8%

[0062] Toughener 7%

[0063] Water retention thickener 0.04%

[0064] Early strength agent 4%

[0065] Powder polycarboxylate superplasticizer 0.4%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides a self-stress and self-leveling grouting material for equipment. The grouting material consists of main materials and auxiliary materials, wherein the main materials comprise 30-45% of cement, 10-25% of mineral admixture and 35-45% of river sand, and the mineral admixture consists of pulverized coal ash, mineral powder and river sand powder which are in the mass ratio of (0.6-1.0): (1.6-2.0): (0.6-1.0); and the auxiliary materials comprise an expansion agent composition, a water retention thickener, an early strength agent and a powdered polycarboxylic acid water reducing agent and contain the ingredients in percentage by mass based on the sum of mass of cement and mineral admixture sequentially: 4%-8% of the expansion agent composition, 0.01%-0.05% of the water retention thickener, 2%-4% of the early strength agent and 0.2%-0.4% of the powdered polycarboxylic acid water reducing agent, wherein the expansion agent composition consists of rice hull ash, MgO and a UEA expansion agent which are in the mass ratio of (0.6-1.0): (0.6-1.0): (1.5-2.0), the water retention thickener is sodium alginate, and the early strength agent consists of gypsum powder, sodium carbonate and silica fume which are in the mass ratio of (0.8-1.0): (0.5-1.0): (0.6-1.0).

Description

technical field [0001] The invention relates to a grouting material for self-stress and self-leveling equipment, which belongs to the field of building materials. Background technique [0002] Cement-based self-leveling equipment grouting material is a kind of dry mixture with reasonable gradation produced by factory production of raw materials such as cement, aggregate (or no aggregate), admixture and mineral admixture. After adding water and mixing evenly, it has the properties of pourable fluidity, micro-swelling, high early and late strength, and no bleeding. The grouting material is mainly used for: anchoring of anchor bolts, emergency repair of airstrips, fixing of nuclear power equipment, reinforcement of road and bridge engineering, machine base, steel structure and foundation opening, secondary grouting of equipment foundation, planting steel bars, concrete structures Reinforcement and reconstruction, crack treatment of old concrete structures, installation of mech...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/08C04B14/06C04B22/14C04B111/70
Inventor 张伟
Owner LINYI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com