PTT polyester based weather resistant flame retardant composite material
A flame-retardant composite material and weather-resistant technology, applied in the field of polymer materials, can solve the problems of easy aging, poor flame retardancy, high notch sensitivity, etc., and achieve good weather resistance stability, good flame retardant performance, and good flame retardant effect. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A weather-resistant and flame-retardant composite material based on PTT polyester, its components are proportioned by mass percentage: PTT 82%, inorganic filler 15%, aluminum-titanium composite coupling agent 0.3%, composite flame retardant 0.2%, benzo 1.5% of triazole ultraviolet absorber, 0.2% of ethylene-methacrylate sodium ion polymer, 0.2% of antioxidant, 0.6% of ethylene bisstearamide, and the PTT is a polymer with an intrinsic viscosity of 0.7-1.2dL / g. Propylene glycol terephthalate, the inorganic filler is calcium carbonate with an average particle size of 0.1-100 μm, and the composite flame retardant is iodate flame retardant potassium perfluorobutylsulfonate and potassium perfluorobutylsulfonate with a mass ratio of 1:1 A compound of polytetrafluoroethylene resistant to dripping, the antioxidant is a compound of hindered phenolic antioxidant 1010 and phosphite antioxidant 168 at a mass ratio of 1:1.
[0022] Preparation method: (1), place PTT in a forced air c...
Embodiment 2
[0024] A weather-resistant and flame-retardant composite material based on PTT polyester, its components are proportioned by mass percentage: PTT 88%, inorganic filler 10%, silane coupling agent 0.1%, composite flame retardant 0.2%, benzophenone 0.9% UV absorber, 0.1% ethylene-methacrylate sodium ion polymer, 0.1% antioxidant, 0.6% pentaerythritol stearate, and the PTT is polyterephthalate with an intrinsic viscosity of 0.7-1.2dL / g Propylene glycol formate, the inorganic filler is magnesium hydroxide with an average particle size of 0.1-100 μm, the composite flame retardant is iodate flame retardant potassium perfluorobutylsulfonate and refractory Drops of polytetrafluoroethylene compound, the antioxidant is a compound of hindered phenolic antioxidant 1010 or 1076 and phosphite antioxidant 168 at a mass ratio of 1:1.
[0025] Preparation method: (1), place PTT in a forced air circulation oven and dry at 110°C-120°C for 6-8 hours, dry the inorganic filler at 60°C-80°C for 1-2 h...
PUM
Property | Measurement | Unit |
---|---|---|
Intrinsic viscosity | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com