Alcohol acid phase-inverted emulsion as well as preparation method and application of alcohol acid phase-inverted emulsion

A phase inversion and alkyd technology, applied in the field of alkyd phase inversion emulsion and its preparation, can solve the problems of aggravating health hazards, high resin viscosity, slow drying of the coating film, etc. good effect

Active Publication Date: 2015-08-12
山东奔腾漆业股份有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, most water-based alkyd products in the market are water-soluble, that is, on the basis of traditional alkyd resins, use trimellitic anhydride or maleic anhydride to control the acid value at 40-60 mg KOH / g, and then add 30-40% glycol ether Or diluted with butanol organic solvents, and finally neutralized by toxic amines, resulting in high resin viscosity, slow drying of the coating film, low hardness, resistance to hydrolysis, storage stability of finished paint and other disadvantages; on the other hand, Organic volatiles are increasingly harmful to people's health, which has gradually increased the haze weather. With the progress of society, the continuous improvement of people's environmental requirements and the continuous improvement of environmental protection standards and regulations, environmentally friendly green products with low VOC and air pollutants Coatings have received increasing attention from people and have developed rapidly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alcohol acid phase-inverted emulsion as well as preparation method and application of alcohol acid phase-inverted emulsion
  • Alcohol acid phase-inverted emulsion as well as preparation method and application of alcohol acid phase-inverted emulsion
  • Alcohol acid phase-inverted emulsion as well as preparation method and application of alcohol acid phase-inverted emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The alkyd phase inversion emulsion white paint comprises the following components by weight:

[0031]

[0032]

[0033] Wherein, the mass solid concentration of alkyd emulsion is 50%, and it is made up of the following components by weight:

[0034]

[0035] Wherein, the preparation method of alkyd phase inversion emulsion white paint comprises the following steps:

[0036] (1) After mixing 50% deionized water, defoamer A-10, pigments and fillers (rutile titanium dioxide), dispersant, and propylene glycol, disperse at a speed of 1000r / min for 20min, and grind until the fineness reaches 35μm, poured into paint pots;

[0037] (2) Add alkyd phase-inversion emulsion, add the remaining amount of deionized water and stir evenly, and disperse at a speed of 700r / min for 5-15min;

[0038] (3) Add rheological agent 8w and rheological agent 2020, and stir at 700r / min for 30min to obtain the product.

[0039] Wherein, the alkyd phase inversion emulsion resin is prepared...

Embodiment 2

[0048] The alkyd phase inversion emulsion white paint comprises the following components by weight:

[0049]

[0050] Wherein, the mass solid concentration of alkyd emulsion is 52%, and it is made up of following components by weight:

[0051]

[0052] Wherein, the preparation method of alkyd phase inversion emulsion white paint comprises the following steps:

[0053] (1) After mixing 40% deionized water, defoamer A-10, pigments and fillers (rutile titanium dioxide), dispersant, and propylene glycol, disperse at a speed of 800r / min for 25min, and grind until the fineness reaches 35μm, poured into paint pots;

[0054] (2) Add alkyd phase-inversion emulsion, add the remaining amount of deionized water and stir evenly, and disperse for 15 minutes at a speed of 600r / min;

[0055] (3) Then add rheological agent 8w and rheological agent 2020, and stir at a speed of 600r / min for 35min to obtain the product.

[0056] Wherein, the alkyd phase inversion emulsion resin is prepar...

Embodiment 3

[0065] The alkyd phase inversion emulsion white paint comprises the following components by weight:

[0066]

[0067]

[0068] Wherein, the mass solid concentration of alkyd emulsion is 48%, and it is made up of the following components by weight:

[0069]

[0070] (1) After mixing 60% deionized water, defoamer A-10, pigments and fillers (rutile titanium dioxide), dispersant, and propylene glycol, disperse at a speed of 1200r / min for 15min, and grind until the fineness reaches 35μm, poured into paint pots;

[0071] (2) Add alkyd phase-inversion emulsion, add the remaining amount of deionized water and stir evenly, and disperse for 5 minutes at a speed of 800r / min;

[0072] (3) Add rheological agent 8w and rheological agent 2020, and stir at 800r / min for 25min to obtain the product.

[0073] Wherein, the alkyd phase inversion emulsion resin is prepared by the following method:

[0074] (1) Put soy oil, phthalic anhydride, pentaerythritol and reflux solvent into an e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an alcohol acid phase-inverted emulsion coating. The alcohol acid phase-inverted emulsion coating comprises the following components in parts by weight: 60-70 parts of alcohol acid phase-inverted emulsion, 10-20 parts of pigment filler, 1-1.5 parts of a rheological agent, 0.05-0.1 part of a defoamer, 0.5-1 part of an oil-based drier and 10-25 parts of deionized water. The alcohol acid phase-inverted emulsion coating has an extremely low VOC value and is good in chemical resistance, waterproofness and salt fog resistance and wide in application range.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to an alkyd phase-inversion emulsion and its preparation method and application. Background technique [0002] Alkyd coatings have excellent technological properties, mechanical properties and physical properties, and are widely used in the fields of mechatronics, aviation, transportation and construction. [0003] Currently, traditional alkyd resins are water-insoluble or solvent-based coatings. On the one hand, most water-based alkyd products in the market are water-soluble, that is, on the basis of traditional alkyd resins, use trimellitic anhydride or maleic anhydride to control the acid value at 40-60 mg KOH / g, and then add 30-40% glycol ether Or diluted with butanol organic solvents, and finally neutralized by toxic amines, resulting in high resin viscosity, slow drying of the coating film, low hardness, resistance to hydrolysis, storage stability of the finished paint and other disad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J3/07C08G63/52C08G63/49C09D167/06C09D7/12
Inventor 孟祥开孟令汉张庆忠徐步峰
Owner 山东奔腾漆业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com