Wood enhancement and corrosion prevention modification liquid and preparation method thereof

A technology for modifying liquid and wood, applied in wood treatment, wood impregnation, wood impregnation, etc., can solve the problems of difficult to guarantee product quality stability, decline in physical and mechanical properties of wood, and limit the application range of carbonized wood, and achieve bright color, The effect of strong three-dimensional effect and increased density of physical stripes

Inactive Publication Date: 2015-07-29
HUNAN DONGLIANG WOOD IND
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the disadvantage is that the oil will soak into the wood and increase the weight of the wood by 50% to 70%, and the heat-treated wood has a smell of oily smoke
[0013] The above four heat treatment processes are complicated, the process conditions are harsh, the control is difficult, and the stability of product quality is difficult to guarantee. Some treatment processes also require special heat treatment media. For example, the French Rectification process requires nitrogen, and the German OHT treatment process requires oil. as a heat treatment medium
[0014] Although the dimensional stability of the wood can be improved after heat treatment modification, the equilibrium moisture content in the wood decreases, the corrosion resistance also increases, the cementation performance improves, the wood color becomes darker, and the appearance of the wood with poor appearance is improved. However, heat treatment The physical and mechanical properties of the finished wood decline, and the wood strength value drops greatly, such as: the bending strength decreases, the surface wettability decreases, etc., and the existing modified wood has poor anticorrosion, which greatly limits the carbonized wood. Application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A wood-enhanced anticorrosion modification liquid, comprising the following raw materials in parts by weight:

[0047] 10 parts of melamine modified urea-formaldehyde resin

[0048] 4 parts dextrin

[0049] Nano modifier 1 part

[0050] Preservative 0.5 parts

[0051] Auxiliary 1 part

[0052] 60 parts of water.

[0053] The preparation of described melamine modified urea-formaldehyde resin comprises the steps:

[0054] a. Raw materials are prepared according to the following proportions by weight: melamine 350, methanol 180, formaldehyde 500, urea 50;

[0055] b, melamine and formaldehyde are added in the reaction kettle, after stirring evenly, sodium hydroxide is added to adjust the pH value of the mixed solution of melamine and formaldehyde, and the reaction is carried out by heating and raising the temperature to obtain a reaction solution, wherein the adjusted pH value is 9.1, and the reaction temperature 75°C, the reaction time is 30min;

[0056] c. Keep th...

Embodiment 2

[0067] A wood-enhanced anticorrosion modification liquid, comprising the following raw materials in parts by weight:

[0068] 15 parts of melamine modified urea-formaldehyde resin

[0069] Dextrin 5 parts

[0070] Nano modifier 2 parts

[0071] Preservative 0.7 parts

[0072] Auxiliary 2 parts

[0073] 70 parts of water.

[0074] The preparation of described melamine modified urea-formaldehyde resin comprises the steps:

[0075] a. Raw materials are prepared according to the following proportions by weight: melamine 375, methanol 190, formaldehyde 510, urea 75;

[0076] b, melamine and formaldehyde are added in the reaction kettle, after stirring evenly, add sodium hydroxide to adjust the pH value of the mixed solution of melamine and formaldehyde, heat and raise the temperature for reaction to obtain a reaction solution, wherein the adjusted pH value is 9.2, and the reaction temperature The temperature is 77°C, and the reaction time is 35 minutes;

[0077] c. Keep the ...

Embodiment 3

[0088] A wood-enhanced anticorrosion modification liquid, comprising the following raw materials in parts by weight:

[0089] 20 parts of melamine modified urea-formaldehyde resin

[0090]Dextrin 6 parts

[0091] Nano modifier 3 parts

[0092] 1 part preservative

[0093] Auxiliary 3 parts

[0094] 80 parts of water.

[0095] The preparation of described melamine modified urea-formaldehyde resin comprises the steps:

[0096] a. Raw materials are prepared according to the following proportions by weight: melamine 400, methanol 210, formaldehyde 520, urea 100;

[0097] B, melamine and formaldehyde are added in the reaction kettle, after stirring evenly, add sodium hydroxide to adjust the pH value of melamine and formaldehyde mixed solution, heat up and react, make reaction solution, wherein, the adjusted pH value is 9.3, and the reaction temperature The temperature is 80°C, and the reaction time is 40 minutes;

[0098] c. Keep the temperature of the reaction solution in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bending strengthaaaaaaaaaa
Flexural modulus of elasticityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of wood modification, in particular to a wood enhancement and corrosion prevention modification liquid and a preparation method thereof. The wood enhancement and corrosion prevention modification liquid comprises the following raw materials in parts by weight: 10-30 parts of melamine modified urea resin, 4-8 parts of dextrin, 1-5 parts of a nano modifier, 0.5-1.5 parts of a preservative, 1-5 parts of auxiliaries and 60-100 parts of water. According to the wood enhancement and corrosion prevention modification liquid, the intensity and the corrosion resistance of woods can be improved; furthermore, the insect bite, mildewing, water, flame, deformation and cracking prevention performance of the modified woods are greatly improved; the density, the hardness, the anti-bending intensity and the elastic modulus are higher, so that the use performance of the woods can be improved, and the service life of the woods is prolonged. The wood enhancement and corrosion prevention modification liquid has natural properties of heat insulation, temperature adjustment, humidity adjustment and the like, is colorful and bright and is high in physical stripe third dimension; a plate looks transparent and natural.

Description

technical field [0001] The invention relates to the technical field of wood modification, in particular to a wood-enhanced anti-corrosion modification liquid and a preparation method thereof. Background technique [0002] With the development of the country's economic construction and the improvement of people's living standards, people's demand for wood is increasing. The implementation of natural forest protection projects has made the contradiction between supply and demand of timber more prominent. In order to alleviate the contradiction between supply and demand, my country has built a large area of ​​industrial plantation. Although the artificial forest wood has the advantages of fast growth and high yield, the physical and mechanical properties of the artificial fast-growing forest wood are poor, the density is low, the material is soft, and it is easy to shrink and deform. [0003] In order to expand the application range of artificial forest timber and improve the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/50
CPCB27K3/50B27K2240/20B27K2240/30B27K2240/70
Inventor 杨杨芳
Owner HUNAN DONGLIANG WOOD IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products