Novel adsorption column for removing heavy metals and preparation method of adsorption column

A heavy metal and adsorption column technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of complex production process, poor mechanical properties, easy aging and deformation, etc., achieve simple preparation process, low cost, and avoid secondary pollution effect

Active Publication Date: 2015-07-29
山西阳中新材有限责任公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, general adsorption equipment is placed in sewage sludge with complex composition, which has problems such as easy corrosion, poor mechanical properties, easy aging and deformation, complicated production process, and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel adsorption column for removing heavy metals and preparation method of adsorption column
  • Novel adsorption column for removing heavy metals and preparation method of adsorption column
  • Novel adsorption column for removing heavy metals and preparation method of adsorption column

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A preparation method for removing a novel adsorption column for heavy metals, comprising the steps of:

[0036] 1) crushing and grinding the recovered biogel material of 5-10 parts by mass;

[0037] 2) Put 20-48 mass parts of environmentally friendly resin into a clean mixing tank, stir at a speed of 900-1500rpm for 5-10min, keep the stirring speed constant, add the above-mentioned ground sodium alginate gel material, continue Stir for 10-15 minutes, keep the stirring rate constant, add 20-48 parts by mass of composite powder, continue stirring for 15-20 minutes, keep the stirring rate constant, add 0.1-1 parts by mass of color paste and 0.1-1 parts by mass of Accelerator, continue to stir for 5-10 minutes, keep the stirring rate constant, add 0.1-1 mass part of curing agent, continue to stir for 5-10 minutes, and form a mixed raw material;

[0038] 3) Open the mold corresponding to each part of the adsorption column, place the glass fiber in each mold, the shape and s...

Embodiment 1

[0056] Environmentally friendly resin includes the following components: 25% phthalic anhydride, 20% maleic anhydride, 15% glycerin, 10% diethylene glycol, 10% ethylene glycol, 2% benzoic acid, and 18% styrene.

[0057] The preparation method for removing heavy metal novel adsorption column comprises the following steps:

[0058] 1) Grinding and grinding the sodium alginate gel material of 6 parts by mass;

[0059] 2) Put 26 parts by mass of environmentally friendly resin into a clean mixing tank, stir for 5 minutes at a speed of 1000 rpm, keep the stirring rate constant, add the above-mentioned ground and crushed sodium alginate gel material, continue stirring for 10 minutes, and keep stirring Speed ​​is constant, add and the calcium carbonate of 25 mass parts, continue stirring 15min, keep stirring speed constant, add the color paste of 0.24 mass part and the cobalt isooctanoate of 0.24 mass part, continue stirring 5min, keep stirring speed constant, add 0.30 parts by mass ...

Embodiment 2

[0065] Environmentally friendly resin includes the following components: 25% phthalic anhydride, 20% maleic anhydride, 15% glycerin, 10% diethylene glycol, 10% ethylene glycol, 2% benzoic acid, and 18% styrene.

[0066] A kind of preparation method for removing heavy metal novel adsorption column comprises the following steps:

[0067] 1) Grinding and grinding the sodium alginate gel material of 10 parts by mass;

[0068] 2) Put 46 parts by mass of environmentally friendly resin into a clean mixing bucket, stir at a speed of 1000rpm for 10 minutes, keep the stirring rate constant, add the above-mentioned ground and pulverized sodium alginate gel material, continue stirring for 10 minutes, and keep stirring Speed ​​is constant, add the calcium carbonate of 45 mass parts, continue stirring 20min, keep stirring speed constant, add the color paste of 0.4 mass part and the copper naphthenate of 0.4 mass part, continue stirring 10min, keep stirring speed constant, add The methyl et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel adsorption column for removing heavy metals and a preparation method of the adsorption column. Recovered waste sodium alginate gel and environment-friendly resin are combined, artificial stones are formed, and the adsorption column is further prepared. The adsorption column has the effect of adsorbing heavy metal ions, the adsorption column which has certain space and is formed by a top cover, a strip-shaped cage body and a bottom plate can be filled with other adsorption gel capsule materials for removing the heavy metal ions, and the problem that the gel capsule materials cannot be recovered after heavy metal adsorption is solved. Tightening ring parts of the adsorption column are used for fixing the body of the adsorption column so as to prevent the adsorption column from falling apart. Recovery, regrinding and sample preparation can be performed after the adsorption column is damaged during adsorption, and recycling is realized. The novel adsorption column for removing the heavy metals has excellent performance such as high mechanical strength, good pollution resistance, acid and alkali corrosion resistance and the like and has very high commercial exploitation value, and secondary pollution can be avoided fundamentally.

Description

technical field [0001] The invention belongs to the technical field of sewage sludge treatment, and in particular relates to a novel adsorption column for removing heavy metals and a preparation method thereof. Background technique [0002] The rapid development of my country's industrial manufacturing industry, on the one hand, has promoted the growth of the national economy, on the other hand, it has also brought a large amount of industrial wastewater, which generally contains a large amount of chemical toxic elements, heavy metal ions, etc., causing environmental pollution and affecting human health. There are two main ways to capture heavy metals in sewage sludge. [0003] (1) Use heavy metal scavengers. [0004] The heavy metal scavenger is a reagent that strongly chelates heavy metal ions, reacts with various heavy metal ions in sewage sludge, and quickly generates flocculent precipitates that are easy to filter and remove, achieving the purpose of removing heavy met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/26B01J20/30
Inventor 王海波李纪元王中元李华章秦晓娟
Owner 山西阳中新材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka